Crack nucleation from a notch in a ductile material under shear dominant loading

We examine the nucleation of a crack from a notch under a dominant shear loading in Al 6061-T6. The specimen is loaded in nominally pure shear over the gage section in an Arcan specimen configuration. The evolution of deformation is monitored using optical and scanning electron microscopy. Quantitative measurements of strain are made using the 2nd phase particles as Lagrangian markers which enable identification of the true (logarithmic) strains to levels in the range of two. Electron microscopy reveals further that the 2nd phase particles do not act as nucleation sites for damage in the regions of pure shear deformation. The initial notch is shown to “straighten out”, forming a new, sharper notch and triggering failure at the newly formed notch. Numerical simulations of the experiment, using the conventional Johnson–Cook model and a modified version based on grain level calibration of the failure strains, reveal that it is necessary to account for large local strain levels prior to the nucleation of a crack in order to capture the large deformations observed in the experiment.

[1]  Imad Barsoum,et al.  Rupture mechanisms in combined tension and shear : Experiments , 2007 .

[2]  K. Ravi-Chandar,et al.  Ductile failure behavior of polycrystalline Al 6061-T6 , 2012, International Journal of Fracture.

[3]  J. Hutchinson,et al.  Modification of the Gurson Model for shear failure , 2008 .

[4]  J. Crépin,et al.  Coupling between experimental measurements and polycrystal finite element calculations for micromechanical study of metallic materials , 2007 .

[5]  K. Liechti,et al.  Finite Element Analysis of the Arcan Specimen for Fiber Reinforced Composites under Pure Shear and Biaxial Loading , 1999 .

[6]  K. Ravi-Chandar,et al.  Ductile failure behavior of polycrystalline Al 6061-T6 under shear dominant loading , 2013, International Journal of Fracture.

[7]  J. Buffière,et al.  3D X‐ray Microtomography Volume Correlation to Study Fatigue Crack Growth , 2011 .

[8]  D. M. Tracey,et al.  On the ductile enlargement of voids in triaxial stress fields , 1969 .

[9]  J. Lowjr.  Fracture of Metals , 1951, Nature.

[10]  B. Bay,et al.  Digital volume correlation: Three-dimensional strain mapping using X-ray tomography , 1999 .

[11]  R. Narasimhan,et al.  A finite element analysis of mixed-mode fracture initiation by ductile failure mechanisms , 1994 .

[12]  R. Narasimhan,et al.  Numerical simulations of hole growth and ductile fracture initiation under mixed-mode loading , 1996 .

[13]  K. Puttick.  The shear component of ductile fracture , 1960 .

[14]  D R Lesuer,et al.  Modeling Large-Strain, High-Rate Deformation in Metals , 2001 .

[15]  T. Wierzbicki,et al.  On fracture locus in the equivalent strain and stress triaxiality space , 2004 .

[16]  Yuanli Bai,et al.  Partially coupled anisotropic fracture model for aluminum sheets , 2010 .

[17]  Stelios Kyriakides,et al.  Ductile failure under combined shear and tension , 2013 .

[18]  Shigeru Aoki,et al.  Elastic-plastic fracture behavior of an aluminum alloy under mixed mode loading , 1990 .

[19]  J. Hancock,et al.  On the mechanisms of ductile failure in high-strength steels subjected to multi-axial stress-states , 1976 .

[20]  N. Petch.  The fracture of metals , 1954 .

[21]  K. Ravi-Chandar,et al.  Ductile failure in polycrystalline OFHC copper , 2011 .

[22]  G. R. Johnson,et al.  Fracture characteristics of three metals subjected to various strains, strain rates, temperatures and pressures , 1985 .

[23]  Dirk Mohr,et al.  Hybrid experimental–numerical analysis of basic ductile fracture experiments for sheet metals , 2010 .

[24]  E. Orowan,et al.  Fracture and strength of solids , 1949 .

[25]  R. Mishra,et al.  Numerical simulations of crack tip fields in polycrystalline plastic solids , 2010 .

[26]  H. Sehitoglu,et al.  On the interactions between strain accumulation, microstructure, and fatigue crack behavior , 2013, International Journal of Fracture.