Easy‐glide hardening of Zn and Cd between 4.2 and 400 K

The work hardening coefficient in the easy glide range is measured on Zn and Cd single crystals in the temperature range from 4.2 to 400 K. For low temperatures T/Tm ⪅ 0.15 work hardening was found to decrease rapidly with rising temperature, passes a minimum and at T/Tm = 0.3 there is a well developed maximum of work hardening. The location of this maximum depends on the shear strain rate. If the temperature becomes T/Tm ⪆ 0.3 the well known decrease of work hardening due to recovery processes can be observed. The measured temperature dependence of work hardening is contradictory to the established theories of work hardening of hexagonal metals, which affirm a constant ∂A in the low temperature range. Der Verfestigungskoeffizient des Bereiches A von Zn- und Cd-Einkristallen wurde erstmals im ganzen Temperaturbereich von 4,2 bis 400 K durchgehend gemessen. Die Verfestigung nimmt im Tieftemperaturbereich T/Tm ⪅ 0,15 fur steigende Temperaturen stark ab, durchlauft ein Minimum und zeigt bei T/Tm = 0,3 ein deutliches Maximum, dessen Lage von der Verformungsgeschwindigkeit abhangt. Fur T/Tm ⪆ 0.3 wird die bekannte Abnahme der Verfestigung auf Grund von Erholungsprozessen beobachtet. Die Temperatur-abhangigkeit ∂A(T) steht im Widerspruch zu den gangigen Verfestigungstheorien, die einen Konstanzbereich fur T/Tm > 0,3 vorhersagen.

[1]  P. Lukáč,et al.  Temperature and concentration dependence of the critical resolved shear stress of cadmium-zinc alloy single crystals , 1973 .

[2]  B. Wielke Thermally activated glide of zinc single crystals from 4.2° to 373°k , 1973 .

[3]  P. Kratochvíl,et al.  Temperature dependence of the flow stress in secondary glide planes of cadmium single crystals , 1971 .

[4]  V. Novák,et al.  Resistivity changes in cold‐worked Cd , 1971 .

[5]  P. Kratochvíl,et al.  The primary and secondary slip relation for basal glide in cadmium and zinc single crystals , 1968 .

[6]  K. Adams Basal Dislocation Mobility in Zinc Single Crystals , 1967 .

[7]  N. R. Risebrough,et al.  THE LINEAR HARDENING OF CADMIUM , 1967 .

[8]  P. Kratochvíl On the dislocation arrangement in deformed crystals of zinc , 1966 .

[9]  P. Hirsch,et al.  The deformation of magnesium single crystals , 1965 .

[10]  W. Mayer,et al.  Moderne Probleme der Metallphysik , 1965 .

[11]  P. Lukáč,et al.  Zur Deutung der Orientierungsabhängigkeit des Verfestigungsanstiegs in Zinkkristallen , 1964, 1964.

[12]  M. Boček,et al.  Die Orientierungs‐ und Temperaturabhängigkeit der Verfestigungskurven von Zinkkristallen , 1964 .

[13]  M. Boček,et al.  Die Temperaturabhängigkeit der Verfestigungskenngrößen von Magnesiumeinkristallen , 1964 .

[14]  M. Boček Zusammenfassende Darstellung der Gleitverformung in Metallen mit dichtest gepackter Struktur , 1963 .

[15]  S. Mader,et al.  Work-hardening of hexagonal Close-packed crystals and in the easy glide region of face-centred cubic crystals , 1961 .

[16]  C. Garland,et al.  Elastic Constants of Cadmium from 4.2K to 300K , 1960 .

[17]  G. Alers,et al.  The elastic constants of zinc between 4.2° and 670°K , 1958 .

[18]  C. Garland,et al.  Elastic Constants of Zinc from 4.2°K to 77.6°K , 1958 .

[19]  N. Mott CXVII. A theory of work-hardening of metal crystals , 1952 .

[20]  E. Schmid,et al.  Kristallplastizität mit besonderer Berücksichtigung der Metalle , 1935 .

[21]  G. Taylor The Mechanism of Plastic Deformation of Crystals. Part I. Theoretical , 1934 .

[22]  R. Honeycombe,et al.  Plastic Deformation of Metals , 1932, Nature.

[23]  E. Schmid,et al.  Über die Temperaturabhängigkeit der Kristallplastizität , 1930 .

[24]  E. Schmid,et al.  Über die Temperaturabhängigkeit der Kristallplastizität. II , 1930 .

[25]  W. Meissner,et al.  Messungen mit Hilfe von flüssigem Helium. XII , 1930 .