Photoelectrochromic performance of tungsten oxide based devices with PEG–titanium complex as solvent-free electrolytes

Abstract Photoelectrochromic (PEC) devices were assembled with an electrochemically deposited tungsten oxide (WO 3 ) thin film on transparent conductive glass (ITO) substrates, a composite polymeric electrolyte (PE), and a Ruthenium 535 sensitized TiO 2 sol–gel film deposited on ITO substrates. The polymeric electrolyte was prepared by the sol–gel method using a viscous polyethylene glycol (PEG, MW 600) and titanium isopropoxide as precursors in an acidic medium. A lithium salt (LiI) was added to the PEG–Ti complex for photoelectrochemical purposes. The color change of WO 3 based PEC devices under 100 mW/cm 2 illumination at short circuit conditions indicates that the introduction of titanium complex inside the polymeric electrolyte accelerates the coloring speed from 26 to 9 s. Electrochemical impedance spectroscopy analyses of PEC devices show that the presence of titanium complex in PE reduces the charge transfer resistance and increases the charge storage capacity of the cells. This improvement could come from the oxidation of iodides and reduction of titanium ions inside the composite electrolytes that increase the lithium ion's mobility.

[1]  Wei-Ting Wu,et al.  Fast-switching photovoltachromic cells with tunable transmittance. , 2009, ACS nano.

[2]  E. Meulenkamp.  Mechanism of WO3 electrodeposition from peroxy-tungstate solution , 1997 .

[3]  Hailing Hu,et al.  In situ formation of polyethylene glycol–titanium complexes as solvent-free electrolytes for electrochromic device application , 2010 .

[4]  Jun Chen,et al.  Novel quasi-solid electrolyte for dye-sensitized solar cells , 2007 .

[5]  M. Paoli,et al.  All-polymeric electrochromic and photoelectrochemical devices: new advances , 2001 .

[6]  M. Grätzel.  Photoelectrochemical cells : Materials for clean energy , 2001 .

[7]  J. Durrant,et al.  Electron Transfer Dynamics in Dye Sensitized Nanocrystalline Solar Cells Using a Polymer Electrolyte , 2001 .

[8]  U. Krašovec,et al.  Photoelectrochromic window with Pt catalyst , 2006 .

[9]  David R. Rosseinsky,et al.  Electrochromism : fundamentals and applications , 1995 .

[10]  Brian A. Gregg,et al.  Photoelectrochromic cells and their applications , 1997 .

[11]  The use of poly(vinylpyridine-co-acrylonitrile) in polymer electrolytes for quasi-solid dye-sensitized solar cells , 2007 .

[12]  Clemens Bechinger,et al.  Photoelectrochromic windows and displays , 1996, Nature.

[13]  B. Orel,et al.  Comparison of Photoelectrochromic Devices with Different Layer Configurations , 2002 .

[14]  Hailing Hu,et al.  Electrochromic responses of low-temperature-annealed tungsten oxide thin films in contact with a liquid and a polymeric gel electrolyte , 2009 .

[15]  Hailing Hu,et al.  Nanostructured polyethylene glycol–titanium oxide composites as solvent-free viscous electrolytes for electrochromic devices , 2011 .

[16]  Kuo-Chuan Ho,et al.  A novel photoelectrochromic device with dual application based on poly(3,4-alkylenedioxythiophene) thin film and an organic dye , 2008 .

[17]  Frederik C. Krebs,et al.  Quasi-solid-state dye-sensitized solar cells: Pt and PEDOT:PSS counter electrodes applied to gel electrolyte assemblies , 2007 .

[18]  X. Tao,et al.  Photoelectrochromic properties and energy storage of TiO2−xNx/NiO bilayer thin films , 2010 .