Effects of hydration on the mechanical response of individual collagen fibrils

Collagen fibrils prepared from bovine Achilles tendon have been mechanically tested through nanoindentation by an atomic force microscope using force volume analysis. In ambient conditions where the fibrils are expected to be dehydrated, the elastic modulus was determined to be 1.9±0.5GPa, while under aqueous fluid, it decreased by three orders of magnitude to 1.2±0.1MPa. In air, fibril fracture occurred along the axis and the crack lengths were quantized to the D-banding periodicity. The apparent hardness of the fibrils was estimated to be in the range of 0.35–0.6GPa.

[1]  H M Berman,et al.  Hydration structure of a collagen peptide. , 1995, Structure.

[2]  F. O. Schmitt,et al.  Electron microscope investigations of the structure of collagen , 1942 .

[3]  R. Marchant,et al.  Force measurements on platelet surfaces with high spatial resolution under physiological conditions. , 2000, Colloids and surfaces. B, Biointerfaces.

[4]  H. El-Shall,et al.  Atomic force microscopy measurement of the elastic properties of the kidney epithelial cells. , 2005, Journal of colloid and interface science.

[5]  Jan Feijen,et al.  Micromechanical testing of individual collagen fibrils. , 2006, Macromolecular bioscience.

[6]  E. Chernoff,et al.  Atomic force microscope images of collagen fibers , 1992 .

[7]  W. G. Matthews,et al.  Determination of the elastic modulus of native collagen fibrils via radial indentation , 2006 .

[8]  G. Pharr,et al.  An improved technique for determining hardness and elastic modulus using load and displacement sensing indentation experiments , 1992 .

[9]  J. Batteas,et al.  The influence of water on the nanomechanical behavior of the plant biopolyester cutin as studied by AFM and solid-state NMR. , 2000, Biophysical journal.

[10]  M. Oyen,et al.  Nanoindentation hardness of mineralized tissues. , 2006, Journal of biomechanics.

[11]  H. Cantow,et al.  The interplay between surface micro-topography and -mechanics of type I collagen fibrils in air and aqueous media: An atomic force microscopy study , 2001 .

[12]  D. Hulmes,et al.  Building collagen molecules, fibrils, and suprafibrillar structures. , 2002, Journal of structural biology.

[13]  W F Heinz,et al.  Relative microelastic mapping of living cells by atomic force microscopy. , 1998, Biophysical journal.

[14]  Jan Feijen,et al.  Mechanical properties of native and cross-linked type I collagen fibrils. , 2008, Biophysical journal.

[15]  Vinod Subramaniam,et al.  Micromechanical bending of single collagen fibrils using atomic force microscopy. , 2007, Journal of biomedical materials research. Part A.

[16]  W. G. Matthews,et al.  Low strain nanomechanics of collagen fibrils. , 2007, Biomacromolecules.

[17]  J. Kinney,et al.  The Importance of Intrafibrillar Mineralization of Collagen on the Mechanical Properties of Dentin , 2003, Journal of dental research.

[18]  Pascal Elleaume,et al.  Insertion devices at the ESRF , 1995 .

[19]  S. Britland,et al.  Poly(vinyl alcohol) Hydrogel as a Biocompatible Viscoelastic Mimetic for Articular Cartilage , 2008, Biotechnology progress.

[20]  M. Radmacher,et al.  Measuring the Elastic Properties of Thin Polymer Films with the Atomic Force Microscope , 1998 .

[21]  J. A. Chapman,et al.  Collagen fibril formation. , 1996, The Biochemical journal.

[22]  Laurent Bozec,et al.  Mechanical properties of collagen fibrils. , 2007, Biophysical journal.