A thermodynamic model for electrical current induced damage

Abstract Electromigration-induced damage, which is in principal an irreversible mass diffusion under high current density, has been a concern for VLSI design for a long time. Miniaturization of electronic device sizes down to nano-scale will make electromigration a concern for all conducting components. This paper uses thermodynamics, statistical mechanics and mass transport (diffusion) principals to propose a model for electromigration process and a damage evolution model to quantify the degradation in microelectronics (and micro electromechanical system) solder joints subjected to high current densities. Entropy production in the system is used as a damage metric. The irreversible thermodynamic damage model utilized in this work has previously been successfully applied to thermo-mechanical fatigue of microelectronic solder joints. In this paper we extend this model to electromigration-induced degradation. Electromigration process is modeled by the atomic vacancy flux (mass diffusion) process. The proposed unified model is compared with several existing analytical and empirical models. A comparison of the damage evolution model proposed in here agrees well with empirical models proposed in the literature.

[1]  C. Basaran,et al.  Failure modes and FEM analysis of power electronic packaging , 2002 .

[2]  Cemal Basaran,et al.  Implementation of a Thermodynamic Framework for Damage Mechanics of Solder Interconnects in Microelectronics Packaging , 2002 .

[3]  Cemal Basaran,et al.  Influence of Microstructure Coarsening on Thermomechanical Fatigue Behavior of Pb/Sn Eutectic Solder Joints , 2001 .

[4]  Chao-Kun Hu,et al.  Copper interconnections and reliability , 1998 .

[5]  M. Korhonen,et al.  Stress evolution due to electromigration in confined metal lines , 1993 .

[6]  King-Ning Tu,et al.  Electromigration in Sn-Pb solder strips as a function of alloy composition , 2000 .

[7]  K. Tu,et al.  Six cases of reliability study of Pb-free solder joints in electronic packaging technology , 2002 .

[8]  C. Basaran,et al.  Experimental damage mechanics of microelectronic solder joints under fatigue loading , 2004, Proceedings Electronic Components and Technology, 2005. ECTC '05..

[9]  C. Basaran,et al.  Damage mechanics of microelectronics solder joints under high current densities , 2003 .

[10]  S. Brandenburg.  Electromigration Studies of Flip Chip Bump Solder Joints , 1998 .

[11]  L. E. Malvern.  Introduction to the mechanics of a continuous medium , 1969 .

[12]  Leon M Keer,et al.  Damage evolution governed by microcrack nucleation with application to the fatigue of 63Sn–37Pb solder , 1999 .

[13]  K. C. Valanis,et al.  Some thoughts on thermodynamics of internal variables , 1997 .

[14]  J. Black.  Electromigration failure modes in aluminum metallization for semiconductor devices , 1969 .

[15]  D. L. Beke,et al.  A direct study of the decrease of the content of magnesium and zinc alloying elements in aluminium alloys during heat treatment , 1979 .

[16]  James R. Lloyd,et al.  A model for conductor failure considering diffusion concurrently with electromigration resulting in a current exponent of 2 , 1986 .

[17]  K. Tu,et al.  Microstructure-electromigration correlation in a thin stripe of eutectic SnPb solder stressed between Cu electrodes , 1999 .

[18]  Hua Ye,et al.  Mechanical degradation of microelectronics solder joints under current stressing , 2003 .

[19]  Cemal Basaran,et al.  A Thermodynamic Framework for Damage Mechanics of Solder Joints , 1998 .

[20]  Reiner Kirchheim,et al.  Stress and electromigration in Al-lines of integrated circuits , 1992 .

[21]  Cemal Basaran,et al.  Measurement of high electrical current density effects in solder joints , 2003, Microelectron. Reliab..

[22]  Cemal Basaran,et al.  A Damage Mechanics-Based Fatigue Life Prediction Model for Solder Joints , 2003 .

[23]  Ludwig Boltzmann,et al.  Lectures on Gas Theory , 1964 .

[24]  D. R. Frear,et al.  Electromigration of eutectic SnPb solder interconnects for flip chip technology , 2001 .

[25]  P. Mazur,et al.  Non-equilibrium thermodynamics, , 1963 .

[26]  William D. Nix,et al.  An Analysis of Void Nucleation In Passivated Interconnect Lines Due to Vacancy Condensation and Interface Contamination , 1996 .

[27]  C. Basaran,et al.  An Irreversible Thermodynamics Theory for Damage Mechanics of Solids , 2004 .

[28]  I. Blech.  Electromigration in thin aluminum films on titanium nitride , 1976 .

[29]  T. M. Makhviladze,et al.  General model for mechanical stress evolution during electromigration , 1999 .

[30]  Hua Ye,et al.  Thermomigration in Pb–Sn solder joints under joule heating during electric current stressing , 2003 .

[31]  J. Chaboche,et al.  Mechanics of Solid Materials , 1990 .

[32]  Cemal Basaran,et al.  Computer simulations of solder joint reliability tests , 2001 .

[33]  F. Shi,et al.  Stochastic simulation of electromigration failure of flip chip solder bumps , 2001 .