Influence of photoirradiation conditions on dentin bond durability and interfacial characteristics of universal adhesives.

The influence of photoirradiation conditions on dentin bond durability and interfacial characteristics of universal adhesives was investigated. Universal adhesives were applied to the dentin surfaces and photoirradiated with 100 mW/cm2 for 40 s, 200 mW/cm2 for 20 s, and 400 mW/cm2 for 10 s. A resin composite was bonded to dentin to determine shear bond strength after 24 h water storage and 30,000 thermal cycles, and water contact angle of cured adhesive were measured by the sessile drop method. Greater dentin bond strengths after 24 h water storage and 30,000 thermal cycles were achieved under these conditions at light intensity exceeding 200 mW/cm2. Universal adhesives photoirradiated above 200 mW/cm2 exhibited significantly higher water contact angles than those at 100 mW/cm2. The results of this study suggested that the photoirradiation conditions affect the dentin bond durability and interfacial characteristics of universal adhesives even at the same total energy.

[1]  W. W. Johnson,et al.  Comparison between universal adhesives and two‐step self‐etch adhesives in terms of dentin bond fatigue durability in self‐etch mode , 2017, European journal of oral sciences.

[2]  T. Takamizawa,et al.  Interfacial Characteristics and Bond Durability of Universal Adhesive to Various Substrates. , 2017, Operative dentistry.

[3]  D. Pashley,et al.  Dentin Bonding Durability of Two-step Self-etch Adhesives with Improved of Degree of Conversion of Adhesive Resins. , 2017, The journal of adhesive dentistry.

[4]  T. Takamizawa,et al.  The Effect of Phosphoric Acid Pre-etching Times on Bonding Performance and Surface Free Energy with Single-step Self-etch Adhesives. , 2016, Operative dentistry.

[5]  T. Takamizawa,et al.  Influence of the Oxygen-inhibited Layer on Bonding Performance of Dental Adhesive Systems: Surface Free Energy Perspectives. , 2016, The journal of adhesive dentistry.

[6]  T. Takamizawa,et al.  Influence of light intensity on surface-free energy and dentin bond strength of single-step self-etch adhesives. , 2015, Dental materials journal.

[7]  M. Gaintantzopoulou,et al.  Effect of Thermocycling, Degree of Conversion, and Cavity Configuration on the Bonding Effectiveness of All-in-One Adhesives. , 2015, Operative dentistry.

[8]  A. Reis,et al.  In vitro longevity of bonding properties of universal adhesives to dentin. , 2015, Operative dentistry.

[9]  K. Jiao,et al.  Bonding of universal adhesives to dentine--Old wine in new bottles? , 2015, Journal of dentistry.

[10]  K. Tsubota,et al.  Influence of light intensity on surface free energy and dentin bond strength of core build-up resins. , 2015, Operative dentistry.

[11]  J. Perdigão,et al.  Effects of solvent evaporation time on immediate adhesive properties of universal adhesives to dentin. , 2014, Dental materials : official publication of the Academy of Dental Materials.

[12]  Q. Ye,et al.  Polymerization- and solvent-induced phase separation in hydrophilic-rich dentin adhesive mimic. , 2014, Acta biomaterialia.

[13]  E. Piva,et al.  Replacing HEMA with alternative dimethacrylates in dental adhesive systems: evaluation of polymerization kinetics and physicochemical properties. , 2014, The journal of adhesive dentistry.

[14]  K. Tsubota,et al.  Important compositional characteristics in the clinical use of adhesive systems. , 2014, Journal of oral science.

[15]  F. Rueggeberg,et al.  Effect of using proper light-curing techniques on energy delivered to a Class 1 restoration. , 2014, Quintessence international.

[16]  Jürgen Durner,et al.  Influence of various irradiation processes on the mechanical properties and polymerisation kinetics of bulk-fill resin based composites. , 2013, Journal of dentistry.

[17]  R. Hickel,et al.  Resin-based composite light-cured properties assessed by laboratory standards and simulated clinical conditions. , 2013, Operative dentistry.

[18]  T. Watson,et al.  Hydrolytic degradation of the resin-dentine interface induced by the simulated pulpal pressure, direct and indirect water ageing. , 2012, Journal of dentistry.

[19]  Yoshiharu Nakamura,et al.  Effects of functional monomers and photo-initiators on the degree of conversion of a dental adhesive. , 2012, Acta biomaterialia.

[20]  J. Tagami,et al.  The influence of light intensities irradiated directly and indirectly through resin composite to self-etch adhesives on dentin bonding. , 2011, Dental materials journal.

[21]  P. Cesar,et al.  Direct comparison of the bond strength results of the different test methods: a critical literature review. , 2010, Dental materials : official publication of the Academy of Dental Materials.

[22]  Y. Kawano,et al.  Evaluation of curing light distance on resin composite microhardness and polymerization. , 2007, Operative dentistry.

[23]  A. Peutzfeldt,et al.  Influence of curing rate of resin composite on the bond strength to dentin. , 2007, Operative dentistry.

[24]  Yong Wang,et al.  Characterization of photopolymerization of dentin adhesives as a function of light source and irradiance. , 2007, Journal of biomedical materials research. Part B, Applied biomaterials.

[25]  Xiaoming Xu,et al.  Shear bond strength with increasing light-guide distance from dentin. , 2006, Journal of esthetic and restorative dentistry : official publication of the American Academy of Esthetic Dentistry ... [et al.].

[26]  Francesca Antoniolli,et al.  Degree of conversion and permeability of dental adhesives. , 2005, European journal of oral sciences.

[27]  R. Aversa,et al.  Light shielding effect of overlaying resin composite on the photopolymerization cure kinetics of a resin composite and a dentin adhesive. , 2005, Dental materials : official publication of the Academy of Dental Materials.

[28]  N. Moszner,et al.  Chemical aspects of self-etching enamel-dentin adhesives: a systematic review. , 2005, Dental materials : official publication of the Academy of Dental Materials.

[29]  G. Ambrosano,et al.  Effect of polymerization modes and resin composite on the temperature rise of human dentin of different thicknesses: an in vitro study. , 2005, Operative dentistry.

[30]  Y. Shimada,et al.  Interfacial structure between dentin and seven dentin bonding systems revealed using argon ion beam etching. , 1993, Operative dentistry.