Cathodoluminescence microscopy and spectroscopy of GaN epilayers microstructured using surface charge lithography

Cathodoluminescence (CL) microscopy and spectroscopy have been used to investigate the optical properties of GaN microstructures patterned by Ar+ ion irradiation and subsequent photoelectrochemical (PEC) etching. Monochromatic CL images and CL spectra reveal an enhancement of several defect-related emission bands in a 10 mu m wide area around each microstructure. In addition, columnar nanostructures and nanoetch pits were found in the PEC etched areas. CL emission of the nanocolumns is dominated by free electron to acceptor transitions, while excitonic luminescence prevails in the rest of the etched GaN layers. Investigation of the sidewalls of the microstructures reveals that a CL emission band centered at about 3.41 eV, attributed to excitons bound to structural defects, is effectively suppressed after PEC etching only in the observed nanocolumns.

[1]  I. Adesida,et al.  Gallium nitride whiskers formed by selective photoenhanced wet etching of dislocations , 1998 .

[2]  Strain Variation with Sample Thicknes s in GaN Grown by Hydride Vapor Phase Epitaxy , 2000 .

[3]  S. Hersee,et al.  Properties of GaN epilayers grown on misoriented sapphire substrates , 1998 .

[4]  L. Coldren,et al.  Development of selective lateral photoelectrochemical etching of InGaN/GaN for lift-off applications , 2001 .

[5]  Ion Tiginyanu,et al.  Surface-charge lithography for GaN microstructuring based on photoelectrochemical etching techniques , 2005 .

[6]  Michael Schmidt,et al.  On the nature of the 3.41 eV luminescence in hexagonal GaN , 1998 .

[7]  L. Coldren,et al.  Channeling as a mechanism for dry etch damage in GaN , 2000 .

[8]  D. C. Reynolds,et al.  Photoluminescence of GaN grown by molecular- beam epitaxy on a freestanding GaN template , 2001 .

[9]  F. Calle,et al.  Luminescence properties and defects in GaN nanocolumns grown by molecular beam epitaxy , 2000 .

[10]  A. Yamamoto,et al.  Anodic Dissolution of N‐Type Gallium Arsenide under Illumination , 1975 .

[11]  Afifuddin,et al.  Gallium and oxygen accumulations on gallium nitride surfaces following argon ion milling in ultra-high vacuum conditions , 2004 .

[12]  E. Hu,et al.  Resolution limitations in focused ion beam damage‐induced masking for photoelectrochemical etching of GaAs , 1992 .

[13]  F. W. Ostermayer,et al.  Using focused ion beam damage patterns to photoelectrochemically etch features in III-V materials , 1986 .

[14]  Ilesanmi Adesida,et al.  Highly anisotropic photoenhanced wet etching of n-type GaN , 1997 .

[15]  O. Ambacher,et al.  Photoluminescence study of excitons in homoepitaxial GaN , 2001 .

[16]  R. Cheung,et al.  Effects of dry processing on the optical properties of GaN , 2000 .

[17]  Krüger,et al.  Strain-related phenomena in GaN thin films. , 1996, Physical review. B, Condensed matter.

[18]  H. Morkoç,et al.  Luminescence properties of defects in GaN , 2005 .

[19]  S. Denbaars,et al.  Enhanced diffusion as a mechanism for ion-induced damage propagation in GaN , 2001 .

[20]  S. S. Park,et al.  Transient photoluminescence of defect transitions in freestanding GaN , 2001 .

[21]  I. Tiginyanu,et al.  Spatially resolved cathodoluminescence of GaN nanostructures fabricated by photoelectrochemical etching , 2005 .

[22]  Pierre Gibart,et al.  TEMPERATURE QUENCHING OF PHOTOLUMINESCENCE INTENSITIES IN UNDOPED AND DOPED GAN , 1999 .

[23]  A. Cavallini,et al.  Time-resolved cathodoluminescence assessment of deep-level transitions in hydride-vapor-phase-epitaxy GaN , 2003 .

[24]  G. Chi,et al.  Electrical and optical changes in the near surface of reactively ion etched n-GaN , 1999 .

[25]  S. Denbaars,et al.  Backside-illuminated photoelectrochemical etching for the fabrication of deeply undercut GaN structures , 2000 .

[26]  R. Beresford,et al.  Exciton and donor - acceptor recombination in undoped GaN on Si(111) , 1997 .