Giant Magnetoresistance and Structure of Electrodeposited Co/Cu Multilayers: The Influence of Layer Thicknesses and Cu Deposition Potential

The giant magnetoresistance (GMR) and structure was investigated for electrodeposited Co/Cu multilayers prepared by a conventional galvanostatic/potentiostatic pulse combination from a pure sulfate electrolyte with various layer thicknesses, total multilayer thickness and Cu deposition potential. X-ray diffraction (XRD) measurements revealed superlattice satellite reflections for many of the multilayers having sufficiently large thickness (at least 2 nm) of both constituent layers. The bilayer repeats derived from the positions of the visible superlattice reflections were typically 10 – 20% higher than the nominal values.The observed GMR was found to be dominated by the multilayer-like ferromagnetic (FM) contribution even for multilayers without visible superlattice satellites. There was always also a modest superparamagnetic (SPM) contribution to the GMR and this term was the largest for multilayers with very thin (0.5 nm) magnetic layers containg apparently a small amount of magnetically decoupled SPM regions. No oscillatory GMR behavior with spacer thickness was observed at any magnetic layer thickness. The saturation of the coercivity as measured by the peak position of the MR(H) curves indicated a complete decoupling of magnetic layers for large spacer thicknesses. The GMR increased with total multilayer thickness which could be ascribed to an increasing SPM contribution to the GMR due to an increasing surface roughness, also indicated by the increasing coercivity. For multilayers with Cu layers deposited at more and more positive potentials, the GMRFM term increased and the GMRSPM term decreased. At the same time, a corresponding reduction of surface roughness measured with atomic force microscopy indicated an improvement of the multilayer structural quality which was, however, not accompanied by an increase of the superlattice reflection intensities. The present results underline that whereas the structural quality as characterized by the surface roughness generally correlates fairly well with the magnitude of the GMR, the microstructural features determining the amplitude of superlattice reflections apparently do not have a direct influence on the GMR.

[1]  S. Mohan,et al.  Structure and Giant Magnetoresistance of Electrodeposited Co/Cu Multilayers Prepared by Two-Pulse (G/P) and Three-Pulse (G/P/G) Plating , 2017, 1704.05105.

[2]  B. Tóth,et al.  Magnetoresistance and Surface Roughness Study of Electrodeposited Ni50Co50/Cu Multilayers , 2016, 1609.06280.

[3]  B. T'oth,et al.  Magnetoresistance and surface roughness study of the initial growth of electrodeposited Co/Cu multilayers , 2016, 1608.04136.

[4]  S. K. Ghosh,et al.  Investigation of ferromagnetic layer dissolution characteristics during pulse electrodeposition of FeCoNiCu/Cu multilayers , 2014, Russian Journal of Electrochemistry.

[5]  D. Oszetzky,et al.  Influence of Cu deposition potential on the giant magnetoresistance and surface roughness of electrodeposited Ni-Co/Cu multilayers , 2013, 1609.00597.

[6]  A. Dogra,et al.  Magnetic and magnetoresistance studies of the evolution of the magnetic layer structure with Co layer thickness in electrodeposited Co–Cu/Cu multilayers , 2013 .

[7]  L. Péter,et al.  Microstructure formation in electrodeposited Co-Cu/Cu multilayers with GMR effect: Influence of current density during magnetic layer deposition , 2011 .

[8]  László Péter,et al.  Electrodeposited multilayer films with giant magnetoresistance (GMR): Progress and problems , 2010 .

[9]  L. Péter,et al.  Formation of microstructural defects in electrodeposited Co/Cu multilayers , 2009 .

[10]  E. Šimon,et al.  Giant magnetoresistance in electrodeposited Co-Cu/Cu multilayers: Origin of the absence of oscillatory behavior , 2009, 1611.02432.

[11]  L. Péter,et al.  Evolution of Structure with Spacer Layer Thickness in Electrodeposited Co ∕ Cu Multilayers , 2008 .

[12]  A. K. Suri,et al.  Structural evolution and giant magnetoresistance in electrodeposited Co-Cu/Cu multilayers , 2008 .

[13]  Á. Cziráki,et al.  Electrodeposition of Co–Ni–Cu/Cu multilayers: 1. Composition, structure and magnetotransport properties , 2007 .

[14]  D. K. Aswal,et al.  High magnetoresistance and low coercivity in electrodeposited Co∕Cu granular multilayers , 2006 .

[15]  Á. Cziráki,et al.  Structure and giant magnetoresistance behaviour of Co-Cu/Cu multilayers electrodeposited under various deposition conditions. , 2006, Journal of nanoscience and nanotechnology.

[16]  H. Hashizume,et al.  Interface Structures and Magnetic Properties of Exchanged-Coupled Co/Cu Multilayers Sputter-Grown on Ta Buffers , 2006 .

[17]  S. Bader,et al.  Twisted magnetization states near the compensation temperature of Fe/Gd multilayers: Anisotropy and surface-termination effects , 2006 .

[18]  L. Péter,et al.  Ferromagnetic and superparamagnetic contributions in the magnetoresistance of electrodeposited Co-Cu/Cu multilayers , 2005 .

[19]  Á. Cziráki,et al.  The role of nucleation in the evolution of giant magnetoresistance with layer thicknesses in electrodeposited Co–Cu/Cu multilayers , 2004 .

[20]  L. Péter,et al.  Decomposition of the magnetoresistance of multilayers into ferromagnetic and superparamagnetic contributions , 2004 .

[21]  W. Schwarzacher.  Kinetic roughening of electrodeposited films , 2004 .

[22]  L. Péter,et al.  Relevance of the potentiodynamic method in parameter selection for pulse-plating of Co-Cu/Cu multilayers , 2004 .

[23]  L. Péter,et al.  Giant Magnetoresistance in Co-Cu/Cu Multilayers Prepared by Various Electrodeposition Control Modes , 2003 .

[24]  W. Schwarzacher,et al.  Giant Magnetoresistance of Electrodeposited Ni81Cu19 / Cu Multilayers , 2002 .

[25]  Á. Cziráki,et al.  Structural properties of electrodeposited Co/Cu multilayers , 1998 .

[26]  C. Michaelsen.  On the structure and homogeneity of solid solutions: The limits of conventional X-ray diffraction , 1995 .

[27]  Christian Schönenberger,et al.  Giant magnetoresistance of electrodeposited Co/Cu multilayers , 1995 .

[28]  H. Kubota,et al.  Giant magnetoresistance and interlayer exchange coupling in Ni-Co/Cu multilayer films , 1994 .

[29]  Schuller,et al.  Structural refinement of superlattices from x-ray diffraction. , 1992, Physical review. B, Condensed matter.

[30]  Parkin,et al.  Oscillatory magnetic exchange coupling through thin copper layers. , 1991, Physical review letters.

[31]  Albert Fert,et al.  Oscillatory interlayer coupling and giant magnetoresistance in Co/Cu multilayers , 1991 .

[32]  T. Mcguire,et al.  Anisotropic magnetoresistance in ferromagnetic 3d alloys , 1975 .

[33]  A. Dinia,et al.  Exchange Coupling and Giant Magnetoresistance in Electrodeposited Co/Cu Multilayers , 1997 .