Direct imaging of Pt single atoms adsorbed on TiO2 (110) surfaces.

Noble metal nanoparticles (e.g., gold and platinum) supported on TiO2 surfaces are utilized in many technological applications such as heterogeneous catalysts. To fully understand their enhanced catalytic activity, it is essential to unravel the interfacial interaction between the metal atoms and TiO2 surfaces at the level of atomic dimensions. However, it has been extremely difficult to directly characterize the atomic-scale structures that result when individual metal atoms are adsorbed on the TiO2 surfaces. Here, we show direct atomic-resolution images of individual Pt atoms adsorbed on TiO2 (110) surfaces using aberration-corrected scanning transmission electron microscopy. Subangstrom spatial resolution enables us to identify five different Pt atom adsorption sites on the TiO2 (110) surface. Combining this with systematic density functional theory calculations reveals that the most favorable Pt adsorption sites are on vacancy sites of basal oxygen atoms that are located in subsurface positions relative to the top surface bridging oxygen atoms.

[1]  H. Onishi,et al.  Probe microscope observation of platinum atoms deposited on the TiO2(110)-(1 x 1) surface. , 2006, The journal of physical chemistry. B.

[2]  O. Gülseren,et al.  Adsorption of Pt and Bimetallic PtAu Clusters on the Partially Reduced Rutile (110) TiO2 Surface: A First-Principles Study , 2012 .

[3]  A. Bell.  The Impact of Nanoscience on Heterogeneous Catalysis , 2003, Science.

[4]  P. Nellist,et al.  Direct Imaging of the Atomic Configuration of Ultradispersed Catalysts , 1996, Science.

[5]  Ş. Ellialtıoğlu,et al.  Theoretical analysis of small Pt particles on rutile TiO 2 (110) surfaces , 2010, 1008.3631.

[6]  Masatake Haruta,et al.  Catalysis of Gold Nanoparticles Deposited on Metal Oxides , 2002 .

[7]  Xiaofeng Yang,et al.  Single-atom catalysis of CO oxidation using Pt1/FeOx. , 2011, Nature chemistry.

[8]  W. Göpel,et al.  The geometric structure of intrinsic defects at TiO2(110) surfaces: an STM study , 1995 .

[9]  Y. Ikuhara,et al.  Interface structures of gold nanoparticles on TiO2 (110). , 2009, Physical review letters.

[10]  J. Sanz,et al.  Oxygen vacancies on TiO2 (110) from first principles calculations. , 2004, The Journal of chemical physics.

[11]  Stephen J. Pennycook,et al.  High-resolution Z-contrast imaging of crystals , 1991 .

[12]  H. Koinuma,et al.  Crystal-face dependences of surface band edges and hole reactivity, revealed by preparation of essentially atomically smooth and stable (110) and (100) n-TiO(2) (rutile) surfaces. , 2005, The journal of physical chemistry. B.

[13]  Ulrike Diebold,et al.  The surface science of titanium dioxide , 2003 .

[14]  B. Parkinson,et al.  Preparation and characterization of terraced surfaces of low-index faces of anatase, rutile, and brookite. , 2006, Langmuir : the ACS journal of surfaces and colloids.

[15]  Preferential growth of Pt on rutile Ti O 2 , 2005, cond-mat/0510718.

[16]  Y. Ikuhara,et al.  Effects of TiO2 Support on the Initial Stage of Pt Nanoparticle Growth , 2013 .

[17]  M. Kuhn,et al.  Intrinsic defects on a TiO2(110)(1×1) surface and their reaction with oxygen: a scanning tunneling microscopy study , 1998 .

[18]  Y. Ikuhara,et al.  Direct Imaging of Reconstructed Atoms on TiO2 (110) Surfaces , 2008, Science.

[19]  N. Browning,et al.  Towards full-structure determination of bimetallic nanoparticles with an aberration-corrected electron microscope. , 2010, Nature nanotechnology.