Exciton localization and large Stokes shift in quaternary BeMgZnO grown by molecular beam epitaxy

Owing to wide range bandgap tunability to more than 5 eV, the quaternary (Be,Mg)ZnO solid solutions are attractive for a variety of UV optoelectronic applications, inclusive of solar blind photodetectors, and intersubband transition devices. The mutual compensation effects of Be and Mg on the formation energy and strain allows a wide range of compositions and bandgaps beyond those achievable by MgZnO and BeZnO ternaries. Localization effects are well pronounced in such wide-bandgap semiconductor alloys due to large differences in metal covalent radii and the lattice constants of the binaries, resulting in strain-driven compositional variations within the film and consequently large potential fluctuations, in addition to that possibly caused by defects. However, carrier localization may suppress recombination through nonradiative channels, and thus, facilitate high-efficiency optoelectronic devices. To investigate potential fluctuations and localization in BexMgyZn(1-x-y)O films grown by plasma-assisted molecular beam epitaxy, optical absorption and steady-state and time-resolved photoluminescence (PL) measurements were performed. O-polar BexMgyZn(1-x-y)O samples grown on GaN templates with compositions up to x = 0.04 and y = 0.18 were used for timeresolved studies, and O-polar BexMgyZn(1-x-y)O samples grown on sapphire with compositions up to x = 0.19 and y = 0.52 were used for absorption measurements. From spectrally resolved PL transients, BeMgZnO samples with higher Mg/Be content ratio were found to exhibit smaller localization depth, Δ0=98 meV for Be0.04Mg0.17Zn0.79O and Δ0=173 meV for Be0.10Mg0.25Zn0.65O, compared to samples with smaller Mg/Be ratio, Δ0=268 meV for Be0.11Mg0.15Zn0.74O. Similar correlation is observed in temporal redshift of the PL peak position of 8 meV, 42 meV and 55 meV for Be0.04Mg0.17Zn0.79O, Be0.10Mg0.25Zn0.65O and Be0.11Mg0.15Zn0.74O, respectively, that originates from potential fluctuations and removal of band filling effect in the localized states. PL transients indicate that emission at low temperature is dominated by recombination of localized excitons, which exhibit decay times as long as τ = 0.36 ns at the peak position. The Sshaped behavior of PL peak with change in temperature was observed for the quaternary alloy Be0.04Mg0.17Zn0.79O. The degree of localization σ was determined to be 22 meV. Relatively high potential fluctuations and localization energy lead to a strong Stokes shift, which increased with bandgap reaching ~0.5 eV for O-polar BeMgZnO on sapphire with 4.6 eV absorption edge.

[1]  Beatriz Cordero,et al.  Covalent radii revisited. , 2008, Dalton transactions.

[2]  Petr G. Eliseev,et al.  BLUE TEMPERATURE-INDUCED SHIFT AND BAND-TAIL EMISSION IN INGAN-BASED LIGHT SOURCES , 1997 .

[3]  Alloy-fluctuation-induced exciton localization in high-Mg-content (0.27 <= x <= 0.55) wurtzite MgxZn1-xO epilayers , 2010 .

[4]  B. Pan,et al.  Wide range bandgap modulation based on ZnO-based alloys and fabrication of solar blind UV detectors with high rejection ratio. , 2014, ACS applied materials & interfaces.

[5]  Yang Jiang,et al.  Temperature-dependent photoluminescence in light-emitting diodes , 2014, Scientific Reports.

[6]  M. Baba,et al.  Temperature dependence of near ultraviolet photoluminescence in ZnO/(Mg, Zn)O multiple quantum wells , 2001 .

[7]  J. Bergman,et al.  Mechanism for radiative recombination in ZnCdO alloys , 2007 .

[8]  Solar-blind wurtzite MgZnO alloy films stabilized by Be doping , 2013 .

[9]  H. Morkoç,et al.  Enhancement of Be and Mg incorporation in wurtzite quaternary BeMgZnO alloys with up to 5.1 eV optical bandgap , 2014 .

[10]  Michael A. Reshchikov,et al.  Hydrogen-carbon complexes and the blue luminescence band in GaN. , 2016 .

[11]  Lattice parameters and electronic structure of BeMgZnO quaternary solid solutions: Experiment and theory , 2016 .

[12]  Bruce W Wessels,et al.  Behavior of 2.8- and 3.2-eV photoluminescence bands in Mg-doped GaN at different temperatures and excitation densities , 1999 .

[13]  Y. Chen,et al.  Photoluminescence properties of ZnO epilayers grown on CaF2(111) by plasma assisted molecular beam epitaxy , 2000 .

[14]  M. Eickhoff,et al.  Optical properties of MgZnO alloys: Excitons and exciton-phonon complexes , 2011 .

[15]  H. Morkoç,et al.  Nondestructive atomic compositional analysis of BeMgZnO quaternary alloys using ion beam analytical techniques , 2015 .