Indium tin oxide thin films for organic light-emitting devices

High-quality indium tin oxide (ITO) thin films (150–200 nm) were grown on glass substrates by pulsed laser deposition (PLD) without postdeposition annealing. The electrical, optical, and structural properties of these films were investigated as a function of substrate temperature, oxygen pressure, and film thickness. PLD provides very uniform ITO films with high transparency (⩾85% in 400–700 nm spectrum) and low electrical resistivity (2–4×10−4 Ω cm). The Hall mobility and carrier density for a 170-nm-thick film deposited at 300 °C are 29 cm2/V s and 1.45×1021 cm−3, respectively. Atomic force microscopy measurements of the ITO films indicated that their root-mean-square surface roughness (∼5 A) is superior to that (∼40 A) of commercially available ITO films deposited by sputtering. ITO films grown at room temperature by PLD were used to study the electroluminescence (EL) performance of organic light-emitting devices. The EL performance was comparable to that measured with commercial ITO anodes.

[1]  V. Vasu,et al.  Reaction kinetics of the formation of indium tin oxide films grown by spray pyrolysis , 1990 .

[2]  Charles D. Merritt,et al.  Dye-doped molecular light-emitting diodes with enhanced performance , 1998, Optics & Photonics.

[3]  Hoi Sing Kwok,et al.  Low Resistivity Indium Tin Oxide Films by Pulsed Laser Deposition , 1993 .

[4]  H. Hartnagel,et al.  Semiconducting Transparent Thin Films , 1995 .

[5]  R. Bunshah,et al.  Electrical and optical properties of In2O3: Sn films prepared by activated reactive evaporation , 1980 .

[6]  C. Tang,et al.  Organic Electroluminescent Diodes , 1987 .

[7]  Junji Kido,et al.  Efficient Electroluminescence from Tris(4-methyl-8-quinolinolato)aluminum(III) , 1997 .

[8]  M. Buchanan,et al.  Preparation of conducting and transparent thin films of tin‐doped indium oxide by magnetron sputtering , 1980 .

[9]  J. C. Roustan,et al.  Fabrication and characterization of ITO thin films deposited by excimer laser evaporation , 1996 .

[10]  T. Moss.  The Interpretation of the Properties of Indium Antimonide , 1954 .

[11]  T. Karasawa,et al.  Electrical and optical properties of indium tin oxide thin films deposited on unheated substrates by d.c. reactive sputtering , 1993 .

[12]  Kunihiro Fukui,et al.  Indium tin oxide thin films prepared by chemical vapour deposition , 1991 .

[13]  Junji Kido,et al.  Fabrication of highly efficient organic electroluminescent devices , 1998 .

[14]  Wen-Fa Wu,et al.  Effect of sputtering power on the structural and optical properties of RF magnetron sputtered ITO films , 1994 .