Modeling of Dendritic Evolution of Continuously Cast Steel Billet with Cellular Automaton

In order to predict the dendritic evolution during the continuous steel casting process, a simple mechanism to connect the heat transfer at the macroscopic scale and the dendritic growth at the microscopic scale was proposed in the present work. As the core of the across-scale simulation, a two-dimensional cell automaton (CA) model with a decentered square algorithm was developed and parallelized. Apart from nucleation undercooling and probability, a temperature gradient was introduced to deal with the columnar-to-equiaxed transition (CET) by considering its variation during continuous casting. Based on the thermal history, the dendritic evolution in a 4 mm × 40 mm region near the centerline of a SWRH82B steel billet was predicted. The influences of the secondary cooling intensity, superheat, and casting speed on the dendritic structure of the billet were investigated in detail. The results show that the predicted equiaxed dendritic solidification of Fe-5.3Si alloy and columnar dendritic solidification of Fe-0.45C alloy are consistent with in situ experimental results [Yasuda et al. Int J Cast Metals Res 22:15–21 (2009); Yasuda et al. ISIJ Int 51:402–408 (2011)]. Moreover, the predicted dendritic arm spacing and CET location agree well with the actual results in the billet. The primary dendrite arm spacing of columnar dendrites decreases with increasing secondary cooling intensity, or decreasing superheat and casting speed. Meanwhile, the CET is promoted as the secondary cooling intensity and superheat decrease. However, the CET is not influenced by the casting speed, owing to the adjusting of the flow rate of secondary spray water. Compared with the superheat and casting speed, the secondary cooling intensity can influence the cooling rate and temperature gradient in deeper locations, and accordingly exerts a more significant influence on the equiaxed dendritic structure.

[1]  C. Bernhard,et al.  Identification of Defect Prone Peritectic Steel Grades by Analyzing High-Temperature Phase Transformations , 2013, Metallurgical and Materials Transactions A.

[2]  Toshihiko Emi,et al.  Steelmaking Technology for the Last 100 Years: Toward Highly Efficient Mass Production Systems for High Quality Steels , 2015 .

[3]  T. Nagira,et al.  In situ observation of solidification phenomena in Al–Cu and Fe–Si–Al alloys , 2009 .

[4]  Yiyi Li,et al.  Multi-scale Simulation for the Columnar to Equiaxed Transition in the Weld Pool , 2016 .

[5]  Q. Zhai,et al.  A Thermal Simulation Method for Solidification Process of Steel Slab in Continuous Casting , 2016, Metallurgical and Materials Transactions B.

[6]  G. G. Stokes.  "J." , 1890, The New Yale Book of Quotations.

[7]  Andrew G. Glen,et al.  APPL , 2001 .

[8]  S. Luo,et al.  Development of a CA-FVM Model with Weakened Mesh Anisotropy and Application to Fe–C Alloy , 2016 .

[9]  T. Takaki.  Phase-field Modeling and Simulations of Dendrite Growth , 2014 .

[10]  Y. Shin,et al.  Multiscale Modeling of Transport Phenomena and Dendritic Growth in Laser Cladding Processes , 2011 .

[11]  M. Rettenmayr,et al.  Perspectives for cellular automata for the simulation of dendritic solidification – A review , 2014 .

[12]  Miao‐yong Zhu,et al.  Dendritic growth of high carbon iron-based alloy under constrained melt flow , 2014 .

[13]  V. Ludlow,et al.  Strategy to minimise central segregation in high carbon steel grades during billet casting , 2005 .

[14]  T. Nagira,et al.  In-situ observation of peritectic solidification in Sn-Cd and Fe-C alloys , 2012 .

[15]  J.-L. Desbiolles,et al.  Modeling of equiaxed microstructure formation in casting , 1989 .

[16]  Miao‐yong Zhu,et al.  Numerical Simulation of Dendritic Growth of Continuously Cast High Carbon Steel , 2014, Metallurgical and Materials Transactions A.

[17]  Amir Khajepour,et al.  Phase-field simulation of solidification morphology in laser powder deposition of Ti-Nb alloys , 2012 .

[18]  Seppo Louhenkilpi,et al.  Numerical Simulation of Solidification Structure of High Carbon Steel in Continuous Casting Using Cellular Automaton Method , 2012 .

[19]  Abdellah Kharicha,et al.  Application of Microprobe Analysis to the Reconstruction and Characterization of Dendritic Structures , 2013, Metallurgical and Materials Transactions A.

[20]  Polydimensional modelling of dendritic growth and microsegregation in multicomponent alloys , 2010 .

[21]  H. Emmerich,et al.  Phase-field simulation of a Fe-Mn alloy under forced flow conditions , 2009 .

[22]  Margaret Nichols.  Trans , 2015, De-centering queer theory.

[23]  S. Osher,et al.  A Simple Level Set Method for Solving Stefan Problems , 1997, Journal of Computational Physics.

[24]  Miaoyong Zhu,et al.  Analysis and Application of Soft Reduction Amount for Bloom Continuous Casting Process , 2014 .

[25]  Miao‐yong Zhu,et al.  Center Segregation with Final Electromagnetic Stirring in Billet Continuous Casting Process , 2017, Metallurgical and Materials Transactions B.

[26]  Y. Shin,et al.  Numerical Modeling of Transport Phenomena and Dendritic Growth in Laser Spot Conduction Welding of 304 Stainless Steel , 2012 .

[27]  Miao‐yong Zhu,et al.  Numerical Simulation of Three-Dimensional Dendritic Growth of Alloy: Part I—Model Development and Test , 2016, Metallurgical and Materials Transactions A.

[28]  D. Eskin,et al.  Phase-field modelling of microstructure formation during the solidification of continuously cast low carbon and HSLA steels , 2012 .

[29]  R. Qin,et al.  A Three Dimensional Cellular Automata Model for Dendrite Growth in Non‐Equilibrium Solidification of Binary Alloy , 2015 .

[30]  Miao‐yong Zhu,et al.  Numerical Simulation of Three-Dimensional Dendritic Growth of Alloy: Part II—Model Application to Fe-0.82WtPctC Alloy , 2016, Metallurgical and Materials Transactions A.

[31]  G. Lesoult,et al.  Macrosegregation in steel strands and ingots : Characterisation, formation and consequences , 2005 .

[32]  J. Hunt,et al.  Steady state columnar and equiaxed growth of dendrites and eutectic , 1984 .

[33]  S. Felicelli,et al.  Dendrite growth simulation during solidification in the LENS process , 2010 .

[34]  Lifeng Zhang,et al.  Analysis on the Deflection Angle of Columnar Dendrites of Continuous Casting Steel Billets Under the Influence of Mold Electromagnetic Stirring , 2016, Metallurgical and Materials Transactions A.

[35]  Wang Su,et al.  Heat Transfer and Central Segregation of Continuously Cast High Carbon Steel Billet , 2014 .

[36]  Pingwen Zhang,et al.  A cellular automaton technique for modelling of a binary dendritic growth with convection , 2007 .

[37]  Nozaki Tsutomu,et al.  A Secondary Cooling Pattern for Preventing Surface Cracks of Continuous Casting Slab , 1978 .

[38]  Zhao Jiuzhou,et al.  DEVELOPMENT OF CELLULAR AUTOMATON MODELS AND SIMULATION METHODS FOR SOLIDIFICATION OF ALLOYS , 2014 .

[39]  B. Santillana,et al.  Multi-Phase-Field Modeling of Solidification in Technical Steel Grades , 2012, Transactions of the Indian Institute of Metals.

[40]  S. Pan,et al.  A three-dimensional sharp interface model for the quantitative simulation of solutal dendritic growth , 2010 .

[41]  H. Esaka,et al.  Mathematical Analysis of Segregations in Continuously-cast Slabs , 1984 .

[42]  Yiyi Li,et al.  Modeling of morphological evolution of columnar dendritic grains in the molten pool of gas tungsten arc welding , 2014 .

[43]  K. Uesugi,et al.  Development of X-ray Imaging for Observing Solidification of Carbon Steels , 2011 .