Degradation progress and protection of cement mortars partially immersed in sulfate–chloride solution

In sulfate-laden environments, salt weathering presents a serious threat to structures. Numerous explorations have focused on weathering due to partial immersion in a single-sulfate solution, but t...

[1]  Jianming Gao,et al.  Deterioration mechanism of plain and blended cement mortars partially exposed to sulfate attack , 2017 .

[2]  Jianming Gao,et al.  Degradation progress of concrete subject to combined sulfate-chloride attack under drying-wetting cycles and flexural loading , 2017 .

[3]  Jianming Gao,et al.  Evaluation of the damage process of recycled aggregate concrete under sulfate attack and wetting-drying cycles , 2017 .

[4]  Geert De Schutter,et al.  The role of Ca(OH)2 in sulfate salt weathering of ordinary concrete , 2016 .

[5]  Beatriz Menéndez,et al.  Effect of mixed vs single brine composition on salt weathering in porous carbonate building stones for different environmental conditions , 2016 .

[6]  A. Soliman,et al.  Effect of surface treatment on durability of concrete exposed to physical sulfate attack , 2014 .

[7]  A. Soliman,et al.  Investigation of concrete exposed to dual sulfate attack , 2014 .

[8]  Jian-kang Chen,et al.  Study on the expansion of concrete under attack of sulfate and sulfate–chloride ions , 2013 .

[9]  N. Belie,et al.  Test Methods for Resistance of Concrete to Sulfate Attack – A Critical Review , 2013 .

[10]  S. Tsivilis,et al.  Sulfate resistance of limestone cement concrete exposed to combined chloride and sulfate environment at low temperature , 2012 .

[11]  Zhiwu Yu,et al.  Chemical sulfate attack performance of partially exposed cement and cement + fly ash paste , 2012 .

[12]  M. Bassuoni,et al.  Physical Salt Attack on Concrete , 2011 .

[13]  C. Oguchi,et al.  Resistance of plain and blended cement mortars exposed to severe sulfate attacks , 2011 .

[14]  Barbara Lothenbach,et al.  Impact of chloride on the mineralogy of hydrated portland cement systems , 2010 .

[15]  S. Goñi,et al.  Effect of temperature on the durability of class C fly ash belite cement in simulated radioactive liquid waste: synergy of chloride and sulphate ions. , 2009, Journal of hazardous materials.

[16]  David Benavente,et al.  Weathering of limestone building material by mixed sulfate solutions. Characterization of stone microstructure, reaction products and decay forms , 2008 .

[17]  Ronan Hébert,et al.  Modification of the porous network by salt crystallization in experimentally weathered sedimentary stones , 2008 .

[18]  M. Nehdi,et al.  Behavior of blended cement mortars exposed to sulfate solutions cycling in relative humidity , 2005 .

[19]  L. Pel,et al.  Salt transport and crystallization in porous building materials. , 2003, Magnetic resonance imaging.

[20]  Y. Cai,et al.  Study of chloride binding and diffusion in GGBS concrete , 2003 .

[21]  C. Rodriguez-Navarro,et al.  Salt weathering: influence of evaporation rate, supersaturation and crystallization pattern , 1999 .

[22]  Y. Xu.  The influence of sulphates on chloride binding and pore solution chemistry , 1997 .

[23]  Claude Hammecker,et al.  The importance of the petrophysical properties and external factors in the stone decay on monuments , 1995 .

[24]  C Arya,et al.  Effect of cement type on chloride binding and corrosion of steel in concrete , 1995 .

[25]  W H Harrison,et al.  EFFECT OF CHLORIDE IN MIX INGREDIENTS ON SULPHATE RESISTANCE OF CONCRETE , 1990 .

[26]  T. J. Reading.  Physical Aspects of Sodium Sulfate Attack on Concrete , 1982 .