Reactive ion etching of TiN, TiAlN, CrN and TiCN Films in CF 4 /O 2 and CHF 3 /O 2 Plasmas

The reactive ion etching of a range of hard coatings (TiN, TiCN, CrN and TiAlN) has been examined as a function of rf power, flow rate and pressure. The films were deposited by filtered arc deposition (TiN, TiAlN and CrN) or low energy electron beam (TiCN) on polished disc substrates of M2 tool steel. The flat surfaces were lithographically patterned with a grating structure (∼1 μm pitch). The TiN and TiCN layers have shown significantly higher etch rates (100-250 nm/min) than the CrN and TiAlN (∼5 nm/min) coatings. These regimes of higher and low etch rate were identified as ion-enhanced chemical etching and physical sputtering, respectively. In CF 4 /O 2 plasma, the etch rate of the TiN and TiCN layers increased with rf power, flow rate and pressure which were parameters known to enhance the density of active fluorine species. The etch rates of TiN and TiCN layers were higher in CF 4 /O 2 plasma than in CHF 3 /O 2 gases in which polymer deposition was produced at pressure ≥ 35 mTorr.

[1]  S. G. Harris,et al.  Transmission electron microscopy of TiN and TiAlN thin films using specimens prepared by focused ion beam milling , 2004 .

[2]  H. Iwai,et al.  Dry etching characteristics of TiN film using Ar/CHF3, Ar/Cl2, and Ar/BCl3 gas chemistries in an inductively coupled plasma , 2003 .

[3]  Erol C. Harvey,et al.  Excimer laser micromachining of TiN films from chromium and copper sacrificial layers , 2002 .

[4]  E. D. Doyle,et al.  Dry cutting performance of partially filtered arc deposited titanium aluminium nitride coatings with various metal nitride base coatings , 2001 .

[5]  A. Matthews,et al.  Handbook of Hard Coatings: Edited by Rointan E Bunshah; Noyes Publications/William Andrew Publishing, New York 2001 (Available from American Technical Publishers Ltd, 27-29 Knowl Piece, Wilbury Way, Hitchin, Herts, SG4 0SX, England, Price £94) , 2001 .

[6]  E. D. Doyle,et al.  Dry machining — commercial viability through filtered arc vapour deposited coatings , 2000 .

[7]  N. R. Rueger,et al.  Selective etching of SiO2 over polycrystalline silicon using CHF3 in an inductively coupled plasma reactor , 1999 .

[8]  Jie Zheng,et al.  Performance of different etch chemistries on titanium nitride antireflective coating layers and related selectivity and microloading improvements for submicron geometries obtained with a high-density metal etcher , 1997 .

[9]  J. Weaver,et al.  Anisotropic pattern transfer of fine resist features to silicon nitride via an intermediate titanium layer , 1997 .

[10]  S. Pearton,et al.  Hybrid electron cyclotron resonance-RF plasma etching of TiNx thin films grown by low pressure rapid thermal metalorganic chemical vapour deposition , 1991 .

[11]  H. W. Lehmann,et al.  Mechanism of Dry Etching of Silicon Dioxide A Case of Direct Reactive Ion Etching , 1985 .

[12]  C. Steinbrüchel,et al.  Langmuir Probe Measurements on CHF 3 and CF 4 Plasmas: The Role of Ions in the Reactive Sputter Etching of SiO2 and Si , 1983 .