Correlationship between electrode mechanics and long-term cycling performance for graphite anode in lithium ion cells

Abstract In the development of lithium ion batteries for electric vehicle applications, much effort has been made in fabrication and optimization of active materials. Mechanical properties of the electrode laminate, which are also very critical determining the durability of the cell, have long been ignored. In this study, graphite laminates of the same chemical composition are prepared by using different mixing technologies. With similar breaking strength, Young’s modulus of the laminate is found to be very different according to the mixing order. Electrochemical performances of the graphite laminates are investigated against Li anode and Li[Ni 1/3 Co 1/3 Mn 1/3 ]O 2 cathode, respectively. Long-term cycling performance is closely related with the Young’s modulus of the graphite laminate. Whereas the laminates of low modulus cycles well during the investigated 600 deep charge–discharge cycles, the electrodes of high modulus fail at around 350 cycles. Electrochemical degradation mechanism for the laminate of high modulus is associated with the significant impedance rise aroused from mechanical failure. After the long-term cycling test, lots of cracks are observed on the high modulus electrode along the particle boundaries while the mechanical integrity of the low modulus laminate is well maintained.

[1]  B. Fultz,et al.  XRD evidence of macroscopic composition inhomogeneities in the graphite–lithium electrode , 2007 .

[2]  Curtis W. Frank,et al.  Interaction of poly(vinylidene fluoride) with graphite particles. 1. Surface morphology of a composite film and its relation to processing parameters , 2003 .

[3]  Stephen J. Harris,et al.  Direct measurement of lithium transport in graphite electrodes using neutrons , 2011 .

[4]  Ann Marie Sastry,et al.  Numerical Simulation of the Effect of the Dissolution of LiMn2O4 Particles on Li-Ion Battery Performance , 2011 .

[5]  R. Kostecki,et al.  Diagnostic evaluation of detrimental phenomena in 13C-labeled composite cathodes for Li-ion batteries , 2007 .

[6]  Kyung Hyun Ahn,et al.  Effect of slurry preparation process on electrochemical performances of LiCoO2 composite electrode , 2010 .

[7]  Dennis W. Dees,et al.  High-energy electrode investigation for plug-in hybrid electric vehicles , 2011 .

[8]  M. Wohlfahrt‐Mehrens,et al.  Ageing mechanisms in lithium-ion batteries , 2005 .

[9]  Ralph E. White,et al.  Theoretical Analysis of Stresses in a Lithium Ion Cell , 2010 .

[10]  Guoying Chen,et al.  Continuity and performance in composite electrodes , 2010 .

[11]  Stephen J. Harris,et al.  In Situ Observation of Strains during Lithiation of a Graphite Electrode , 2010 .

[12]  John Newman,et al.  Stress generation and fracture in lithium insertion materials , 2005 .

[13]  Xiangyun Song,et al.  Cathode Performance as a Function of Inactive Material and Void Fractions , 2010 .

[14]  Xiangyun Song,et al.  Correlation between dissolution behavior and electrochemical cycling performance for LiNi1/3Co1/3Mn1/3O2-based cells , 2012 .

[15]  Z. Suo,et al.  Averting cracks caused by insertion reaction in lithium–ion batteries , 2010 .

[16]  Andrew M. Minor,et al.  Optimization of Acetylene Black Conductive Additive and PVDF Composition for High-Power Rechargeable Lithium-Ion Cells , 2007 .

[17]  Xiangyun Song,et al.  Particles and Polymer Binder Interaction: A Controlling Factor in Lithium-Ion Electrode Performance , 2012 .

[18]  Soon Ho Chang,et al.  Effect of mixing sequences on the electrode characteristics of lithium-ion rechargeable batteries , 1999 .

[19]  Ahmet T. Alpas,et al.  A transmission electron microscopy study of crack formation and propagation in electrochemically cycled graphite electrode in lithium-ion cells , 2011 .

[20]  I. Jung,et al.  Effects of anode active materials to the storage-capacity fading on commercial lithium-ion batteries , 2007 .

[21]  B. N. Popov,et al.  Studies on Capacity Fade of Lithium-Ion Batteries , 2000 .

[22]  A. Sastry,et al.  Numerical Simulation of Stress Evolution in Lithium Manganese Dioxide Particles due to Coupled Phase Transition and Intercalation , 2011 .

[23]  Masaki Yoshio,et al.  An Investigation of Lithium Ion Insertion into Spinel Structure Li‐Mn‐O Compounds , 1996 .

[24]  Xiangyun Song,et al.  Cooperation between Active Material, Polymeric Binder and Conductive Carbon Additive in Lithium Ion Battery Cathode , 2012 .

[25]  Young-Min Choi,et al.  Aqueous processing of natural graphite particulates for lithium-ion battery anodes and their electrochemical performance , 2005 .

[26]  Matthieu Dubarry,et al.  Identify capacity fading mechanism in a commercial LiFePO4 cell , 2009 .

[27]  Xiangyun Song,et al.  Calendering effects on the physical and electrochemical properties of Li[Ni1/3Mn1/3Co1/3]O2 cathode , 2012 .

[28]  Zhigang Suo,et al.  Fracture of electrodes in lithium-ion batteries caused by fast charging , 2010 .

[29]  G. Botte.  Modeling volume changes due to lithium intercalation in a carbon fiber , 2005 .

[30]  I. Bloom,et al.  Performance degradation of high-power lithium-ion cells—Electrochemistry of harvested electrodes , 2007 .