Microstructure degradation of cermet anodes for solid oxide fuel cells: Quantification of nickel grain growth in dry and in humid atmospheres

Abstract The effects of compositional and environmental parameters on the kinetics of microstructural degradation are investigated for porous Ni/CGO anodes in solid oxide fuel cells (SOFC). Improved methodologies of SEM-imaging, segmentation and object recognition are described which enable a precise quantification of nickel grain growth over time. Due to these methodological improvements the grain growth can be described precisely with a standard deviation of only 5–15 nm for each time step. In humid atmosphere (60 vol.% H2O, 40% N2/H2) the growth rates of nickel are very high (up to 140%/100 h) during the initial period ( 1000 h) the growth rates decrease significantly to nearly 0%/100 h. In contrast, under dry conditions (97 vol.% N2, 3 vol.% H2) the growth rates during the initial period are much lower (ca. 1%/100 h) but they do not decrease over a period of 2000 h. In addition to the humidity factor there are other environmental and compositional parameters which have a strong influence on the kinetics of the microstructural degradation. The nickel coarsening is strongly depending on the gas flow rate. Also the initial microstructures and the anode compositions have a big effect on the degradation kinetics. Thereby small average grain sizes, wide distribution of particle size and high contents of nickel lead to higher coarsening and degradation rates. Whereas the nickel coarsening appears to be the dominant degradation mechanism during the initial period ( 1000 h) in humidified gas. Thereby the evaporation of volatile nickel species may lead to a local increase of the Ni/CGO ratio. Due to the surface wetting of CGO a continuous layer tends to form on the surface of the nickel grains which prevents further grain growth and evaporation of nickel. These phenomena lead to a microstructural reorganization between 1000 and 2300 h of exposure. This complex pattern of degradation phenomena also leads to a change of the amount of active microstructural sites that are important for catalytic reactions at the pore-nickel interfaces and for electrochemical reactions at the triple phase boundaries (TPB).

[1]  W. Bessler,et al.  The influence of equilibrium potential on the hydrogen oxidation kinetics of SOFC anodes , 2007 .

[2]  J. Van herle,et al.  Nickel–Zirconia Anode Degradation and Triple Phase Boundary Quantification from Microstructural Analysis , 2009 .

[3]  Lucille A. Giannuzzi,et al.  A review of focused ion beam milling techniques for TEM specimen preparation , 1999 .

[4]  Francesco De Carlo,et al.  Nondestructive Nanoscale 3D Elemental Mapping and Analysis of a Solid Oxide Fuel Cell Anode , 2010 .

[5]  Frank Tietz,et al.  Nickel coarsening in annealed Ni/8YSZ anode substrates for solid oxide fuel cells , 2000 .

[6]  Dimitris Sarantaridis,et al.  Redox Cycling of Ni‐Based Solid Oxide Fuel Cell Anodes: A Review , 2007 .

[7]  S. Pizer,et al.  The Image Processing Handbook , 1994 .

[8]  N. Stanietsky,et al.  The interaction of TIGIT with PVR and PVRL2 inhibits human NK cell cytotoxicity , 2009, Proceedings of the National Academy of Sciences.

[9]  Sidney Diamond,et al.  Mercury porosimetry: An inappropriate method for the measurement of pore size distributions in cement-based materials , 2000 .

[10]  B. Münch,et al.  Toward Reproducible Three-Dimensional Microstructure Analysis of Granular Materials and Complex Suspensions , 2009, Microscopy and Microanalysis.

[11]  J. Sehested,et al.  Sintering of nickel catalysts: Effects of time, atmosphere, temperature, nickel-carrier interactions, and dopants , 2006 .

[12]  Ki Hyun Yoon,et al.  Quantitative analysis of microstructure and its related electrical property of SOFC anode, Ni-YSZ cermet , 2002 .

[13]  R. Vaßen,et al.  Modelling of the agglomeration of Ni-particles in anodes of solid oxide fuel cells , 2001 .

[14]  W. Lehnert,et al.  Statistical geometry of reaction space in porous cermet anodes based on ion-conducting electrolytes: Patterns of degradation , 1999 .

[15]  Kazunari Sasaki,et al.  Poisoning of SOFC anodes by various fuel impurities , 2008 .

[16]  P. Levitz,et al.  Off-lattice reconstruction of porous media: critical evaluation, geometrical confinement and molecular transport , 1998 .

[17]  P. Levitz,et al.  Three-dimensional analysis of a loamy-clay soil using pore and solid chord distributions , 1996 .

[18]  Lorenz Holzer,et al.  Contradicting Geometrical Concepts in Pore Size Analysis Attained with Electron Microscopy and Mercury Intrusion , 2008 .

[19]  B Münch,et al.  Three‐dimensional analysis of porous BaTiO3 ceramics using FIB nanotomography , 2004, Journal of microscopy.

[20]  Boris Iwanschitz,et al.  Degradation of SOFC Anodes upon Redox Cycling: A Comparison Between Ni/YSZ and Ni/CGO , 2010 .

[21]  J. Sehested,et al.  Four challenges for nickel steam-reforming catalysts , 2006 .

[22]  Robert J. Flatt,et al.  FIB-Nanotomography of Particulate Systems—Part I: Particle Shape and Topology of Interfaces , 2006 .

[23]  Marco Cannarozzo,et al.  Experimental and Theoretical Investigation of Degradation Mechanisms by Particle Coarsening in SOFC Electrodes , 2009 .

[24]  Werner Lehnert,et al.  Degradation of Solid Oxide Fuel Cell Anodes Due to Sintering of Metal Particles Correlated Percolation Model , 1997 .

[25]  Y. Bultel,et al.  Modeling of a SOFC Fueled by Methane:Anode Barrier to Allow Gradual Internal Reforming Without Coking , 2008 .

[26]  K. Thydén,et al.  Microstructural characterization of SOFC Ni–YSZ anode composites by low-voltage scanning electron microscopy , 2008 .

[27]  L. Gauckler,et al.  The Electrochemistry of Ni Pattern Anodes Used as Solid Oxide Fuel Cell Model Electrodes , 2001 .

[28]  Peter Vang Hendriksen,et al.  Degradation of Anode Supported SOFCs as a Function of Temperature and Current Load , 2006 .

[29]  R. Wepf,et al.  3D-microstructure analysis of hydrated bentonite with cryo-stabilized pore water , 2010 .

[30]  Masamichi Ippommatsu,et al.  Preparation of Nickel Pattern Electrodes on YSZ and Their Electrochemical Properties in  H 2 ‐  H 2 O  Atmospheres , 1994 .

[31]  Mogens Bjerg Mogensen,et al.  Ni–YSZ Solid Oxide Fuel Cell Anode Behavior Upon Redox Cycling Based on Electrical Characterization , 2007 .

[32]  Robert J. Flatt,et al.  FIB-Nanotomography of Particulate Systems—Part II: Particle Recognition and Effect of Boundary Truncation , 2006 .

[33]  Boris Iwanschitz,et al.  Quantitative relationships between composition, particle size, triple phase boundary length and surface area in nickel-cermet anodes for Solid Oxide Fuel Cells , 2011 .

[34]  Jon M. Hiller,et al.  Three-dimensional reconstruction of a solid-oxide fuel-cell anode , 2006, Nature materials.

[35]  J. Israelachvili.  Intermolecular and surface forces , 1985 .

[36]  S. Jiang,et al.  Sintering behavior of Ni/Y2O3-ZrO2cermet electrodes of solid oxide fuel cells , 2003 .

[37]  Tomoo Iwata,et al.  Characterization of Ni‐YSZ Anode Degradation for Substrate‐Type Solid Oxide Fuel Cells , 1996 .

[38]  Boris Iwanschitz,et al.  Fundamental mechanisms limiting solid oxide fuel cell durability , 2008 .

[39]  W. D. Halstead.  A review of saturated vapour pressures and allied data for the principal corrosion products of iron, chromium, nickel and cobalt in flue gases , 1976 .