Synthesis of the Hydroxyl-Containing Poly(dimethyl siloxane) Modified Polyacrylate Core-Shell Latex and the Application as a Novel Binder for Pigment Printing of Fabric

A core-shell latex based on methyl methacrylate, n-butyl acrylate, and methacrylic acid was synthesized, and the core of which was modified by hydroxyl-containing poly(dimethyl siloxane). Glycidyl methacrylate was empolyed as one of monomers in the shell and served as a cross-linker when the core-shell latex was used as an binder of the pigment printing. The chemical structure of the copolymer was characterized by infrared spectrum. The stucture and the particle size of the core-shell particles were characterized by transmission electron microscopy, nanoscale granularity analysis, and differential scanning calorimetry. The latex was used as a binder in pigment printing of fabrics.

[1]  Bin Wang,et al.  Preparation of composite polyacrylate latex particles with in situ‐formed methylsilsesquioxane cores , 2009 .

[2]  C. Li,et al.  Preparation and Characterization of Polymer Core Shell Latex Particles , 2008 .

[3]  Xuejun Cui,et al.  Preparation and characterization of polytetrafluoroethylene‐polyacrylate core–shell nanoparticles , 2007 .

[4]  Hongzheng Chen,et al.  Preparation and application of nanoscale microemulsion as binder for fabric inkjet printing , 2006 .

[5]  C. Chern,et al.  Emulsion polymerization mechanisms and kinetics , 2006 .

[6]  R. Schneider,et al.  Development of ecofriendly binders for pigment printing of all types of textile fabrics , 2006 .

[7]  Bojana Voncina,et al.  Properties of UV-cured pigment prints on textile fabric , 2006 .

[8]  Songjun Li,et al.  Core/shell particles containing 3-(methacryloxypropyl)-trimethoxysilane in the shell: synthesis, characterization, and application. , 2005, Macromolecular bioscience.

[9]  Zhicheng Zhang,et al.  Preparation and characterization of polysiloxane–polyacrylates composite latices and their film properties , 2005 .

[10]  F. Tiarks,et al.  Studies for a new generation of acrylic binders for exterior wood coatings , 2002 .

[11]  X. Kong,et al.  Morphological prediction and its application to the synthesis of polyacrylate/polysiloxane core/shell latex particles , 2001 .

[12]  Zhicheng Zhang,et al.  Copolymerization of styrene with acrylates in emulsion and microemulsion , 1998 .

[13]  S. Fu,et al.  Synthesis of nanosize poly(methyl methacrylate) microlatexes with high polymer content by a modified microemulsion polymerization , 1998 .

[14]  Xiaoli Zhu,et al.  Graft emulsion copolymerization of acrylates and siloxane , 1997 .

[15]  Shi-Yow Lin,et al.  Emulsion polymerization of styrene stabilized by mixed anionic and nonionic surfactants , 1997 .

[16]  S. Devi,et al.  High solids content semicontinuous microemulsion copolymerization of methylmethacrylate and butylacrylate , 1997 .