Room temperature Cu–Cu direct bonding using surface activated bonding method

Thin copper (Cu) films of 80 nm thickness deposited on a diffusion barrier layered 8 in. silicon wafers were directly bonded at room temperature using the surface activated bonding method. A low energy Ar ion beam of 40–100 eV was used to activate the Cu surface prior to bonding. Contacting two surface-activated wafers enables successful Cu–Cu direct bonding. The bonding process was carried out under an ultrahigh vacuum condition. No thermal annealing was required to increase the bonding strength since the bonded interface was strong enough at room temperature. The chemical constitution of the Cu surface was examined by Auger electron spectroscope. It was observed that carbon-based contaminations and native oxides on copper surface were effectively removed by Ar ion beam irradiation for 60 s without any wet cleaning processes. An atomic force microscope study shows that the Ar ion beam process causes no surface roughness degradation. Tensile test results show that high bonding strength equivalent to bulk ...

[1]  Douglas Ray Sparks,et al.  Wafer-to-wafer bonding of nonplanarized MEMS surfaces using solder , 2001 .

[2]  Kuan-Neng Chen,et al.  Microstructure examination of copper wafer bonding , 2001 .

[3]  A. Fan,et al.  Copper Wafer Bonding , 1999 .

[4]  T. Suga,et al.  Transmission Electron Microscope Observations of Si/Si Interface Bonded at Room Temperature by Ar Beam Surface Activation , 1999 .

[5]  Yves Morand,et al.  Copper metallization for advanced IC: requirements and technological solutions , 1999 .

[6]  U. Gösele,et al.  SemiConductor Wafer Bonding: Science and Technology , 1998 .

[7]  R. Bower,et al.  Low Temperature Copper to Copper Direct Bonding , 1998 .

[8]  M. T. Bohr,et al.  Technology for advanced high-performance microprocessors , 1998 .

[9]  K. Enisherlova,et al.  SOI-structures produced by the silicon direct bonding method , 1997 .

[10]  Ryutaro Maeda,et al.  Surface activated bonding of silicon wafers at room temperature , 1996 .

[11]  Werner Langheinrich,et al.  Application of oxygen plasma processing to silicon direct bonding , 1993 .

[12]  Tadashi Shibata,et al.  Evaluating the Large Electromigration Resistance of Copper Interconnects Employing a Newly Developed Accelerated Life‐Test Method , 1993 .

[13]  Stefan Bengstsson Semiconductor wafer bonding: a review of interfacial properties and applications , 1992 .

[14]  U. Gösele,et al.  Semiconductor wafer bonding , 1998 .

[15]  C. Ting,et al.  Selective electroless copper for VLSI interconnection , 1989, IEEE Electron Device Letters.

[16]  J. Lasky Wafer bonding for silicon‐on‐insulator technologies , 1986 .

[17]  J. Cuomo,et al.  Summary Abstract: Modification of metals by low energy ions during thin film deposition , 1985 .

[18]  J. Cuomo,et al.  Reactive sputtering of copper and silicon near the sputtering threshold , 1985 .

[19]  K.C. Saraswat,et al.  Effect of scaling of interconnections on the time delay of VLSI circuits , 1982, IEEE Transactions on Electron Devices.

[20]  S. Murarka,et al.  Copper metallization for ULSL and beyond , 1995 .