Transparent conducting p-type NiO thin films prepared by magnetron sputtering

Abstract Transparent and conductive thin films consisting of p -type nickel oxide (NiO) semiconductors were prepared by r.f. magnetron sputtering. A resistivity of 1.4 × 10 −1 ohms cm and a hole concentration of 1.3 × 10 19 cm −3 were obtained for non-intentionally doped NiO films prepared at a substrate temperature of 200°C in a pure oxygen sputtering gas. An average transmittance of about 40% in the visible range was obtained for a 110 nm thick NiO film. A semitransparent thin film pin diode consisting of p -NiO/i-NiO/i-ZnO/ n -ZnO layer having a voltage-current rectification characteristic and an average transmittance above 20% in the visible range was fabricated on a glass substrate.