Transmission electron microscopy characterization of irradiated U–7Mo/Al–2Si dispersion fuel

The plate-type dispersion fuels, with the atomized U(Mo) fuel particles dispersed in the Al or Al alloy matrix, are being developed for use in research and test reactors worldwide. It is found that the irradiation performance of a plate-type dispersion fuel depends on the radiation stability of the various phases in a fuel plate. Transmission electron microscopy was performed on a sample (peak fuel mid-plane temperature approximately 109 degrees C and fission density approximately 4.5 x 10 27 fm-3) taken from an irradiated U–7Mo dispersion fuel plate with Al–2Si alloy matrix to investigate the role of Si addition in the matrix on the radiation stability of the phase(s) in the U–7Mo fuel/matrix interaction layer. A similar interaction layer that forms in irradiated U–7Mo dispersion fuels with pure Al matrix has been found to exhibit poor irradiation stability, likely as a result of poor fission gas retention. The interaction layer for both U–7Mo/Al–2Si and U–7Mo/Al fuels is observed to be amorphous. However, unlike the latter, the amorphous layer for the former was found to effectively retain fission gases in areas with high Si concentration. When the Si concentration becomes relatively low, the fission gas bubbles agglomerate into fewer large pores. Withinmore » the U–7Mo fuel particles, a bubble superlattice ordered as fcc structure and oriented parallel to the bcc metal lattice was observed where the average bubble size and the superlattice constant are approximately 3.5 nm and approximately 7.5 nm, respectively. The estimated fission gas inventory in the bubble superlattice correlates well with the fission density in the fuel.« less

[1]  Eduardo Gallego,et al.  Transactions of the American Nuclear Society , 2009 .

[2]  P. Johnson,et al.  The gas-bubble superlattice and the development of surface structure in He+ and H irradiated metals at 300 K , 1980 .

[3]  P. Johnson,et al.  Helium gas-bubble superlattice formation in molybdenum , 2006 .

[4]  K. Krishan Invited review article ordering of voids and gas bubbles in radiation environments , 1982 .

[5]  F. Hodaj,et al.  Further insight into mechanisms of solid-state interactions in UMo/Al system , 2008 .

[6]  J. L. Snelgrove,et al.  Low-temperature irradiation behavior of uranium–molybdenum alloy dispersion fuel☆ , 2002 .

[7]  S. V. D. Berghe,et al.  Post-irradiation examination of AlFeNi cladded U3Si2 fuel plates irradiated under severe conditions , 2008 .

[8]  Donald R. Olander,et al.  Fundamental Aspects of Nuclear Reactor Fuel Elements , 1976 .

[9]  P. Johnson,et al.  A temperature threshold for gas-bubble superlattice formation in molybdenum , 1998 .

[10]  S. Van den Berghe,et al.  Transmission electron microscopy investigation of irradiated U–7 wt%Mo dispersion fuel , 2008 .

[11]  P. Johnson,et al.  Importance of stress in bubble ordering in the helium gas-bubble superlattice in copper , 1987, Nature.

[13]  P. Johnson,et al.  Gas-bubble superlattice formation in bcc metals , 1995 .

[14]  J. Rest,et al.  Analysis of intergranular fission-gas bubble-size distributions in irradiated uranium–molybdenum alloy fuel , 2009 .

[15]  D. Keiser,et al.  Electron microscopy characterization of an as-fabricated research reactor fuel plate comprised of U–7Mo particles dispersed in an Al–2Si alloy matrix , 2010 .

[16]  Y. Kim,et al.  A CLASSIFICATION OF UNIQUELY DIFFERENT TYPES OF NUCLEAR FISSION GAS BEHAVIOR , 2005 .

[17]  G. Hofman Crystal structure stability and fission gas swelling in intermetallic uranium compounds , 1986 .

[18]  J. Snelgrove,et al.  Irradiation behaviour of uranium silicide compounds , 2004 .