Resistance of Injection Molded Wood-Polypropylene Composites against Basidiomycetes According to EN 15534-1: New Insights on the Test Procedure, Structural Alterations, and Impact of Wood Source

In this study, we investigated injection molded wood-polypropylene composites based on various wood sources and their decay resistance against white rot (Trametes versicolor) and brown rot (Coniophora puteana) in a laboratory test according to EN 15534-1:2014. The manufactured composites consisted of poplar (Populus spp.), willow (Salix spp.), European beech (Fagus sylvatica L.), Norway spruce (Picea abies (L.) H. Karst.), and a commercial wood source (Arbocel® C100), respectively. All formulations were compounded on a co-rotating twin screw extruder and subsequently injection molded to wood–PP specimens with a wood content of 60% or 70% by weight. It was found that the test procedure had a significant effect on the mechanical properties. Loss in mechanical properties was primarily caused by moisture and less by fungal decay. Moisture caused a loss in the modulus of rupture and modulus of elasticity of 34 to 45% and 29 to 73%, respectively. Mean mass and wood mass losses were up to a maximum of 3.7% and 5.3%, respectively. The high resistance against fungal decay was generally attributed to the encapsulation of wood by the polymer matrix caused by sample preparation, and enhanced by reduced moisture uptake during the preconditioning procedure. Notable differences with respect to the wood particle source and decay fungi were also observed. Structural characterization confirmed the decay pattern of the fungi such as void cavities close the surface and the deposition of calcium oxalates.

[1]  Robert J. Ross,et al.  Wood handbook : wood as an engineering material , 2010 .

[2]  Marcelo F. da Silveira,et al.  Natural resistance of eight Brazilian wood species from the region Caatinga determined by an accelerated laboratory decay test against four fungi , 2018, Holzforschung.

[3]  S. Peters.  Handbook of Composites , 1998 .

[4]  Andrzej K. Bledzki,et al.  Injection moulded microcellular wood fibre-polypropylene composites , 2006 .

[5]  Rebecca E. Ibach,et al.  Application of laboratory fungal resistance tests to solid wood and wood-plastic composite , 2003 .

[6]  L. Sobczak,et al.  Polypropylene composites with natural fibers and wood – General mechanical property profiles , 2012 .

[7]  C. Hill,et al.  Silane coupling agents used for natural fiber/polymer composites: A review , 2010 .

[8]  A. Krause,et al.  Enhanced water resistance of extruded wood–polypropylene composites based on alternative wood sources , 2016, European Journal of Wood and Wood Products.

[9]  Armando G. McDonald,et al.  DEGRADATION OF POLYPROPYLENE IN NATURALLY AND ARTIFICIALLY WEATHERED PLASTIC MATRIX COMPOSITES , 2014 .

[10]  Itana Radovanovic,et al.  Verarbeitung und Optimierung der Rezeptur von Wood Plastic Composites (WPC) , 2007 .

[11]  Robert A. Blanchette,et al.  Microbial and Enzymatic Degradation of Wood and Wood Components , 2012, Springer Series in Wood Science.

[12]  Mats Westin,et al.  Moisture Sorption, Biological Durability, and Mechanical Performance of WPC Containing Modified Wood and Polylactates , 2012 .

[13]  Jérôme Alteyrac,et al.  Termite and decay resistance of bioplast-spruce green wood-plastic composites , 2018, European Journal of Wood and Wood Products.

[14]  Holger Militz,et al.  Converting Wood from Short Rotation Coppice and Low‐Value Beech Wood into Thermoplastic Composites , 2015 .

[15]  Eric P. Verrecchia,et al.  Experimental calcium-oxalate crystal production and dissolution by selected wood-rot fungi , 2011 .

[16]  Michael P. Wolcott,et al.  Biological Degradation of Wood-Plastic Composites (WPC) and Strategies for Improving the Resistance of WPC against Biological Decay , 2008 .

[17]  Peter E. Laks,et al.  Flavonoid Biocides: Wood Preservatives Based on Condensed Tannins , 1988 .

[18]  Jeffrey J. Morrell,et al.  Patterns of Fungal Attack in Wood-Plastic Composites Following Exposure in a Soil Block Test , 2000 .

[19]  Kentaro Uesugi,et al.  Micro-CT observations of the 3D distribution of calcium oxalate crystals in cotyledons during maturation and germination in Lotus miyakojimae seeds. , 2013, Microscopy.

[20]  Jan Van den Bulcke,et al.  Moisture dynamics of WPC and the impact on fungal testing , 2010 .

[21]  P. Niemz.  [Physics of wood and wood-based materials] , 1993 .

[22]  Marek Gnatowski,et al.  Laboratory and exterior decay of wood–plastic composite boards: voids analysis and computed tomography , 2017 .

[23]  Francis W. M. R. Schwarze,et al.  WOOD DECAY UNDER THE MICROSCOPE , 2007 .

[24]  Michael P. Wolcott,et al.  INFLUENCE OF FUNGAL DECAY AND MOISTURE ABSORPTION ON MECHANICAL PROPERTIES OF EXTRUDED WOOD-PLASTIC COMPOSITES , 2005 .

[25]  Andreas Krause,et al.  Evaluating durability of thermoplastic wood composites against basidiomycetes and development of a suitable test design , 2014 .

[26]  P. Cooper,et al.  Recycled plastic/wood composite lumber attacked by fungi , 1998 .

[27]  Marek Gnatowski,et al.  Laboratory and environmental decay of wood–plastic composite boards: flexural properties , 2018 .

[28]  Jeffrey J. Morrell,et al.  Durability of wood-plastic composites , 2006 .

[29]  R. A. Correa,et al.  Effect of injections on the orientation of short fibre composites. An optical microscopic analysis , 1996 .

[30]  David P. Harper,et al.  Effect of Wood Species on Water Sorption and Durability of Wood-Plastic Composites , 2008 .

[31]  M. A. Verges,et al.  X-ray computed microtomography of internal damage in fiber reinforced polymer matrix composites , 2005 .

[32]  C. Evans,et al.  Oxalate production by fungi : its role in pathogenicity and ecology in the soil environment , 1996 .

[33]  Alain Bourmaud,et al.  Observation of the structure of a composite polypropylene/flax and damage mechanisms under stress , 2013 .

[34]  Charles L. Tucker,et al.  Fiber orientation in simple injection moldings. Part I: Theory and numerical methods , 1991 .

[35]  D Van Loo,et al.  Potential of X-ray computed tomography for 3D anatomical analysis and microdensitometrical assessment in wood research with focus on wood modification , 2013 .

[36]  Holger Militz,et al.  Resistance of modified polyvinyl chloride/wood flour composites to basidiomycetes , 2013, European Journal of Wood and Wood Products.

[37]  John J. Balatinecz,et al.  Durability of Wood Flour-Thermoplastic Composites under Extreme Environmental Conditions and Fungal Exposure , 2000 .

[38]  Oliver Mertens.  Performance and processing evaluation of thermoplastic wood fiber composites , 2018 .

[39]  Andreas Krause,et al.  Tomographic analysis of siliceous particulates in Australian turpentine wood (Syncarpia glomulifera) through X-ray micro-computed tomography. , 2019, Micron.

[40]  Geoffrey Daniel,et al.  Use of electron microscopy for aiding our understanding of wood biodegradation , 1994 .

[41]  Charles L. Tucker,et al.  Fiber orientation in simple injection moldings. Part II: Experimental results , 1992 .