Structure and Properties of Ultradrawn Polylactide/Thermoplastic Polyurethane Elastomer Blends

Highly oriented self-reinforced 80/20 blends of polylactide (PLA)/thermoplastic polyurethane elastomer (TPU) were successfully fabricated through solid hot stretching technology. Different from the isotropic sample, stress rose rapidly in a low strain region, and exhibited strain hardening for the drawn samples of the PLA/TPU blend. Superior mechanical properties of the blend, with the notched Charpy impact strength 150 KJ/m2, and tensile strength 197 MPa, were achieved. With increasing hot stretch ratio, the storage modulus increased, the glass transition temperatures of the PLA-rich phase and TPU-rich phase in the blends moved to higher temperatures, and the melting temperature and crystallinity of the blend increased, indicating the stress-induced crystallization of the blend during drawing. The longitudinal fracture surfaces of the blends at different stretch ratios exhibited orderly arranged fibrillar bundle structure, which contributed to the significantly higher strength and toughness of the blend.

[1]  Z. Stachurski,et al.  Orientation and Structure Development in Poly(lactide) under Uniaxial Deformation , 2008 .

[2]  I. Ward,et al.  Orientation of polyoxymethylene by rolling with side constraints , 2008 .

[3]  R. Storey,et al.  Poly(lactic Acid) and Chain-Extended Poly(lactic acid)−Polyurethane Functionalized with Pendent Carboxylic Acid Groups , 2008 .

[4]  Q. Cao,et al.  Structure and mechanical properties of thermoplastic polyurethane, based on hyperbranched polyesters , 2006 .

[5]  Shen‐guo Wang,et al.  Manufacturing and morphology structure of polylactide-type microtubules orientation-structured scaffolds. , 2006, Biomaterials.

[6]  A. Galeski,et al.  Plasticization of semicrystalline poly(l-lactide) with poly(propylene glycol) , 2006 .

[7]  Mitsuhiro Shibata,et al.  Mechanical properties, morphology, and crystallization behavior of blends of poly(l-lactide) with poly(butylene succinate-co-l-lactate) and poly(butylene succinate) , 2006 .

[8]  D. Cohn,et al.  Biodegradable multiblock PEO/PLA thermoplastic elastomers: molecular design and properties , 2005 .

[9]  Andrzej Galeski,et al.  Strength and toughness of crystalline polymer systems , 2003 .

[10]  S. Lim,et al.  Toughening of polylactide by melt blending with linear low‐density polyethylene , 2003 .

[11]  S. Im,et al.  Miscibility and morphology in blends of poly(l-lactic acid) and poly(vinyl acetate-co-vinyl alcohol) , 2003 .

[12]  Michael J. Bevis,et al.  Improvement of the mechanical properties of poly(D,L-lactide) by orientation , 2002 .

[13]  F. Chang,et al.  Poly(oxypropylene)-amide grafted polypropylene as novel compatibilizer for PP and PA6 blends , 2001 .

[14]  I. Ward,et al.  Solid phase processing of polymers , 2000 .

[15]  C. Xiong,et al.  Synthesis and characterization of poly(?-caprolactone)-poly(ethylene glycol) block copolymer , 1997 .

[16]  Y. Ikada,et al.  Blends of aliphatic polyesters. I. Physical properties and morphologies of solution-cast blends from poly(DL-lactide) and poly(ε-caprolactone) , 1996 .