Control of epitaxial growth of Fe-based nanocrystals on Si substrates using well-controlled nanometer-sized interface

We have developed an epitaxial growth technique for Fe-based nanocrystals (NCs) on Si substrates with high selectivity of their crystal structure. Ge NCs with controlled shape and strain were initially epitaxially grown on Si substrates covered with an ultrathin SiO2 film. Using these well-controlled Ge NCs as nucleation sites, Fe-based NCs could be formed with crystal-structure selectivity. In Fe deposition on the Ge NCs at room temperature, bcc-Fe NCs were formed, where epitaxial growth was influenced by the Ge NC shapes related to surface coverage. For Fe deposition at 250–300 °C, Fe-Ge alloying occurred without intermixing with Si. The epitaxially grown crystal structures were determined by the strain state of the Ge NCs: Fe1.7Ge NCs with a B82 structure for spherical strain-relaxed Ge NCs with a lattice constant close to that of bulk Ge, and e-FeGe NCs with a B20 structure for flattened strained Ge NCs with a lattice constant close to that of bulk Si. All the NCs had sharp interfaces, where interfaci...

[1]  J. Kikkawa,et al.  Influence of nanometer-sized interface on reaction of iron nanocrystals epitaxially grown on silicon substrates with oxygen gas , 2013 .

[2]  Y. Tokura,et al.  Skyrmion flow near room temperature in an ultralow current density , 2012, Nature Communications.

[3]  M. Ichikawa,et al.  Epitaxial Growth of High Quality Ge Films on Si(001) Substrates by Nanocontact Epitaxy , 2011 .

[4]  Y. Tokura,et al.  Near room-temperature formation of a skyrmion crystal in thin-films of the helimagnet FeGe. , 2011, Nature materials.

[5]  Y. Tokura,et al.  Real-space observation of a two-dimensional skyrmion crystal , 2010, Nature.

[6]  Yoshiaki Nakamura,et al.  Self-organized formation and self-repair of a two-dimensional nanoarray of Ge quantum dots epitaxially grown on ultrathin SiO2-covered Si substrates , 2010, Nanotechnology.

[7]  M. Miyao,et al.  Epitaxial ferromagnetic Fe3Si∕Si(111) structures with high-quality heterointerfaces , 2008, 0810.2835.

[8]  J. Bubendorff,et al.  Room-temperature ferromagnetism in single crystal Fe1.7Ge thin films of high thermal stability grown on Ge(111) , 2008 .

[9]  N. Tanaka,et al.  Epitaxial growth of ultrahigh density Ge1−xSnx quantum dots on Si (111) substrates by codeposition of Ge and Sn on ultrathin SiO2 films , 2007 .

[10]  M. Ichikawa,et al.  Influence of growth and annealing conditions on photoluminescence of Ge/Si layers grown on oxidized Si surfaces , 2007 .

[11]  C. Binek,et al.  Piezomagnetism in epitaxial Cr2O3 thin films and spintronic applications , 2007 .

[12]  M. Ichikawa,et al.  Photoluminescence of Si layers grown on oxidized Si surfaces , 2007 .

[13]  I. Schuller,et al.  Fabrication and structural characterization of highly ordered sub-100-nm planar magnetic nanodot arrays over 1cm2 coverage area , 2006 .

[14]  N. Tanaka,et al.  Observation of the quantum-confinement effect in individual β-FeSi2 nanoislands epitaxially grown on Si (111) surfaces using scanning tunneling spectroscopy , 2006 .

[15]  C. Vittoria,et al.  Single crystal Fe films grown on Ge (001) substrates by magnetron sputtering , 2006 .

[16]  N. Tanaka,et al.  Formation of ultrahigh density and ultrasmall coherent β‐FeSi2 nanodots on Si (111) substrates using Si and Fe codeposition method , 2006 .

[17]  Kentaroh Watanabe,et al.  Observation of the quantum-confinement effect in individual Ge nanocrystals on oxidized Si substrates using scanning tunneling spectroscopy , 2005 .

[18]  Chong-Min Wang,et al.  Co-doped anatase TiO2 heteroepitaxy on Si(001) , 2005 .

[19]  Yoshiaki Nakamura,et al.  Nonthermal decomposition of C60 polymers induced by tunneling electron injection , 2004 .

[20]  A. Ulman,et al.  Surface chemistry of Fe2O3 nanoparticles on ultrathin oxide layers on Si and Ge , 2003 .

[21]  Yoshiaki Nakamura,et al.  Nanoscale imaging of electronic surface transport probed by atom movements induced by scanning tunneling microscope current. , 2002, Physical review letters.

[22]  Tomoji Kawai,et al.  Magnetic and electric properties of transition-metal-doped ZnO films , 2001 .

[23]  Yu-Nu Hsu,et al.  Effects of Ag underlayers on the microstructure and magnetic properties of epitaxial FePt thin films , 2001 .

[24]  Oliver G. Schmidt,et al.  Multiple layers of self-asssembled Ge/Si islands: Photoluminescence, strain fields, material interdiffusion, and island formation , 2000 .

[25]  A. Ercole,et al.  Evolution of the ferromagnetic phase of ultrathin Fe films grown on GaAs(100)- 4 × 6 , 1998 .

[26]  P. Norton,et al.  GROWTH OF ULTRATHIN FE FILMS ON GE(100) : STRUCTURE AND MAGNETIC PROPERTIES , 1997 .

[27]  D. Leong,et al.  A silicon/iron-disilicide light-emitting diode operating at a wavelength of 1.5 μm , 1997, Nature.

[28]  Kota,et al.  Ferromagnetic-resonance studies of epitaxial Ni, Co, and Fe films grown on Cu(100)/Si(100). , 1993, Physical review. B, Condensed matter.

[29]  T. Sands,et al.  Epitaxial growth of ferromagnetic ultrathin MnGa films with perpendicular magnetization on GaAs , 1993 .

[30]  Miranda,et al.  Metallization-induced spontaneous silicide formation at room temperature: The Fe/Si case. , 1992, Physical review. B, Condensed matter.

[31]  W. Meng,et al.  Epitaxial growth of α‐Fe films on Si(111) substrates , 1991 .

[32]  R. Miranda,et al.  The Fe/Si(100) interface , 1991 .

[33]  N. Cherief,et al.  Optical and electrical characterization of β‐FeSi2 epitaxial thin films on silicon substrates , 1991 .