Sol-gel preparation and characterization of SiO2 coated VO2 films with enhanced transmittance and high thermochromic performance

Abstract Vanadium dioxide (VO2) films prepared at low-temperature with a low cost are considerable for energy-saving applications. Here, SiO2 coated VO2 films with clearly enhanced visible transmittance by introducing antireflection coatings (ARCs) and excellent thermochromic performance were present. The VO2 films have been prepared via a stable and low-cost sol–gel synthesis route using vanadium pentaoxide powder as precursor, and their structural, morphological, optical and electrical properties and thermochromic performance were systemically characterized. The resistance of VO2 films varies by 4 orders of magnitude and the transmittance changes from 11.8% to 69.3% at 2500 nm while no significant deviation appears in the visible region during metal–insulator transition (MIT). Nanoporous SiO2 coating with good optical transparency was coated on the surface of VO2 film via sol–gel dip-coating technique to enhance its optical transmittance, and the visible transmittance is increased by 14.6% due to the significantly decreased reflectance. The critical transition temperature (63 °C) and infrared switching properties of VO2 films are not much deteriorated by applying SiO2 layer. The synergistic effect of antireflection and thermochromism on SiO2 coated VO2 films was investigated.

[1]  M. Anpo,et al.  Enhancement of photocatalytic activity of P25 TiO2 by vanadium-ion implantation under visible light irradiation. , 2007, Journal of colloid and interface science.

[2]  Wei Zhao,et al.  Tunable assembly of vanadium dioxide nanoparticles to create porous film for energy-saving applications. , 2013, ACS applied materials & interfaces.

[3]  M. Fu,et al.  Optical nonlinearities of nanostructured VO2 thin films with low phase transition temperature , 2012 .

[4]  M. Rubner,et al.  Deformable Antireflection Coatings from Polymer and Nanoparticle Multilayers , 2006 .

[5]  Shao-Wei Wang,et al.  Properties of VO2 thin film prepared with precursor VO(acac)2 , 2004 .

[6]  Moon-Hee Lee,et al.  Better thermochromic glazing of windows with anti-reflection coating , 2000 .

[7]  Mark A. Richardson,et al.  Molybdenum-doped vanadium dioxide coatings on glass produced by the aqueous sol-gel method , 2003 .

[8]  Zheshen Li,et al.  SRPES studies of the NO2 reaction with vanadium oxide thin films on TiO2(110)-1×1 , 2002 .

[9]  C. H. Griffiths,et al.  Influence of stoichiometry on the metal‐semiconductor transition in vanadium dioxide , 1974 .

[10]  Claes-Göran Granqvist,et al.  Mg doping of thermochromic VO2 films enhances the optical transmittance and decreases the metal-insulator transition temperature , 2009 .

[11]  Gunnar A. Niklasson,et al.  Thermochromic VO2 Films for Energy-Efficient Windows , 1987, Optics & Photonics.

[12]  Shangjun Ding,et al.  Sol–gel preparation and characterization of nanoporous ZnO/SiO2 coatings with broadband antireflection properties , 2011 .

[13]  T. Venkatesan,et al.  Coherently coupled ZnO and VO2 interface studied by photoluminescence and electrical transport across a phase transition , 2012 .

[14]  Jun Shen,et al.  Ultrafast coloring-bleaching performance of nanoporous WO3-SiO2 gasochromic films doped with Pd catalyst. , 2011, ACS applied materials & interfaces.

[15]  Sea-Fue Wang,et al.  The preparation and characterization of transparent nano-sized thermochromic VO2–SiO2 films from the sol–gel process , 2004 .

[16]  Chel-Jong Choi,et al.  Direct observation of the structural component of the metal-insulator phase transition and growth habits of epitaxially grown VO2 nanowires. , 2007, Nano letters.

[17]  K. Sandhage,et al.  Freestanding monolithic silicon aerogels , 2012 .

[18]  F. J. Morin,et al.  Oxides Which Show a Metal-to-Insulator Transition at the Neel Temperature , 1959 .

[19]  Jagdish Narayan,et al.  Phase transition and critical issues in structure-property correlations of vanadium oxide , 2006 .

[20]  Allen,et al.  Resistivity of the high-temperature metallic phase of VO2. , 1993, Physical review. B, Condensed matter.

[21]  Yong Ding,et al.  Phase and shape controlled VO2 nanostructures by antimony doping , 2012 .

[22]  Hisao Suzuki,et al.  Fabrication of thermochromic composite using monodispersed VO2 coated SiO2 nanoparticles prepared by modified chemical solution deposition , 2007 .

[23]  Norio Miura,et al.  New Preparation Process of V2O5 Thin Film Based on Spin-Coating from Organic Vanadium Solution , 1990 .

[24]  E. B. Shadrin,et al.  Vanadium oxide films with improved characteristics for ir microbolometric matrices , 2001 .

[25]  Pouget,et al.  Comment on "VO2: Peierls or Mott-Hubbard? A view from band theory" , 1994, Physical Review Letters.

[26]  Ivan P. Parkin,et al.  Doped and un-doped vanadium dioxide thin films prepared by atmospheric pressure chemical vapour deposition from vanadyl acetylacetonate and tungsten hexachloride: the effects of thickness and crystallographic orientation on thermochromic properties , 2007 .

[27]  Ziyu Wu,et al.  Understanding the nature of the kinetic process in a VO2 metal-insulator transition. , 2010, Physical review letters.

[28]  Alain J. Kreisler,et al.  Recent progress in high-temperature superconductor bolometric detectors: from the mid-infrared to the far-infrared (THz) range , 2000 .

[29]  W. Pickett,et al.  Half-metallic semi-Dirac-point generated by quantum confinement in TiO2/VO2 nanostructures. , 2009, Physical review letters.

[30]  H. Kroto,et al.  Catalysed growth of novel aluminium oxide nanorods , 2003 .

[31]  Gang Xu,et al.  Optimization of antireflection coating for VO2-based energy efficient window , 2004 .

[32]  Moon-Hee Lee,et al.  Thermochromic glazing of windows with better luminous solar transmittance , 2002 .

[33]  Gang Xu,et al.  Design, formation and characterization of a novel multifunctional window with VO2 and TiO2 coatings , 2003 .

[34]  D. Kaur,et al.  VO2–WO3 nanocomposite thin films synthesized by pulsed laser deposition technique , 2011 .

[35]  Byung-Gyu Chae,et al.  Temperature dependence of the first-order metal-insulator transition in VO2 and programmable critical temperature sensor , 2007 .

[36]  Yi Xie,et al.  New Vanadium Oxide Nanostructures: Controlled Synthesis and Their Smart Electrical Switching Properties , 2010, Advanced materials.

[37]  Zu Rong Dai,et al.  Novel Nanostructures of Functional Oxides Synthesized by Thermal Evaporation , 2003 .

[38]  Mark A. Richardson,et al.  Comparison between vanadium dioxide coatings on glass produced by sputtering, alkoxide and aqueous sol–gel methods , 2002 .

[39]  Jacob O. Barnes,et al.  Electrical and optical switching properties of ion implanted VO2 thin films , 2009 .

[40]  Cheol-Eui Lee,et al.  Charge and spin dynamics in VO2 nanorods , 2009 .

[41]  T. E. Haynes,et al.  Switchable reflectivity on silicon from a composite VO2-SiO2 protecting layer , 2004 .

[42]  Byung-Gyu Chae,et al.  Characteristics of W- and Ti-Doped VO2 Thin Films Prepared by Sol-Gel Method , 2008 .