Effect of Ambient Gases on the Characteristics of ITO Thin Films for OLEDs

We have investigated the effect of ambient gases on the structural, electrical, and optical characteristics of ITO thin films intended for use as anode contacts in OLED (organic light emitting diodes) devices. These ITO thin films are deposited by radio frequency (RF) magnetron sputtering under different ambient gases (Ar, Ar+O2, and Ar+H2) at 300°C. In order to investigate the influences of the oxygen and hydrogen, the flow rate of oxygen and hydrogen in argon mixing gas has been changed from 0.5 sccm to 5 sccm and from 0.01 sccm to 0.25 sccm, respectively. The intensity of the (400) peak in the ITO thin films increased with increasing O2, flow rate whilst the (400) peak was nearly invisible in an atmosphere of Ar+H2. The electrical resistivity of the ITO thin films increased with increasing O2 flow rate, whereas the electrical resistivity decreased sharply under an Ar+H2 atmosphere and was nearly similar regardless of the H2 flow rate. The change of electrical resistivity with changes in the ambient gas composition was mainly interpreted in terms of the charge carrier mobility rather than the charge carrier concentration. All the films showed an average transmittance of over 80% in the visible range. The OLED device was fabricated with different ITO substrates made with the configuration of ITO/α-NPD/DPVB/Alq3/LiF/Al in order to elucidate the performance of the ITO substrate. Current density and luminance of OLED devices with ITO thin films deposited in Ar+H2 ambient gas is the highest among all the ITO thin films. [DOI: 10.4313/TEEM.2009.10.6.203]

[1]  F. Shan,et al.  Band gap energy of pure and Al-doped ZnO thin films , 2004 .

[2]  Zakya H. Kafafi,et al.  Indium tin oxide thin films grown on flexible plastic substrates by pulsed-laser deposition for organic light-emitting diodes , 2001 .

[3]  Michael L. Simpson,et al.  A statistical parameter study of indium tin oxide thin films deposited by radio-frequency sputtering , 2005 .

[4]  K. No,et al.  Effects of oxygen partial pressure on the microstructure and electrical properties of indium tin oxide film prepared by d.c. magnetron sputtering , 1995 .

[5]  M. Ferenets,et al.  Thin Solid Films , 2010 .

[6]  Andrew G. Glen,et al.  APPL , 2001 .

[7]  S. Ray,et al.  The role of oxygen and hydrogen partial pressures on structural and optical properties of ITO films deposited by reactive rf-magnetron sputtering , 2007 .

[8]  Denghui Xu,et al.  An anode with aluminum doped on zinc oxide thin films for organic light emitting devices , 2005 .

[9]  K. Ellmer,et al.  In situ measurement of mechanical stress in polycrystalline zinc-oxide thin films prepared by magnetron sputtering , 2000 .

[10]  F. Zhu,et al.  Optimized indium tin oxide contact for organic light emitting diode applications , 2000 .

[11]  Haeri Kim,et al.  Properties of dc magnetron sputtered indium tin oxide films on polymeric substrates at room temperature , 2001 .

[12]  M. Rottmann,et al.  Electrical and structural properties of indium tin oxide films deposited by reactive DC sputtering , 1995 .

[13]  A. Aberle,et al.  Optimisation of ZnO:Al films by change of sputter gas pressure for solar cell application , 2002 .

[14]  Masashi Kawasaki,et al.  Room-temperature ultraviolet laser emission from self-assembled ZnO microcrystallite thin films , 1998 .