One-step, hydrothermal synthesis of nitrogen, carbon co-doped titanium dioxide (N,CTiO2) photocatalysts. Effect of alcohol degree and chain length as carbon dopant precursors on photocatalytic activity and catalyst deactivation

a b s t r a c t A one-step, hydrothermal method for the synthesis of nitrogen, carbon co-doped titanium dioxide (N,C TiO2) photocatalysts is demonstrated. The incorporation of nitrogen from ammonia and car- bon from alcohols with different chain length (methanol, ethanol, isopropanol, 1-butanol, 2-butanol, tert-butanol) used as carbon precursors was confirmed by FTIR/DRS and XPS analyses. The UV-vis/DR absorption spectra of the modified photocatalysts extended into the visible. XRD, BET and Zeta Sizer- Nano techniques were used for the characterization of the modified photocatalysts. The crystallite size of N,C TiO2 was not affected by the nature of the alcohol or the pressure acquired during the modification process but surface area, particle size (crystal agglomerate) and anatase content increased with synthesis pressure. In contrast with other studies in literature, the photoactivity of the different synthesized mate- rials was evaluated at a constant volumetric rate of photon absorption (VRPA) in an annular photoreactor. This innovative method allows the evaluation of the intrinsic photoactivity of each material. As a result, the effect of N,C-co-modification on the TiO2 photoactivity was evaluated without interference from the amount of radiation absorbed by each suspended powder since the total radiant energy absorbed by each slurry suspension was kept constant. Phenol decomposition confirmed that activity increased with the chain length of the alcohol precursor. The highest intrinsic photoactivity was for N,C TiO2 pre- pared from 2-butanol, and 1-butanol as carbon precursor which also exhibited much stronger resistance to deactivation during multiple catalyst reuse compared to pristine TiO2 and commercial Degussa P25 photocatalysts.

[1]  A. Murphy.  Modified Kubelka–Munk model for calculation of the reflectance of coatings with optically-rough surfaces , 2006 .

[2]  A. Morawski,et al.  Enhanced adsorption of two azo dyes produced by carbon modification of TiO2. , 2009 .

[3]  D. W. Sheel,et al.  Antimicrobial activity of titania/silver and titania/copper films prepared by CVD , 2010 .

[4]  P. Kubelka,et al.  New Contributions to the Optics of Intensely Light-Scattering Materials. Part I , 1948 .

[5]  X. Zu,et al.  Microstructure and Photoluminescence of Carbon and Nitrogen Dual Doped TiO(2) Powders , 2009 .

[6]  Nick Serpone,et al.  Is the band gap of pristine TiO(2) narrowed by anion- and cation-doping of titanium dioxide in second-generation photocatalysts? , 2006, The journal of physical chemistry. B.

[7]  A. Morawski,et al.  Solar-light-induced photocatalytic decomposition of two azo dyes on new TiO2 photocatalyst containing nitrogen , 2006 .

[8]  Dong Yang,et al.  Carbon and Nitrogen Co-doped TiO2 with Enhanced Visible-Light Photocatalytic Activity , 2007 .

[9]  ChenFeng,et al.  Carbon and Nitrogen-codoped TiO2 with High Visible Light Photocatalytic Activity , 2006 .

[10]  G. Galbács,et al.  Structural properties and photocatalytic behaviour of phosphate-modified nanocrystalline titania films , 2007 .

[11]  A. Morawski,et al.  Removal of organic dyes in the hybrid photocatalysis/nanofiltration system , 2009 .

[12]  Pierre Pichat,et al.  Some views about indoor air photocatalytic treatment using TiO2: Conceptualization of humidity effects, active oxygen species, problem of C1–C3 carbonyl pollutants , 2010 .

[13]  Changling Yu,et al.  A Simple Way to Prepare C–N-Codoped TiO2 Photocatalyst with Visible-Light Activity , 2009 .

[14]  Hao Wang,et al.  Hydrothermal Synthesis and Photocatalytic Properties of Pyrochlore La2Sn2O7 Nanocubes , 2007 .

[15]  M. L. Satuf,et al.  Photocatalytic degradation of 4-chlorophenol: A kinetic study , 2008 .

[16]  G. L. Puma,et al.  Enhancement of photocatalytic oxidation of oxalic acid by gold modified WO3/TiO2 photocatalysts under UV and visible light irradiation , 2010 .

[17]  A. E. Jiménez,et al.  Development and Modeling of Solar Photocatalytic Reactors , 2009 .

[18]  A. Abdullah,et al.  Reactive dye degradation by combined Fe(III)/TiO2 catalyst and ultrasonic irradiation: Effect of Fe(III) loading and calcination temperature. , 2011, Ultrasonics sonochemistry.

[19]  A. Morawski,et al.  New method of improving photocatalytic activity of commercial Degussa P25 for azo dyes decomposition , 2007 .

[20]  Miguel Pelaez,et al.  Mesoporous nitrogen-doped TiO2 for the photocatalytic destruction of the cyanobacterial toxin microcystin-LR under visible light irradiation. , 2007, Environmental science & technology.

[21]  P. Calza,et al.  Size dependent photocatalytic activity of hydrothermally crystallized titania nanoparticles on poorly adsorbing phenol in absence and presence of fluoride ion , 2007 .

[22]  E. Kim,et al.  Variation of structural and optical properties of sol-gel TiO2 thin films with catalyst concentration and calcination temperature , 2003 .

[23]  A. Sclafani,et al.  Comparison of the Photoelectronic and Photocatalytic Activities of Various Anatase and Rutile Forms of Titania in Pure Liquid Organic Phases and in Aqueous Solutions , 1996 .

[24]  T. Nagatomo,et al.  The Response of TiO2 Photocatalysts Codoped with Nitrogen and Carbon to Visible Light , 2005 .

[25]  J. Augustynski.  The role of the surface intermediates in the photoelectrochemical behaviour of anatase and rutile TiO2 , 1993 .

[26]  Oğuzhan Alagöz,et al.  Selective photocatalytic oxidation of 4-substituted aromatic alcohols in water with rutile TiO2 prepared at room temperature , 2009 .

[27]  C. Hung,et al.  Characterization of N,C-codoped TiO2 films prepared by reactive DC magnetron sputtering , 2009 .

[28]  A. Murphy.  Band-gap determination from diffuse reflectance measurements of semiconductor films, and application to photoelectrochemical water-splitting , 2007 .

[29]  F. Saito,et al.  Synthesis of visible-light responsive nitrogen/carbon doped titania photocatalyst by mechanochemical doping , 2007 .

[30]  A. Morawski,et al.  Azo dyes decomposition on new nitrogen-modified anatase TiO2 with high adsorptivity. , 2009, Journal of hazardous materials.

[31]  Jinlong Zhang,et al.  Synthesis and Characterization of Nitrogen-Doped TiO2 Nanophotocatalyst with High Visible Light Activity , 2007 .

[32]  Efstathios Z Panagou,et al.  Use of titanium dioxide (TiO2) photocatalysts as alternative means for Listeria monocytogenes biofilm disinfection in food processing. , 2011, Food microbiology.

[33]  Xiaobo Chen,et al.  Titanium dioxide nanomaterials: synthesis, properties, modifications, and applications. , 2007, Chemical reviews.

[34]  A. Morawski,et al.  Carbon Modified TiO2 Photocatalyst with Enhanced Adsorptivity for Dyes from Water , 2009 .

[35]  Fiderman Machuca-Martínez,et al.  Radiation absorption and optimization of solar photocatalytic reactors for environmental applications. , 2010, Environmental science & technology.

[36]  A. Morawski,et al.  Lifetime of Carbon-Modified TiO2 Photocatalysts Under UV Light Irradiation , 2009 .

[37]  L. Erickson,et al.  Synthesis of visible-light-active TiO2-based photocatalysts by carbon and nitrogen doping , 2008 .

[38]  G. Palmisano,et al.  Environmentally Friendly Photocatalytic Oxidation of Aromatic Alcohol to Aldehyde in Aqueous Suspension of Brookite TiO2 , 2008 .

[39]  Z. Yaakob,et al.  Synergistic effect of cobalt on nitrogen and carbon codoped anatase titania for photodegradation under visible light , 2010 .

[40]  Yuan-Yao Li,et al.  Preparation of Visible-Light-Responsive Nitrogen-carbon Co-doped Titania by Chemical Vapor Deposition , 2010 .

[41]  R. Asahi,et al.  Visible-Light Photocatalysis in Nitrogen-Doped Titanium Oxides , 2001, Science.

[42]  S. Lacombe,et al.  N-doped TiO2 by low temperature synthesis: Stability, photo-reactivity and singlet oxygen formation in the visible range , 2010 .

[43]  R. Nogueira,et al.  Photodegradation of dichloroacetic acid and 2,4-dichlorophenol by ferrioxalate/H2O2 system , 2000 .

[44]  Shujuan Zhang,et al.  Preparation of visible-light-active carbon and nitrogen codoped titanium dioxide photocatalysts with the assistance of aniline , 2009 .

[45]  P. Chubukov,et al.  Correlations for photocatalytic activity and spectral features of the absorption band edge of TiO2 modified by thiourea , 2009 .

[46]  G. L. Puma,et al.  Photocatalytic oxidation of herbicides in single-component and multicomponent systems: Reaction kinetics analysis , 2006 .

[47]  M. Maneira,et al.  Influence of O2 partial pressure on the growth of nanostructured anatase phase TiO2 thin films prepared by DC reactive magnetron sputtering , 2011 .

[48]  Xiaoping Wang,et al.  Solvothermal synthesis of C–N codoped TiO2 and photocatalytic evaluation for bisphenol A degradation using a visible-light irradiated LED photoreactor , 2010 .

[49]  Dionysios D. Dionysiou,et al.  Synthesis, structural characterization and evaluation of sol-gel-based NF-TiO2 films with visible light-photoactivation for the removal of microcystin-LR , 2010 .

[50]  M. Stutzmann,et al.  Hydroxyapatite growth induced by native extracellular matrix deposition on solid surfaces. , 2005, European cells & materials.