Precise Determination of Thicknesses of Multilayer Polyethylene Composite Materials by Terahertz Time-Domain Spectroscopy

The multilayer structure of an ultra-high molecular weight polyethylene (UHMWPE) composite material was investigated in the terahertz (THz) spectral range by means of time-domain spectroscopy (TDS) technique. Such structures consist of many alternating layers of fibers, each being perpendicular to the other and each having a thickness of about 50 μm. Refractive indices of two composite samples and of a sample composed of four single layers (plies) having the same fiber orientation were determined for two orthogonal orientations of the electric field in a transmission TDS system. The birefringence of a single layer was measured, and the origin of this phenomenon is discussed. Using the TDS system in reflection, the formation of many pulses shifted in time was observed originating from reflections from interfaces of successive layers caused by the periodic modulation of the refractive index along the propagation of the THz radiation. This phenomenon is theoretically described and simulated by means of a transfer matrix method (TMM). A time-domain fitting procedure was used to determine thicknesses of all layers of the composite material. The reconstructed waveform based on the optimized thicknesses shows very good agreement with the measured waveform, with typical differences between measurements and simulations between 3 and 7 μm (depending on the sample). As a result, we were able to determine the thicknesses of all layers of two multilayer (~200 plies) structures by means of the reflection TDS technology with high accuracy.

[1]  G. Bastiaans,et al.  Absorption coefficients of selected explosives and related compounds in the range of 0.1-2.8 THz. , 2007, Optics express.

[2]  Maya R. Gupta,et al.  Recent advances in terahertz imaging , 1999 .

[3]  B. Fischer,et al.  Far-infrared vibrational modes of DNA components studied by terahertz time-domain spectroscopy , 2002, Physics in medicine and biology.

[4]  T. Tanabe,et al.  Polarization sensitive THz absorption spectroscopy for the evaluation of uniaxially deformed ultra-high molecular weight polyethylene , 2010 .

[5]  David K. Hsu,et al.  Nondestructive characterization of UHMWPE armor materials , 2012 .

[6]  Christopher D. Stoik,et al.  Nondestructive evaluation of aircraft composites using reflective terahertz time domain spectroscopy , 2010 .

[7]  Rainer Storn,et al.  Differential Evolution – A Simple and Efficient Heuristic for global Optimization over Continuous Spaces , 1997, J. Glob. Optim..

[8]  Patrick Mounaix,et al.  Aeronautics composite material inspection with a terahertz time-domain spectroscopy system , 2013 .

[9]  Christopher D. Stoik,et al.  Nondestructive evaluation of aircraft composites using transmissive terahertz time domain spectroscopy. , 2008, Optics express.

[10]  H. Merbold,et al.  Stratified dispersive model for material characterization using terahertz time-domain spectroscopy. , 2014, Optics letters.

[11]  W. Swiderski,et al.  Studying Efficiency of NDE Techniques Applied to Composite Materials in Aerospace Applications , 2010 .

[12]  N. Palka,et al.  Detailed non-destructive evaluation of UHMWPE composites in the terahertz range , 2014 .

[13]  Cunlin Zhang,et al.  Compact continuous-wave subterahertz system for inspection applications , 2005 .

[14]  Mira Naftaly,et al.  Methodologies for determining the dynamic ranges and signal-to-noise ratios of terahertz time-domain spectrometers. , 2009, Optics letters.

[15]  J. R. Birch,et al.  The optical constants of some common low-loss polymers between 4 and 40 cm -1 , 1981 .

[16]  Jean-Claude Mollier,et al.  THz QCL-based active imaging dedicated to non-destructive testing of composite materials used in aeronautics , 2010, NanoScience + Engineering.

[17]  M. Koch,et al.  Terahertz spectroscopy to study the orientation of glass fibres in reinforced plastics , 2010 .

[18]  Zach DeVito,et al.  Opt , 2017 .

[19]  N. Fleck,et al.  The soft impact response of composite laminate beams , 2013 .

[20]  H. Wadley,et al.  Defect controlled transverse compressive strength of polyethylene fiber laminates , 2015 .

[21]  L. Piché,et al.  Ultrasonic behavior of polymer blends , 1995 .

[22]  N. Fleck,et al.  The high strain rate response of Ultra High Molecular-weight Polyethylene: From fibre to laminate , 2013 .

[23]  M. Koch,et al.  Terahertz imaging: a new non-destructive technique for the quality control of plastic weld joints , 2007 .

[24]  Withawat Withayachumnankul,et al.  A Review on Thin-film Sensing with Terahertz Waves , 2012 .

[25]  I. Amenabar,et al.  In Introductory Review to THz Non-Destructive Testing of Composite Mater , 2013 .

[26]  T. Yasui,et al.  Terahertz paintmeter for noncontact monitoring of thickness and drying progress in paint film. , 2005, Applied optics.

[27]  Antonio Nanni,et al.  Microwave detection of delaminations between fiber reinforced polymer (FRP) composite and hardened cement paste , 2002 .

[28]  P. N. Suganthan,et al.  Differential Evolution Algorithm With Strategy Adaptation for Global Numerical Optimization , 2009, IEEE Transactions on Evolutionary Computation.