Performance enhancement in interfacially synthesized thin-film composite polyamide-urethane reverse osmosis membrane for seawater desalination

Abstract This paper aims to enhance the performance of thin-film composite (TFC) polyamide-urethane seawater reverse osmosis membrane prepared by interfacial polymerization of m-phenylenediamine (MPD) and 5-chloroformyloxyisophthaloyl chloride (CFIC). Attempts were made, such as using mixed cross-linking agents, selecting organic solvents of different MPD solubility and/or diffusivity, varying CFIC-organic temperature, modifying curing conditions as well as post-treatment. Water flux and salt rejection of the resulting membrane were evaluated through permeation experiment with synthetic seawater; chemical composition and hydrophilicity of the skin layer were characterized by XPS and contact angle measurement, respectively. The results show that the permeability of the TFC membrane is enhanced in an effective way while the selectivity remains stable or increases by adding diacyl chloride, or selecting organic solvent of high amine diffusivity, or preparing membrane at a relatively high temperature, or adopting the modified two-stage curing process, or soaking the membrane in an aqueous solution containing hypochlorite. The water flux of the improved membrane increases from about 35 l/m2 h to around 42 l/m2 h for seawater desalination, while the salt rejection is always above 99.4%. Additionally, polyamide-urethane seawater reverse osmosis membrane with optimal reverse osmosis performance appears to comprise a selective skin layer of certain cross-linking and a relatively hydrophobic surface.

[1]  Cong-jie Gao,et al.  Study on a novel polyamide-urea reverse osmosis composite membrane (ICIC–MPD): I. Preparation and characterization of ICIC–MPD membrane , 2006 .

[2]  D. Campos,et al.  Aromatic/cycloaliphatic polyamide membrane , 1987 .

[3]  Bart Van der Bruggen,et al.  Distillation vs. membrane filtration: overview of process evolutions in seawater desalination , 2002 .

[4]  R. L. Fox,et al.  Spiral-wound poly (ether/amide) thin-film composite membrane systems , 1976 .

[5]  Abdul Latif Ahmad,et al.  Properties–performance of thin film composites membrane: study on trimesoyl chloride content and polymerization time , 2005 .

[6]  R. Rangarajan,et al.  Interfacially synthesized thin film composite RO membranes for seawater desalination , 1997 .

[7]  R. J. Petersen,et al.  Composite reverse osmosis and nanofiltration membranes , 1993 .

[8]  R. Baker.  Other Membrane Processes , 2004 .

[9]  Takeshi Matsuura,et al.  Progress in membrane science and technology for seawater desalination — a review , 2001 .

[10]  Lei Li,et al.  Polyamide thin film composite membranes prepared from 3,4',5-biphenyl triacyl chloride, 3,3',5,5'-biphenyl tetraacyl chloride and m-phenylenediamine , 2007 .

[11]  Masahiko Hirose,et al.  Effect of skin layer surface structures on the flux behaviour of RO membranes , 1996 .

[12]  J. Leckie,et al.  Hypochlorite degradation of crosslinked polyamide membranes: II. Changes in hydrogen bonding behavior and performance , 2006 .

[13]  Lei Li,et al.  Polyamide thin film composite membranes prepared from isomeric biphenyl tetraacyl chloride and m-phenylenediamine , 2008 .

[14]  Shen Jian,et al.  Crosslinked PVA-PS thin-film composite membrane for reverse osmosis , 1987 .

[15]  Cong-jie Gao,et al.  Preparation and characterization of polyamide-urethane thin-film composite membranes , 2005 .

[16]  R. Baker.  Membrane Technology and Applications , 1999 .

[17]  R. C. Weast.  CRC Handbook of Chemistry and Physics , 1973 .

[18]  Ashish Kulkarni,et al.  Flux enhancement by hydrophilization of thin film composite reverse osmosis membranes , 1996 .

[19]  Paul W. Morgan,et al.  Interfacial polycondensation. I. , 1959 .

[20]  Hisham Ettouney,et al.  Evaluating the economics of desalination , 2002 .

[21]  Yong Taek Lee,et al.  Effect of silane coupling agents on the performance of RO membranes , 2007 .

[22]  Cong-jie Gao,et al.  Preparation, structure characteristics and separation properties of thin-film composite polyamide-urethane seawater reverse osmosis membrane , 2008 .

[23]  P. Morgan,et al.  Interfacial polycondensation. II. Fundamentals of polymer formation at liquid interfaces , 1959 .

[24]  Zhou Yong,et al.  Polyamide thin film composite membrane prepared from m-phenylenediamine and m-phenylenediamine-5-sulfonic acid , 2006 .

[25]  A. Ahmad,et al.  Preparation and characterization of co-polyamide thin film composite membrane from piperazine and 3,5-diaminobenzoic acid , 2003 .

[26]  J. E. Cadotte,et al.  A new thin-film composite seawater reverse osmosis membrane , 1980 .

[27]  Eric M.V. Hoek,et al.  Impacts of reaction and curing conditions on polyamide composite reverse osmosis membrane properties , 2008 .

[28]  Thomas Melin,et al.  State-of-the-art of reverse osmosis desalination , 2007 .