Effects of CMP Process Conditions on Defect Generation in Low-k Materials An Atomic Force Microscopy Study

The effects of chemical mechanical planarization (CMP) process parameters and consumables on the polish rate and defects generated in various low-k materials with k values ranging from 2.2 to 3.0 were studied in detail. The process consumables and conditions evaluated include slurry material (alumina and silica), pad type (soft and hard), polish pressure, and polish time. Atomic force microscopy (AFM) images and roughness numbers were used to evaluate the post-CMP defect generation under various process conditions and revealed nano/microscratches, pits, voids, and film delamination. For a given material, the removal rate increased with increasing pressure. The dependence of defects on pressure appeared highly driven by the slurry material, pad type, and low-k material properties. Defects increased with increasing pad hardness and decreasing k values. The increasing defects with decreasing k value can be attributed to the lower elastic modulus observed with low-k materials. Removal rates exhibited both a decrease and an increase in conjunction with polish time, depending on the type of low-k material used. AFM analysis showed an improvement in global surface roughness with increasing polish time; however, an increase in localized defects such as pits was also observed. Fourier transform infrared and X-ray photoelectron spectroscopy analyses showed no change in film chemistry under the conditions studied here.

[1] H. Cui,et al. Chemical Mechanical Polishing of Low Dielectric Constant Oxide Films Deposited Using Flowfill Chemical Vapor Deposition Technology , 2000 .

[2] G. Zwicker,et al. A selective CMP process for stacked low- k CVD oxide films , 1999 .

[3] Chemical-mechanical polishing of low dielectric constant poly(silsesquioxane): HSQ , 1999 .

[4] Some Aspects of the Materials Science of Low-K Integration , 2003 .

[5] Toshiaki Kurosu,et al. Chemical Mechanical Polishing of Polyarylether Low Dielectric Constant Layers by Manganese Oxide Slurry , 1999 .

[6] W. A. Pliskin. Comparison of properties of dielectric films deposited by various methods , 1977 .

[7] S. Sze,et al. Improvement of post-chemical mechanical planarization characteristics on organic low k methylsilsesquioxane as intermetal dielectric , 2000 .

[8] Wen‐Chang Chen,et al. Effects of slurry formulations on chemical-mechanical polishing of low dielectric constant polysiloxanes: hydrido-organo siloxane and methyl silsesquioxane , 2000 .

[9] Baozhen Li,et al. Influence of underlying interlevel dielectric films on extrusion formation in aluminum interconnects , 2000 .

[10] Bau-Tong Dai,et al. Chemical Mechanical Polishing of Low‐Dielectric‐Constant Polymers: Hydrogen Silsesquioxane and Methyl Silsesquioxane , 1999 .