Some surface properties of thermally modified scots pine after artificial weathering

In this study, it was aimed to investigate some surface characteristics such as surface roughness, color, and glossiness of Scots pine (Pinus sylvestris) wood specimens after 500 hours artificial weathering exposure.  The results showed that surface characteristics of thermally modified Scots pine gave better results than unmodified Scots pine after artificial weathering. Artificial weathering caused an increase in surface roughness and a decrease in glossiness of Scots pine wood. Results showed artificial weathered wood become darker, reddish, and yellowish. Generally, higher duration and temperature for Scots pine resulted in better surface characteristics of Scots pine after artificial weathering.

[1]  S. Yıldız,et al.  Effect of artificial weathering on the properties of heat treated wood , 2013 .

[2]  S. Hiziroglu,et al.  Effect of Heat Treatment on Surface Characteristics of Wild Cherry Wood , 2013 .

[3]  C. Krause,et al.  Structural analysis of heat-treated birch (Betule papyrifera) surface during artificial weathering , 2013 .

[4]  K. Pandey,et al.  Photodegradation of thermally modified wood. , 2012, Journal of photochemistry and photobiology. B, Biology.

[5]  S. Korkut,et al.  The effect of heat treatment on some chemical properties and colour in Scots pine and Uludağ fir wood , 2012 .

[6]  A. Act,et al.  SURFACE CHARACTERISTICS OF CCA TREATED SCOTS PINE AFTER ACCELERATED WEATHERING , 2012 .

[7]  Derya Sevim Korkut,et al.  VARNISH LAYER HARDNESS, SCRATCH RESISTANCE, AND GLOSSINESS OF VARIOUS WOOD SPECIES AS AFFECTED BY HEAT TREATMENT , 2011 .

[8]  Ummu Karagoz,et al.  EFFECT OF HEAT TREATMENT ON SURFACE ROUGHNESS OF THERMAL WOOD MACHINED BY CNC , 2011 .

[9]  I. Horman,et al.  HEAT TREATED WOOD , 2010 .

[10]  D. Aydemir,et al.  Some Physical Properties of Heat-Treated Hornbeam (Carpinus betulus L.) Wood , 2009 .

[11]  G. Sèbe,et al.  A new process for the esterification of wood by reaction with vinyl esters , 2008 .

[12]  N. As,et al.  The effect of boiling time on the surface roughness of rotary-cut veneers from oriental beech (Fagus orientalis L.) , 2008 .

[13]  Alessandro Gandini,et al.  Chemical Modification of Wood , 2008 .

[14]  H. Pereira,et al.  Heat-induced colour changes of pine (Pinus pinaster) and eucalypt (Eucalyptus globulus) wood , 2008, Wood Science and Technology.

[15]  D. Hon,et al.  Photoprotection of Wood Surfaces by Wood-Ion Complexes , 2007 .

[16]  G. Sèbe,et al.  A novel simple route to wood acetylation by transesterification with vinyl acetate , 2007 .

[17]  A. Temiz,et al.  Weathering, water absorption, and durability of silicon, acetylated, and heat‐treated wood , 2006 .

[18]  K. Pandey,et al.  Photostability of wood surfaces esterified by benzoyl chloride , 2006 .

[19]  C. Hill,et al.  Wood Modification: Chemical, Thermal and Other Processes , 2006 .

[20]  M. Petrič,et al.  Patination of cherry wood and spruce wood with ethanolamine and surface finishes , 2004 .

[21]  T. Vuorinen,et al.  Heat‐treated softwood exposed to weathering , 2004 .

[22]  Y. Imamura,et al.  Weathering durability of CCB-impregnated wood for clear varnish coatings , 1999, Journal of Wood Science.

[23]  B. Sundqvist.  Colour changes and acid formation in wood during heating , 2004 .

[24]  P. Evans,et al.  Studies of the degradation and protection of wood surfaces , 2004, Wood Science and Technology.

[25]  A. Merlin,et al.  Color stability of heat-treated wood during artificial weathering , 2003, Holz als Roh- und Werkstoff.

[26]  Xueyuan Zhang.  Photo-resistance of alkylammonium compound treated wood , 2003 .

[27]  M. Sehlstedt-Persson.  Colour responses to heat-treatment of extractives and sap from pine and spruce , 2003 .

[28]  M. Meijer.  Review on the durability of exterior wood coatings with reduced VOC-content , 2001 .

[29]  S. Grelier,et al.  Photoprotection of Copper-Amine-Treated Pine , 2000 .

[30]  R. Young,et al.  Reduction of Weathering Degradation of Wood Through Plasma-Polymer Coating , 1999 .

[31]  S. Hiziroglu,et al.  Effect of press closing time and target thickness on surface roughness of particleboard. , 1998 .

[32]  H. Militz,et al.  Performance of finishes on wood that is chemically modified by acetylation , 1998 .

[33]  P. Evans,et al.  Photostabilisation of wood surfaces using a grafted benzophenone UV absorber , 1998 .

[34]  S. Grelier,et al.  Attempt to Protect Wood Colour Against UV/Visible Light by Using Antioxidants Bearing Isocyanate Groups and Grafted to the Material with Microwave , 1997 .

[35]  S. Hiziroglu.  Surfact roughness analysis of wood composites : A stylus method , 1996 .

[36]  Roger M. Rowell,et al.  The Chemistry of solid wood , 1984 .

[37]  William C. Feist,et al.  Chemistry of weathering and protection , 1984 .

[38]  R. S. Williams.  Effect of grafted UV stabilizers on wood surface erosion and clear coating performance , 1983 .

[39]  W. Feist.  Protection of Wood Surfaces with Chromium Trioxide. , 1979 .

[40]  Walter J. Murphy,et al.  ADVANCES IN CHEMISTRY SERIES: Numbers 15 and 17 Demonstrate Rapidly Crowing Interest in Documentation; International Conference To Be Held in 1958 , 1956 .

[41]  P. Evansa,et al.  Weathering and photostability of benzoylated wood , 2022 .