Enhanced luminescence from GaN-based blue LEDs grown on grooved sapphire substrates

Luminescence from GaN-based blue light-emitting diodes grown on grooved sapphire substrates was investigated using cathodoluminescence (CL) and electroluminescence (EL). The 60-nm-deep 2 (ridge) /spl times/4 /spl mu/m (trench) grooves along the <101~0> direction were created by BCl/sub 3/-Cl/sub 2/-based inductively coupled plasma reactive ion etching. Stronger CL and EL from the trench regions of the grooves in GaN and InGaN-GaN multiquantum-wells were observed, confirming its better crystalline quality over the trench regions, further supported by the EL mapping results. Epitaxial lateral growth was believed to initiate from the ridge regions to cover the trench regions at the foremost stage of GaN growth that is similar to the coalescence of islands.

[1]  S. Nakamura,et al.  Spontaneous emission of localized excitons in InGaN single and multiquantum well structures , 1996 .

[2]  A. A. Allerman,et al.  Improved brightness of 380 nm GaN light emitting diodes through intentional delay of the nucleation island coalescence , 2002 .

[3]  P. Dapkus,et al.  Temperature dependence of excitonic recombination in lateral epitaxially overgrown InGaN/GaN quantum wells studied with cathodoluminescence , 2004 .

[4]  Yan-Kuin Su,et al.  Nitride-based LEDs fabricated on patterned sapphire substrates , 2003 .

[5]  Zhihong Feng,et al.  GaN-based blue light-emitting diodes grown and fabricated on patterned sapphire substrates by metalorganic vapor-phase epitaxy , 2004 .

[6]  Masahiko Sano,et al.  High-Power, Long-Lifetime InGaN/GaN/AlGaN-Based Laser Diodes Grown on Pure GaN Substrates , 1998 .

[7]  Jung Han,et al.  Low-Dislocation-Density GaN from a Single Growth on a Textured Substrate , 2000 .

[8]  Takashi Mukai,et al.  InGaN-Based Near-Ultraviolet and Blue-Light-Emitting Diodes with High External Quantum Efficiency Using a Patterned Sapphire Substrate and a Mesh Electrode , 2002 .

[9]  Tsunemasa Taguchi,et al.  High Output Power InGaN Ultraviolet Light-Emitting Diodes Fabricated on Patterned Substrates Using Metalorganic Vapor Phase Epitaxy , 2001 .

[10]  Fernando Ponce,et al.  High dislocation densities in high efficiency GaN‐based light‐emitting diodes , 1995 .

[11]  Robert F. Davis,et al.  Dislocation density reduction via lateral epitaxy in selectively grown GaN structures , 1997 .

[12]  A. Strittmatter,et al.  Maskless epitaxial lateral overgrowth of GaN layers on structured Si(111) substrates , 2001 .

[13]  Akira Sakai,et al.  Defect structure in selectively grown GaN films with low threading dislocation density , 1997 .