Synthesis and characterization of high-temperature hexagonal P2-Na0.6 MnO2 and its electrochemical behaviour as cathode in sodium cells

A layered sodium manganese oxide, Na0.6MnO2, stable at temperatures above 800 °C, was synthesized by using a sol–gel method that employs Mn(acac)3 (ac = acetylacetonate), Na2CO3 and propionic acid to form the resin framework. This layered bronze possesses a hexagonal, P2-type structure, in which the distortion associated with Mn3+ is hardly perceptible. It reacts slowly, though reversibly, with atmospheric moisture, which causes the interlayer spacing in the structure to increase by ca. 2.5 A, through intercalation of water molecules into the interlayer gap occupied by Na+ ions. The anhydrous material was tested as a cathode in sodium cells. Although the electrochemical intercalation of Na+ occurs in two steps, the host retains its main structural features, with a slight tendency in the interlayer spacing to contract as the sodium content increases. The similarity between the discharge and charge profiles of the first cycles reveals a quasi-reversible nature in the intercalation process and that the cell can deliver a constant specific capacity of ca. 140 A h kg−1 at 0.1 mA cm−2 when cycled in a voltage window of 3.8–2.0 V. However, the continuous strains and distortions resulting from the insertion and extraction of Na+ ions cause the host structure to gradually collapse and yield an amorphous material after the first eight cycles. This leads to a progressive reduction of the cell capacity, irrespective of the specific voltage window used.

[1]  S. Suib,et al.  Sol−Gel Synthesis of Layered Birnessite-Type Manganese Oxides , 1997 .

[2]  T. R. Jow,et al.  Rechargeable Electrodes from Sodium Cobalt Bronzes , 1988 .

[3]  Thomas J. Richardson,et al.  Lithium insertion processes of orthorhombic Na{sub x}MnO{sub 2}-based electrode materials , 1996 .

[4]  J. Pereira‐Ramos,et al.  Structural and electrochemical characteristics of a lamellar sodium manganese oxide synthesized via a sol-gel process , 1993 .

[5]  S. Hirano,et al.  Hydrothermal synthesis and properties of Na0.70MnO2.25 layer crystal , 1984 .

[6]  C. Delmas,et al.  A new variety of LiMnO2 with a layered structure , 1996 .

[7]  Seung M. Oh,et al.  Preparation of Layered MnO2 via Thermal Decomposition of KMnO4 and Its Electrochemical Characterizations , 1999 .

[8]  J. Morales,et al.  Sol-gel derived Li-V-Mn-O spinels as cathodes for rechargeable lithium batteries , 2000 .

[9]  Peter G. Bruce,et al.  Synthesis of layered LiMnO2 as an electrode for rechargeable lithium batteries , 1996, Nature.

[10]  Marca M. Doeff,et al.  Rechargeable Na/Na[sub x]CoO[sub 2] and Na[sub 15]Pb[sub 4]/Na[sub x]CoO[sub 2] polymer electrolyte cells , 1993 .

[11]  J. Pereira‐Ramos,et al.  Chemistry and Electrochemistry of Low‐Temperature Manganese Oxides as Lithium Intercalation Compounds , 2000 .

[12]  J. Dahn,et al.  Layered Li‐Mn‐Oxide with the O2 Structure: A Cathode Material for Li‐Ion Cells Which Does Not Convert to Spinel , 1999 .

[13]  A. Mendiboure,et al.  Electrochemical intercalation and deintercalation of NaxMnO2 bronzes , 1985 .

[14]  P. Hagenmuller,et al.  Comportement electrochimique des phases NaxCoO2 , 1980 .

[15]  W. A. Dollase,et al.  Correction of intensities for preferred orientation in powder diffractometry: application of the March model , 1986 .

[16]  J. Dahn,et al.  Key Factors Controlling the Reversibility of the Reaction of Lithium with SnO2 and Sn2 BPO 6 Glass , 1997 .