Enhancement of Iron Melting Rate under the Co-existence of Graphite and Wüstite

Carburization and melting processes of solid Fe under the co-existence of graphite and wustite has been investigated based on a confocal laser scanning microscope “in-situ” observation of the movement of the interface between Fe–C melt and solid Fe at 1523 K. In the experiments, strong stirring flow at the surface of the Fe–C melt is observed. This flow is found to be Marangoni flow and is introduced by the surface tension gradient due to the difference of oxygen concentration between the Fe–C melt interface with graphite and solid iron. The velocity of Marangoni flow is measured from the moving velocities of bubbles at the molten Fe–C surface. The melting rate of Fe is analyzed by computational fluid flow simulations of the Fe–C melt. Based on these results, it is confirmed that the carburization and melting rate of solid Fe can be enhanced by allowing Fe–C melt to come into contact with wustite and graphite simultaneously.

[1]  Y. Sasaki,et al.  Carburization Degree of Iron Nugget Produced by Rapid Heating of Powdery Iron, Iron Oxide in Slag and Carbon Mixture , 2008 .

[2]  Y. Kashiwaya,et al.  In Situ Observation of Reduction Behavior of Hematite with Solid Carbon and Crystallographic Orientation between Hematite and Magnetite , 2007 .

[3]  S. Endo,et al.  Carburized Carbon Content of Reduced Iron and Direct Carburization in Carbon Composite Iron Ore Pellets Heated at Elevated Temperature , 2004 .

[4]  Y. Kashiwaya,et al.  Gas Evolution during Mechanical Milling of Hematite-Graphite Mixture , 2004 .

[5]  S. Endo,et al.  Reactions, Coalescence of Reduced Iron Particles, and Liberation of Carbon Particles in Carbon Composite Iron Ore Pellets , 2004 .

[6]  Y. Iguchi,et al.  Rate of Direct Reactions Measured in Vacuum of Iron Ore-Carbon Composite Pellets Heated at High Temperatures: Influence of Carbonaceous Materials, Oxidation Degree of Iron Oxides and Temperature , 2004 .

[7]  K. Nagata,et al.  NEW IRONMAKING PROCESS FROM THE VIEWPOINT OF CARBURIZATION AND IRON MELTING AT LOW TEMPERATURE , 2003 .

[8]  K. Nagata,et al.  Mechanisms of Pig-iron Making from Magnetite Ore Pellets Containing Coal at Low Temperature , 2001 .

[9]  Kuniyoshi Ishii,et al.  Reaction Behavior of Facing Pair Between Hematite and Graphite: A Coupling Phenomenon of Reduction and Gasification , 2001 .

[10]  Y. Sasaki,et al.  The Effect of the Liquid Fe–C Phase on the Kinetics in the Carburization of Iron by CO at 1523 K , 2001 .

[11]  D. R. Poirier,et al.  Interfacial Properties of Dilute Fe-O-S Melts on Alumina Substrates , 1998 .