Influence of plate position, tool offset and tool rotational speed on mechanical properties and microstructures of dissimilar Al/Cu friction stir welding joints

Abstracts In this research, dissimilar friction stir welding between aluminium (Al) and copper (Cu) is investigated. The experimental results indicate that high quality joints can be obtained by placing the Cu plate on the advancing side of the tool rotation. Further improvement of mechanical properties and defect free joints could be obtained under specific critical offset towards the Al side. The maximum ultimate tensile strength of the weld was 95% of the Al base metal and bending angle was around 65°. The Vickers micro-hardness distributions indicate that hardness values increased from Al to Cu side and maximum at the joint interfaces and hardness at the bottom of the nugget zone (NZ) was higher compare to middle and top layers. Broken grains were observed in the fractograph images at nano level. The XRD analysis of intermetallic compounds revealed that percentage of Cu and Al are almost same at the joint center and maximum at 2 mm away from the joint center towards Al and Cu sides, respectively. Line scanning indicated mixed flow of Al/Cu materials throughout the NZ. Microstructural analysis revealed the variation of the grain size in the weld zones and also with the process parameters.

[1]  Radovan Kovacevic,et al.  Microstructural evolution in the friction stir welded 6061 aluminum alloy (T6-temper condition) to copper , 2006 .

[2]  Sukhomay Pal,et al.  Multi-response optimization of process parameters in friction stir welded AM20 magnesium alloy by Taguchi grey relational analysis , 2015 .

[3]  Rajiv S. Mishra,et al.  Friction Stir Welding and Processing , 2007 .

[4]  Guillaume Racineux,et al.  Interfacial Reaction during Friction Stir Welding of Al and Cu , 2011 .

[5]  M. Y. Yau,et al.  Formation of Al2Cu and AlCu intermetallics in Al(Cu) alloy matrix composites by reaction sintering , 2004 .

[6]  G. Grant,et al.  Friction Stir Lap Welding of Magnesium Alloy to Steel: A Preliminary Investigation , 2010 .

[7]  Peng Liu,et al.  Microstructure and XRD analysis of FSW joints for copper T2/aluminium 5A06 dissimilar materials , 2008 .

[8]  V. Jayabalan,et al.  Tool travel speed effects on the microstructure of friction stir welded aluminum–copper joints , 2015 .

[9]  Altino Loureiro,et al.  Study of the welding conditions during similar and dissimilar aluminium and copper welding based on torque sensitivity analysis , 2012 .

[10]  Antonino Squillace,et al.  Microstructural aspects in Al–Cu dissimilar joining by FSW , 2015 .

[11]  Tomotake Hirata,et al.  Comprehensive analysis of joint strength for dissimilar friction stir welds of mild steel to aluminum alloys , 2009 .

[12]  Sindo Kou,et al.  Al-to-Cu Friction Stir Lap Welding , 2011, Metallurgical and Materials Transactions A.

[13]  Esther T. Akinlabi,et al.  Effect of Shoulder Size on Weld Properties of Dissimilar Metal Friction Stir Welds , 2012, Journal of Materials Engineering and Performance.

[14]  Datong Zhang,et al.  Microstructure and mechanical properties of dissimilar pure copper/1350 aluminum alloy butt joints by friction stir welding , 2012 .

[15]  B. Xiao,et al.  Effect of friction stir welding parameters on the microstructure and mechanical properties of the dissimilar Al-Cu joints , 2011 .

[16]  Caiwang Tan,et al.  Microstructural evolution and mechanical properties of dissimilar Al–Cu joints produced by friction stir welding , 2013 .

[17]  R. Karppi,et al.  The application of electron beam welding for the joining of dissimilar metals: an overview , 1996 .

[18]  V. Subramanya Sarma,et al.  Effect of post weld heat treatment on the microstructure and tensile properties of dissimilar friction stir welded AA 2219 and AA 6061 alloys , 2009 .

[19]  A. Tavakoli,et al.  The influences of rotational and welding speeds on microstructures and mechanical properties of friction stir welded Al5083 and commercially pure copper sheets lap joints , 2013 .

[20]  A. Loureiro,et al.  Influence of Tool Offsetting on the Structure and Morphology of Dissimilar Aluminum to Copper Friction-Stir Welds , 2012, Metallurgical and Materials Transactions A.

[21]  Jun Shen,et al.  Microstructural characterisation and mechanical properties of friction stir welded joints of aluminium alloy to copper , 2011 .

[22]  Andre D. L. Batako,et al.  Experimental and theoretical analysis of friction stir welding of Al–Cu joints , 2014 .

[23]  B. Xiao,et al.  Enhanced mechanical properties of friction stir welded dissimilar Al–Cu joint by intermetallic compounds , 2010 .

[24]  Mohsen Kazeminezhad,et al.  Microstructure and Mechanical Properties in Dissimilar Butt Friction Stir Welding of Severely Plastic Deformed Aluminum AA 1050 and Commercially Pure Copper Sheets , 2014 .