Modeling and experimental study of a multi-frequency electromagnetic sensor system for rail decarburisation measurement

This paper presents a modeling and experimental study using a multi-frequency electromagnetic (EM) sensor system, for non-destructive evaluation of rail decarburisation. The EM sensor is configured with a H-shaped ferrite core, which was excited with a multi-frequency waveform over the range of approximately 1–100 kHz. Finite-element (FE) simulation was carried out to establish the link between the EM sensor output and the level of decarburization. Rail samples with different levels of decarburisation, due to different bloom reheat times prior to rolling were tested in the laboratory. It was found that the zero-crossing frequency of the EM sensor response is linearly proportional to the decarburisation level by FE simulation, theoretic analysis and experiment. This finding is helpful in understanding the response of the EM sensor to rail decarburisation and could lead to a non-contact, non destructive method for use during rail manufacturing. In addition, on-site measurement (tests carried out in the Rail & Section Mill at Tata Steel) was taken on a 110 m long rail product, with the results indicating that the EM sensor response correctly follows the expected decarburisation profile along the rail length.

[1]  Xiaodong Li,et al.  Mössbauer study of the 430 °C decomposition of 18Ni(350) maraging steel , 1996 .

[2]  Didier Chicot,et al.  Eddy currents and hardness testing for evaluation of steel decarburizing , 2006 .

[3]  R. P. Smith.  The diffusivity of carbon in iron by the steadystate method , 1953 .

[4]  H. K. D. H. Bhadeshia,et al.  Diffusion of carbon in substitutionally alloyed austenite , 1995 .

[5]  Wuliang Yin,et al.  Modelling and experimental study of an electromagnetic sensor with an H-shaped ferrite core used for monitoring the hot transformation of steel in an industrial environment , 2011 .

[6]  Gary G. Tibbetts,et al.  Diffusivity of carbon in iron and steels at high temperatures , 1980 .

[7]  Wuliang Yin,et al.  Evaluation of rail decarburisation depth using a H-shaped electromagnetic sensor , 2012 .

[8]  Mehrdad Kashefi,et al.  Application of eddy current nondestructive method for determination of surface carbon content in carburized steels , 2009 .

[9]  John H. Beynon,et al.  Decarburisation and rolling contact fatigue of a rail steel , 2006 .

[10]  M. Gildersleeve,et al.  Relationship between decarburisation and fatigue strength of through hardened and carburising steels , 1991 .

[11]  Wenqian Zhu,et al.  Electromagnetic Techniques for On-line Inspection of Steel Microstructure , 2013 .

[12]  R. G. Baggerly,et al.  Determination of decarburization in steel , 1993 .

[13]  Toshiyuki Takagi,et al.  Characterization of ductile cast iron by eddy current method , 2005 .

[14]  B. A. Auld,et al.  Eddy-Current Reflection Probes: Theory and Experiment , 1989 .

[15]  A. J. Peyton,et al.  Imaging the transformation of hot strip steel using magnetic techniques , 2001, J. Electronic Imaging.

[16]  Wuliang Yin,et al.  Characterization of Decarburization of Steels Using a Multifrequency Electromagnetic Sensor: Experiment and Modeling , 2009 .

[17]  Brian A. Shaw,et al.  Surface decarburisation of steel detected by magnetic barkhausen emission , 2005 .

[18]  O. Bouaziz,et al.  Physical modelling of microstructure and mechanical properties of dual-phase steel , 2001 .

[19]  Toshiyuki Takagi,et al.  Eddy current evaluation of cast irons for material characterization , 2003 .