Optimization of conditions for the preparation of activated carbon from olive stones for application in gold recovery

The purpose of this study is to prepare a new activated carbon from olive stones for use in gold recovery by carbon-in-leach (CIL) and carbon-in-pulp (CIP). The preparation method chosen was physical activation using steam. The effect of four process parameters: the residence time for carbonization, the activation temperature, the residence time for activation, and steam flow, were studied by the mean of response surface method (RSM) in order to optimize the yield, iodine index, and attrition characteristics. These two last responses were used as primary indicators of gold recovery capacity and mechanical strength. The results obtained show that optimal activated carbon can be prepared under the following conditions: a carbonization time of 157 minutes, activation at 921°C for 53 minutes, and a water vapour flow of 0.18 mL/min. This optimum carbon has an iodine value greater than 1100 mg/g and an attrition index in the order of 0.74%. These values reflect the quality of the precursor (olive stones) as a raw material for the development of an effective new activated carbon for the gold mining industry.

[1]  É. Cavalheiro,et al.  The use of DSC curves to determine the acetylation degree of chitin/chitosan samples , 2006 .

[2]  M. Dantas,et al.  Selective adsorption of gold over copper cyanocomplexes on activated carbon , 2014 .

[3]  R. García,et al.  Retention of aurocyanide and thiourea-gold complexes on activated carbons obtained from lignocellulosic materials , 1997 .

[4]  A. Arol,et al.  Gold cyanide adsorption characteristics of activated carbon of non-coconut shell origin , 2002 .

[5]  I. Tan,et al.  Preparation of oil palm empty fruit bunch-based activated carbon for removal of 2,4,6-trichlorophenol: optimization using response surface methodology. , 2009, Journal of hazardous materials.

[6]  C. Saka,et al.  Preparation and characterization of activated carbon from acorn shell by physical activation with H2O-CO2 in two-step pretreatment. , 2013, Bioresource technology.

[7]  A. Dutta,et al.  Production of activated carbon from coconut shell: optimization using response surface methodology. , 2008, Bioresource technology.

[8]  A. B. Fuertes,et al.  The production of carbon materials by hydrothermal carbonization of cellulose , 2009 .

[9]  Shaoxian Song,et al.  Adsorption of the complex ion Au(CN)2- onto sulfur-impregnated activated carbon in aqueous solutions. , 2010, Journal of colloid and interface science.

[10]  P. Szabó-Révész,et al.  DSC, X-ray and FTIR studies of a gemfibrozil/dimethyl-β-cyclodextrin inclusion complex produced by co-grinding. , 2012, Journal of pharmaceutical and biomedical analysis.

[11]  S. Bhatia,et al.  Optimization of microporous palm shell activated carbon production for flue gas desulphurization: experimental and statistical studies. , 2009, Bioresource technology.

[12]  Suhas,et al.  Lignin--from natural adsorbent to activated carbon: a review. , 2007, Bioresource technology.

[13]  Paul T. Williams,et al.  Activated carbons prepared from refuse derived fuel and their gold adsorption characteristics , 2010, Environmental technology.

[14]  D. Fawcett,et al.  Adsorption of the aurocyanide, Au(CN)2- complex on granular activated carbons derived from macadamia nut shells – A preliminary study , 2011 .

[15]  K. Gergova,et al.  A comparison of adsorption characteristics of various activated carbons , 2007 .

[16]  M. Soleimani,et al.  Adsorption of gold ions from industrial wastewater using activated carbon derived from hard shell of apricot stones - an agricultural waste. , 2008, Bioresource technology.

[17]  Andrew J. McAloon,et al.  Acid-activated carbons from almond shells: physical, chemical and adsorptive properties and estimated cost of production. , 2000 .

[18]  Nilgün Karatepe,et al.  Influence of preparation conditions on porous structures of olive stone activated by H3PO4 , 2010 .

[19]  M. Valix,et al.  Modelling of gold (I) cyanide adsorption based on the properties of activated bagasse , 2003 .

[20]  C. A. Snyders,et al.  The extraction of Pt, Pd and Au from an alkaline cyanide simulated heap leachate by granular activated carbon , 2014 .

[21]  N. Alonso-Morales,et al.  Preparation of granular activated carbons from grape seeds by cycles of liquid phase oxidation and thermal desorption , 2014 .

[22]  J. Howse,et al.  The effect of the hydrothermal carbonization process on palm oil empty fruit bunch , 2012 .

[23]  U. Westermark,et al.  Determination of formic-acid and acetic acid concentrations formed during hydrothermal treatment of birch wood and its relation to colour, strength and hardness , 2006, Wood Science and Technology.

[24]  V. Gómez-Serrano,et al.  Enhanced adsorption of metal ions onto functionalized granular activated carbons prepared from cherry stones. , 2009, Journal of hazardous materials.

[25]  Q. Guo,et al.  Preparation and characteristics of medicinal activated carbon powders by CO2 activation of peanut shells , 2013 .

[26]  F. J. Maldonado-Hódar,et al.  Optimization of conditions for the preparation of activated carbons from olive-waste cakes , 2001 .