Effect of high temperatures on the physical and mechanical properties of HDPE geomembranes in air

ABSTRACT: The effect of elevated temperatures, particularly between 95 and 115°C as encountered in some geoenvironmental applications, on the physical and mechanical properties of high-density polyethylene (HDPE) geomembranes (GMBs) is examined. Four commercially available HDPE GMBs were incubated in air at temperatures ≥ 85°C. Investigation of the thermograms by differential scanning calorimetry showed a significant change in the polymer morphology with an increase of the incubation temperature and duration, especially at 105 and 115°C. The morphological changes due to annealing involve thickening of the lamella crystals of the polymer and a change in the tie molecules joining the lamella crystals. The effect of annealing was most evident in the stress crack resistance of the GMB incubated at 105 and 115°C prior to polymer degradation. In particular, an increase in stress crack resistance due to annealing could mask the effects of polymer degradation at temperatures above 95°C. Changes in morphology did ...

[1]  M. Y. Hellman,et al.  Autoxidation of semicrystalline polyethylene , 1966 .

[2]  R. Lang,et al.  Influence of various stabilizer systems on the ageing behavior of PE–MD—II. Ageing of pipe specimens in air and water at elevated temperatures , 1998 .

[3]  R. Rowe,et al.  Aging of High-Density Polyethylene Geomembranes of Three Different Thicknesses , 2014 .

[4]  R. Brachman,et al.  Antioxidant Depletion from a High Density Polyethylene Geomembrane under Simulated Landfill Conditions , 2010 .

[5]  Jiasong He,et al.  Definitions of terms relating to crystalline polymers (IUPAC Recommendations 2011) , 2011 .

[6]  U. Gedde,et al.  Degradation of unstabilized medium-density polyethylene pipes in hot-water applications , 1994 .

[7]  N. Brown,et al.  Effect of thermal history on the initiation of slow crack growth in linear polyethylene , 1987 .

[8]  R. Rowe,et al.  Durability of Three HDPE Geomembranes Immersed in Different Fluids at 85°C , 2015 .

[9]  John Scheirs,et al.  A Guide to Polymeric Geomembranes , 2009 .

[10]  R. Rowe,et al.  Effect of leachate composition on the long-term performance of a HDPE geomembrane ☆ , 2014 .

[11]  R. Rowe,et al.  Effects of Thickness on the Aging of HDPE Geomembranes , 2010 .

[12]  P. Castell,et al.  Anisotropic thermosets from liquid‐crystalline azomethynic epoxy resins and primary aromatic diamines , 2003 .

[13]  U. Gedde,et al.  Molecular structure and morphology of crosslinked polyethylene in an aged hot‐water pipe , 1990 .

[14]  W. Müller,et al.  Oxidative resistance of high-density polyethylene geomembranes , 2003 .

[15]  N. Brown,et al.  The effect of blending high-density and linear low-density polyethylenes on slow crack growth , 1993 .

[16]  W. Müller,et al.  ANTIOXIDANT DEPLETION AND OIT VALUES OF HIGH IMPACT PP STRANDS , 2009 .

[17]  Sabira.  Time and temperature effects on geomembrane strain from a gravel particle subjected to sustained vertical force , 2012 .

[18]  R. Rowe,et al.  Antioxidant depletion from five geomembranes of same resin but of different thicknesses immersed in leachate , 2014 .

[19]  A. Holmström.  The Course of Thermooxidative Degradation of LD- and HD- Polyethylene under Accelerated Testing Conditions , 1979 .

[20]  Grant D. Smith,et al.  Molecular structure, morphology, and antioxidant consumption in medium density polyethylene pipes in hot-water applications , 1992 .

[21]  F. Abdelaal.  Durability of HDPE Geomembranes for Municipal Solid Waste Landfill Applications , 2013 .

[22]  R. K. Rowe,et al.  Effects of blown film process on initial properties of HPDE geomembranes of different thicknesses , 2014 .

[23]  R. Kerry Rowe,et al.  Aging of HDPE Geomembrane in Three Composite Landfill Liner Configurations , 2008 .

[24]  M. Islam,et al.  LONG-TERM PERFORMANCE OF HDPE GEOMEMBRANES AS LANDFILL LINERS , 2009 .

[25]  R. Kerry.  Short- and long-term leakage through composite liners. The 7th Arthur Casagrande Lecture1 1This lecture was presented at the 14th Pan-American Conference on Soil Mechanics and Geotechnical Engineering, Toronto, Ont., October 2011, and a pre-print appeared in the conference proceedings. , 2012 .

[26]  C. Benson,et al.  Effect of acidic mine drainage on the polymer properties of an HDPE geomembrane , 2004 .

[27]  B. Wunderlich,et al.  A Study of Equilibrium Melting of Polyethylene , 1977 .

[28]  Effects of annealing on the hierarchical crystalline structures and mechanical properties of injection‐molded bars of high‐density polyethylene , 2014 .

[29]  H. Hendus,et al.  Schmelzpunkt und kristallitgröße von aus schmelze und lösung kristallisiertem polyäthylen , 1968 .

[30]  W. Hawkins,et al.  Thermal and oxidative degradation of polymers , 1964 .

[31]  R. Cairncross,et al.  Depletion mechanism of antioxidants in MDPE-clay nanocomposites under thermal aging , 2012 .

[32]  R. K. Rowe,et al.  Antioxidant depletion of HDPE geomembrane with sand protection layer , 2013 .

[33]  Timothy D. Stark,et al.  Aluminum Waste Reaction Indicators in a Municipal Solid Waste Landfill , 2012 .

[34]  J. Seppälä,et al.  Specific structures enabled by metallocene catalysis in polyethenes , 2004 .

[35]  S. Al‐Malaika.  Perspectives in stabilisation of polyolefins , 2004 .

[36]  J. Scheirs,et al.  Characterizing the solid-state thermal oxidation of poly(ethylene oxide) powder , 1991 .

[37]  R. Rowe,et al.  Degradation behaviour of HDPE geomembranes with high and low initial high-pressure oxidative induction time , 2014 .

[38]  R. Lang,et al.  Influence of various stabilizer systems on the ageing behavior of PE–MD—I. Hot-water ageing of compression molded plaques , 1998 .

[39]  R. K. Rowe,et al.  Brittle rupture of an aged HPDE geomembrane at local gravel indentations under simulated field conditions , 2014 .

[40]  Aliakbar Akbarzadeh,et al.  Heat extraction methods from salinity-gradient solar ponds and introduction of a novel system of heat extraction for improved efficiency , 2011 .

[41]  R. Koerner,et al.  Antioxidant depletion lifetime in high density polyethylene geomembranes , 1998 .

[42]  R. Rowe,et al.  Ageing of HDPE geomembrane exposed to air, water and leachate at different temperatures , 2009 .

[43]  R. Rowe,et al.  Effect of high temperatures on antioxidant depletion from different HDPE geomembranes , 2014 .

[44]  M. Miles,et al.  Growth of polymer crystals during annealing , 1976 .

[45]  J. Luongo.  Effect of oxidation on polyethylene morphology , 1963 .

[46]  L. Reich,et al.  Structure vs stability in polymer degradation , 1980 .