A very high-selectivity silicon nitride etch process has been developed on an inductively coupled plasma etching system which uses a NF3/O2/NH3 (nonchlorine) chemistry. Etch selectivity of low-pressure chemical vapor deposition nitride to thermal oxide greater than 100:1 was achieved at a nitride etch rate of 500 A/min. A NF3/O2 chemistry was optimized for nitride to oxide selectivity of about 12:1, with a nitride etch rate of 1200 A/min. The addition of NH3 inhibits oxide etching thus enhancing selectivity. The net etch rate for oxide may be reduced to zero while maintaining a reasonably high etch rate for nitride thus resulting in essentially infinite selectivity. The process is stable, repeatable and creates no particles. A split lot test on device wafers against standard wet etch process demonstrates superior process and device performance.
[1]
L. Loewenstein.
Temperature dependence of silicon nitride etching by atomic fluorine
,
1989
.
[2]
J. B. Boos,et al.
Low-resistance AuZn gate ohmic contacts for InP JFETs
,
1988
.
[3]
R. Huttemann,et al.
Ammonium Hexafluorosilicate Formation during Plasma Etching of Silicon Nitride
,
1988
.
[4]
Selective interhalogen etching of tantalum compounds and other semiconductor materials
,
1985
.
[5]
H. Nishino,et al.
Damage‐free selective etching of Si native oxides using NH3/NF3 and SF6/H2O down‐flow etching
,
1993
.
[6]
J. Stevens,et al.
Role of nitrogen in the downstream etching of silicon nitride
,
1996
.