Alkali-activated complex binders from class C fly ash and Ca-containing admixtures.

Processes that maximize utilization of industrial solid wastes are greatly needed. Sodium hydroxide and sodium silicate solution were used to create alkali-activated complex binders (AACBs) from class C fly ash (CFA) and other Ca-containing admixtures including Portland cement (PC), flue gas desulfurization gypsum (FGDG), and water treatment residual (WTR). Specimens made only from CFA (CFA100), or the same fly ash mixed with 40 wt% PC (CFA60-PC40), with 10 wt% FGDG (CFA90-FGDG10), or with 10 wt% WTR (CFA90-WTR10) had better mechanical performance compared to binders using other mix ratios. The maximum compressive strength of specimens reached 80.0 MPa. Geopolymeric gel, sodium polysilicate zeolite, and hydrated products coexist when AACB reactions occur. Ca from CFA, PC, and WTR precipitated as Ca(OH)(2), bonded in geopolymers to obtain charge balance, or reacted with dissolved silicate and aluminate species to form calcium silicate hydrate (C-S-H) gel. However, Ca from FGDG probably reacted with dissolved silicate and aluminate species to form ettringite. Utilization of CFA and Ca-containing admixtures in AACB is feasible. These binders may be widely utilized in various applications such as in building materials and for solidification/stabilization of other wastes, thus making the wastes more environmentally benign.

[1]  J. Deventer,et al.  Reaction mechanisms in the geopolymeric conversion of inorganic waste to useful products. , 2007, Journal of hazardous materials.

[2]  C. Kaps,et al.  Alkali-activated metakaolin-slag blends—performance and structure in dependence of their composition , 2007 .

[3]  L Zou,et al.  Reduction of metal leaching in brown coal fly ash using geopolymers. , 2004, Journal of hazardous materials.

[4]  S. Antiohos,et al.  A novel way to upgrade the coarse part of a high calcium fly ash for reuse into cement systems. , 2007, Waste management.

[5]  Hua Xu.  Geopolymerisation of aluminosilicate minerals , 2002 .

[6]  Xiaolu Guo,et al.  Use of Heat‐Treated Water Treatment Residuals in Fly Ash‐Based Geopolymers , 2010 .

[7]  Rubina Chaudhary,et al.  Mechanism of geopolymerization and factors influencing its development: a review , 2007 .

[8]  Ángel Palomo,et al.  Composition and Microstructure of Alkali Activated Fly Ash Binder: Effect of the Activator , 2005 .

[9]  Jianmin Wang,et al.  Impacts of pH and ammonia on the leaching of Cu(II) and Cd(II) from coal fly ash. , 2006, Chemosphere.

[10]  J.S.J. van Deventer,et al.  Geopolymerisation kinetics. 2. Reaction kinetic modelling , 2007 .

[11]  María Teresa Blanco-Varela,et al.  Chemical stability of cementitious materials based on metakaolin , 1999 .

[12]  X. Guihua.  Progress of modification and application of coal fly ash in water treatment , 2008 .

[13]  Á. Palomo,et al.  Characterisation of fly ashes. Potential reactivity as alkaline cements , 2003 .

[14]  John L. Provis,et al.  Effect of Calcium Silicate Sources on Geopolymerisation , 2008 .

[15]  J. Provis,et al.  Designing Precursors for Geopolymer Cements , 2008 .

[16]  Raymond John Hodges,et al.  Using inorganic polymer to reduce leach rates of metals from brown coal fly ash , 2004 .

[17]  J. Deventer,et al.  The geopolymerisation of alumino-silicate minerals , 2000 .

[18]  J. Davidovits.  Geopolymers : inorganic polymeric new materials , 1991 .

[19]  J. C. Swanepoel,et al.  Utilisation of fly ash in a geopolymeric material , 2002 .