Evaluation of Defects of Thermal Barrier Coatings by Thermal Shock Test Using Eddy Current Testing

Abstract Periodical thermal shock can introduce defects in thermal barrier coating made by layers of CoNiCrAlY bond coating(BC) and ZrO 2 -8wt%Y 2 O 3 ceramic top coating(TC) on Inconel-738 substrate using plasma spraying. Thermal shock test is performed by severe condition that is to heat until 1000℃ and cool until 20℃. As the number of cycle is increased, the fatigue by thermal shock is also increased. After test, the micro-structures and mechanical characteristics of thermal barrier coating were investigated by SEM, XRD. The TGO layer of Al 2 O 3 is formed between BC and TC by periodical thermal shock test, and its change in thickness is inspected by eddy current test(ECT). By ECT test, it is shown that TGO and micro-crack can be detected and it is possible to predict the life of thermal barrier coating. Keywords: Thermal Barrier Coating(TBC), Thermal Shock, Plasma Spray, Thermally Grown Oxide(TGO), Eddy Current Testing(ECT) [논 문] - 비파괴검사학회지 Journal of the Korean Societyfor Nondestructive TestingVol. 29, No. 5 (2009. 10)