Withdrawal strength of fasteners in rice straw fibre-thermoplastic composites under dry and wet conditions

Abstract The withdrawal strength of nail and screw fasteners has been studied in rice straw fibre-thermoplastic composites. Two types of thermoplastic, virgin polyethylene (PE) and polypropylene (PP), were selected as separate composite matrices. Three levels of dry rice straw fibre, 45%, 60% and 75%, based on the composition by weight and passed through a 40-mesh size screen was mixed with the polymeric matrices without and with 2% (based on weight) maleic anhydride grafted polypropylene (MAPP) as coupling agent. A dry-blending method was used for compounding the materials. The 12 formulations for the polymer composites were used to prepare samples with dimensions 25 cm by 15 cm by 1 cm. The final composites were made by pressing the prepared mats between the hot plates of a compression press by employing combinations of temperature and pressure in three stages. After keeping the composites at room temperature for 15 days, the withdrawal strengths of nails and screws were measured according to BS Standard (CEN/TS 15534–1:2007) for dry composites. Withdrawal strengths were also measured after immersion of the composites for 24 h in distilled water (wet condition). The results showed that the withdrawal strength of screws is more than that of nails. Also, irrespective of the type of polymer, the percentage of rice straw fibre may significantly influence the withdrawal strength of fasteners, especially at the higher fibre to polymer ratios. Furthermore, it was found that in the wet condition the withdrawal strengths of the nail fasteners are reduced more (73.66%) than for the screws (28.9%).

[1]  A. Dufresne,et al.  Processing and characterization of reinforced polyethylene composites made with lignocellulosic fibers from Egyptian agro-industrial residues , 2008 .

[2]  Qinglin Wu,et al.  Rice straw fiber-reinforced high-density polyethylene composite: Effect of fiber type and loading , 2008 .

[3]  Qinglin Wu,et al.  Wood‐fiber/high‐density‐polyethylene composites: Coupling agent performance , 2005 .

[4]  Jennifer Markarian,et al.  Wood-plastic composites: current trends in materials and processing , 2005 .

[5]  Roger M. Rowell,et al.  Advances and Challenges of Wood Polymer Composites , 2006 .

[6]  Qinglin Wu,et al.  Preparation and properties of recycled HDPE/natural fiber composites , 2007 .

[7]  R. Portier,et al.  Studies on Mechanical Properties of Wood-Polymer Composites , 1997 .

[8]  P. Wambua,et al.  Natural fibres: can they replace glass in fibre reinforced plastics? , 2001 .

[9]  S. Kamel.  Preparation and properties of composites made from rice straw and poly(vinyl chloride) (PVC) , 2004 .

[10]  Michael P. Wolcott,et al.  Opportunities for wood/natural fiber-plastic composites in residential and industrial applications , 2006 .

[11]  J. Markarian.  Outdoor living space drives growth in wood-plastic composites , 2008 .

[12]  Alireza Ashori,et al.  Wood-plastic composites as promising green-composites for automotive industries! , 2008, Bioresource technology.

[13]  John C. F. Walker.  Primary Wood Processing: Principles and Practice , 1993 .

[14]  C. Ha,et al.  Mechanical properties of polypropylene/natural fiber composites: Comparison of wood fiber and cotton fiber , 2008 .

[15]  S. Y. Zhang,et al.  Effects of wood fiber content and coupling agent content on tensile properties of wood fiber polyethylene composites , 2008, Holz als Roh- und Werkstoff.

[16]  Robert H. Falk,et al.  Performance of fasteners in wood flour-thermoplastic composite panels , 2001 .

[17]  S. Hiziroglu,et al.  Some of the properties of wood–plastic composites , 2007 .

[18]  R. Gupta,et al.  Improved wood–plastic composites through better processing , 2008 .

[19]  R. Portier,et al.  Studies on Polymer-Wood Interface Bonding: Effect of Coupling Agents and Surface Modification , 1999 .

[20]  S. Pang,et al.  Dimensional stability and mechanical behaviour of wood–plastic composites based on recycled and virgin high-density polyethylene (HDPE) , 2008 .

[21]  Han-Seung Yang,et al.  Rice straw-wood particle composite for sound absorbing wooden construction materials. , 2003, Bioresource technology.