Development of a new rapid, relevant and reliable (R3) test method to evaluate the pozzolanic reactivity of calcined kaolinitic clays

Abstract The present paper introduces a new rapid, relevant and reliable (R 3 ) test to predict the pozzolanic activity of calcined clays with kaolinite contents ranging from 0 to 95%. The test is based on the correlation between the chemical reactivity of calcined clays in a simplified system and the compressive strength of blends in standard mortar. The simplified system consists of calcined clay portlandite and limestone pastes with sulfate and alkali levels adjusted to reproduce the reaction environment of hydrating blended cements. The pastes were hydrated for 6 days at 20 °C or for 1 day at 40 °C. The chemical reactivity of the calcined clay can be obtained first by measurement of the heat release during reaction using isothermal calorimetry and second by bound water determination in a heating step between 110 °C and 400 °C. Very good correlations were found between the mortar compressive strength and both measures of chemical reactivity.

[1]  W. Tuan,et al.  Microstructural evolution of mullite during the sintering of kaolin powder compacts , 2000 .

[2]  Karen Scrivener,et al.  Pozzolanic reactivity of low grade kaolinitic clays: Influence of calcination temperature and impact of calcination products on OPC hydration , 2015 .

[3]  Alejandra Tironi,et al.  Assessment of pozzolanic activity of different calcined clays , 2013 .

[4]  R. Snellings,et al.  Use of X-ray diffraction to quantify amorphous supplementary cementitious materials in anhydrous and hydrated blended cements , 2014 .

[5]  K. Scrivener,et al.  Effect of temperature on the microstructure of calcium silicate hydrate (C-S-H) , 2013 .

[6]  B. Lothenbach,et al.  Thermodynamic Modelling of the Effect of Temperature on the Hydration and Porosity of Portland Cement , 2008 .

[7]  Konstantin Kovler,et al.  The effect of dehydroxylation/amorphization degree on pozzolanic activity of kaolinite , 2003 .

[8]  F. Glasser,et al.  Hydration of cements based on metakaolin: thermochemistry , 1990 .

[9]  Frank Winnefeld,et al.  Effect of temperature on the pore solution, microstructure and hydration products of Portland cement pastes , 2007 .

[10]  R. Snellings,et al.  Rapid screening tests for supplementary cementitious materials: past and future , 2016 .

[11]  B. Lothenbach,et al.  Effect of temperature on the hydration of Portland cement blended with siliceous fly ash , 2013 .

[12]  Karen Scrivener,et al.  The origin of the pozzolanic activity of calcined clay minerals: A comparison between kaolinite, illite and montmorillonite , 2011 .

[13]  Christopher R. Cheeseman,et al.  Comparison of test methods to assess pozzolanic activity , 2010 .

[14]  Emil Makovicky,et al.  Pozzolanic reactions of six principal clay minerals: Activation, reactivity assessments and technological effects , 1995 .

[15]  Karen Scrivener,et al.  Cement substitution by a combination of metakaolin and limestone , 2012 .

[16]  M. Moranville,et al.  The U phase formation in cement-based systems containing high amounts of Na2SO4 , 1996 .

[17]  Carl D. Palmer,et al.  Solubility of ettringite (Ca6[Al(OH)6]2(SO4)3 · 26H2O) at 5–75°C , 1999 .