Modelling distinct failure mechanisms in composite materials by a combined phase field method

Abstract A numerical computational framework that combines a phase field model (PFM) and cohesive element (CE) for modelling progressive failure in composite material is proposed. In this setting, cracks in single material and the interface are captured separately by using the PFM and CE. A unified PFM that incorporates general cohesive softening laws is adopted for quasi-brittle fracture process. An energy split scheme is used to prevent material cracking under compressive state. The irreversibility of the damage evolution is enforced by introducing a history related energy density. The compatibility issue between the CE and PFM is considered for accurately capturing complicated failure mechanisms in composite. The developed approach is implemented into commercial software ABAQUS through user-defined subroutine element (UEL). Validation is made by modelling an experiment on delamination migration of a cross ply composite. Failure mechanisms including delamination, matrix crack, and location of delamination migration that observed in the experiment are all well captured. Moreover, the importance of considering the compatibility between CE and other numerical methods is discussed through a complementary modelling.

[1]  Gilles A. Francfort,et al.  Revisiting brittle fracture as an energy minimization problem , 1998 .

[2]  V. Tan,et al.  On cohesive element parameters and delamination modelling , 2019, Engineering Fracture Mechanics.

[3]  M. Crisfield,et al.  Finite element interface models for the delamination analysis of laminated composites: mechanical and computational issues , 2001 .

[4]  Julien Réthoré,et al.  Phase field modelling of anisotropic crack propagation , 2017 .

[5]  Ratna Kumar Annabattula,et al.  Modeling crack propagation in variable stiffness composite laminates using the phase field method , 2019, Composite Structures.

[6]  Tong Earn Tay,et al.  Integrated XFEM-CE analysis of delamination migration in multi-directional composite laminates , 2016 .

[7]  Jie Zhi,et al.  Geometrically nonlinear analysis of matrix cracking and delamination in composites with floating node method , 2018, Computational Mechanics.

[8]  M F Pernice,et al.  Experimental Study on Delamination Migration in Composite Laminates , 2015 .

[9]  Pedro P. Camanho,et al.  An engineering solution for mesh size effects in the simulation of delamination using cohesive zone models , 2007 .

[10]  C. S. Lopes,et al.  Characterization of crack propagation in mode I delamination of multidirectional CFRP laminates , 2012 .

[11]  N. P. Dijk,et al.  A phase-field model for strength and fracture analyses of fiber-reinforced composites , 2019, Composites Science and Technology.

[12]  Vincent B. C. Tan,et al.  A separable cohesive element for modelling coupled failure in laminated composite materials , 2018 .

[13]  John W. Hutchinson,et al.  Crack deflection at an interface between dissimilar elastic-materials , 1989 .

[14]  H. Lee,et al.  Modelling damage growth in composites subjected to impact and compression after impact , 2017 .

[15]  Vinh Phu Nguyen,et al.  Modelling complex cracks with finite elements: a kinematically enriched constitutive model , 2016, International Journal of Fracture.

[16]  P.M.S.T. de Castro,et al.  Mode-I interlaminar fracture of carbon/epoxy cross-ply composites , 2002 .

[17]  M. Benzeggagh,et al.  Measurement of mixed-mode delamination fracture toughness of unidirectional glass/epoxy composites with mixed-mode bending apparatus , 1996 .

[18]  Peng Zhang,et al.  Modelling progressive failure in multi-phase materials using a phase field method , 2019, Engineering Fracture Mechanics.

[19]  Bin Li,et al.  Phase‐field modeling and simulation of fracture in brittle materials with strongly anisotropic surface energy , 2015 .

[20]  Pedro P. Camanho,et al.  A damage model for the simulation of delamination in advanced composites under variable-mode loading , 2006 .

[21]  A. A. Griffith.  The Phenomena of Rupture and Flow in Solids , 1921 .

[22]  Tong Earn Tay,et al.  Modeling delamination migration in cross-ply tape laminates , 2015 .

[23]  John D. Clayton,et al.  Phase Field Modeling of Directional Fracture in Anisotropic Polycrystals , 2015 .

[24]  Vincent B. C. Tan,et al.  Adaptive floating node method for modelling cohesive fracture of composite materials , 2018 .

[25]  Emile S. Greenhalgh,et al.  Fractographic observations on delamination growth and the subsequent migration through the laminate , 2009 .

[26]  Marco Paggi,et al.  Revisiting the problem of a crack impinging on an interface: A modeling framework for the interaction between the phase field approach for brittle fracture and the interface cohesive zone model , 2017, 1702.01102.

[27]  Laura De Lorenzis,et al.  A review on phase-field models of brittle fracture and a new fast hybrid formulation , 2015 .

[28]  L. J. Sluys,et al.  Mesh-independent modeling of both distributed and discrete matrix cracking in interaction with delamination in composites , 2010 .

[29]  Marco Paggi,et al.  A 3D finite strain model for intralayer and interlayer crack simulation coupling the phase field approach and cohesive zone model , 2017 .

[30]  Tinh Quoc Bui,et al.  A rate-dependent hybrid phase field model for dynamic crack propagation , 2017 .

[31]  Tong Earn Tay,et al.  Numerical analysis of size effects on open-hole tensile composite laminates , 2013 .

[32]  Zhanli Liu,et al.  Numerical study on crack propagation in linear elastic multiphase composite materials using phase field method , 2018, Engineering Computations.

[33]  Kazuyoshi Fushinobu,et al.  Hybrid phase field simulation of dynamic crack propagation in functionally graded glass-filled epoxy , 2016 .

[34]  X. J. Fang,et al.  An augmented cohesive zone element for arbitrary crack coalescence and bifurcation in heterogeneous materials , 2011 .

[35]  Christian Miehe,et al.  Thermodynamically consistent phase‐field models of fracture: Variational principles and multi‐field FE implementations , 2010 .

[36]  Anthony R. Ingraffea,et al.  Transition elements to be used with quarter-point crack-tip elements , 1978 .

[37]  Markus Kästner,et al.  Phase-field modelling of interface failure in brittle materials , 2019, Computer Methods in Applied Mechanics and Engineering.

[38]  Tinh Quoc Bui,et al.  A new cohesive crack tip symplectic analytical singular element involving plastic zone length for fatigue crack growth prediction under variable amplitude cyclic loading , 2017 .

[39]  Timon Rabczuk,et al.  Fracture properties prediction of clay/epoxy nanocomposites with interphase zones using a phase field model , 2017 .

[40]  Debasish Roy,et al.  Phase field based peridynamics damage model for delamination of composite structures , 2017 .

[41]  Vinh Phu Nguyen,et al.  A length scale insensitive phase-field damage model for brittle fracture , 2018, Journal of the Mechanics and Physics of Solids.

[42]  R. Barsoum.  On the use of isoparametric finite elements in linear fracture mechanics , 1976 .

[43]  Cv Clemens Verhoosel,et al.  A phase-field description of dynamic brittle fracture , 2012 .

[44]  X. F. Hu,et al.  Modelling delamination migration using virtual embedded cohesive elements formed through floating nodes , 2018, Composite Structures.

[45]  Adrian Willenbücher,et al.  Phase field approximation of dynamic brittle fracture , 2014 .

[46]  Qingda Yang,et al.  Cohesive models for damage evolution in laminated composites , 2005 .

[47]  A. T. Marques,et al.  Modeling Compression Failure after Low Velocity Impact on Laminated Composites Using Interface Elements , 1997 .

[48]  Jian-Ying Wu,et al.  A unified phase-field theory for the mechanics of damage and quasi-brittle failure , 2017 .

[49]  P. Camanho,et al.  Numerical Simulation of Mixed-Mode Progressive Delamination in Composite Materials , 2003 .

[50]  Mahabub Alam,et al.  Crack Penetration and Deflection Behavior at Interfaces , 2016 .

[51]  M. D. Moura,et al.  Mixed-Mode Decohesion Elements for Analyses of Progressive Delamination , 2001 .

[52]  Brian Falzon,et al.  Predicting low velocity impact damage and Compression-After-Impact (CAI) behaviour of composite laminates , 2015 .

[53]  Timon Rabczuk,et al.  Abaqus implementation of phase-field model for brittle fracture , 2015 .

[54]  Cv Clemens Verhoosel,et al.  A phase‐field model for cohesive fracture , 2013 .

[55]  Christopher J. Larsen,et al.  A time-discrete model for dynamic fracture based on crack regularization , 2011 .

[56]  Patrick E. Farrell,et al.  Linear and nonlinear solvers for variational phase‐field models of brittle fracture , 2015, 1511.08463.

[57]  Antonin Chambolle,et al.  Implementation of an adaptive finite-element approximation of the Mumford-Shah functional , 2000, Numerische Mathematik.

[58]  Anthony Gravouil,et al.  2D and 3D Abaqus implementation of a robust staggered phase-field solution for modeling brittle fracture , 2017 .

[59]  Jeremy Bleyer,et al.  Phase-field modeling of anisotropic brittle fracture including several damage mechanisms , 2018, Computer Methods in Applied Mechanics and Engineering.

[60]  Xiaoyi Wang,et al.  An iteration scheme for phase field model for cohesive fracture and its implementation in Abaqus , 2018, Engineering Fracture Mechanics.

[61]  Emile S. Greenhalgh,et al.  Delamination growth directionality and the subsequent migration processes – The key to damage tolerant design , 2013 .

[62]  Christian Miehe,et al.  A phase field model for rate-independent crack propagation: Robust algorithmic implementation based on operator splits , 2010 .

[63]  Vinh Phu Nguyen,et al.  Modeling dynamic fracture of solids with a phase-field regularized cohesive zone model , 2018, Computer Methods in Applied Mechanics and Engineering.

[64]  Vincent B. C. Tan,et al.  Modelling the tensile failure of composites with the floating node method , 2016 .

[65]  Julien Yvonnet,et al.  A phase-field method for computational modeling of interfacial damage interacting with crack propagation in realistic microstructures obtained by microtomography , 2016 .