Calculation of the water requirement of mortar and concrete

The term “water requirement” is defined as the amount of mixing water that is needed for a specified consistency of a mortar or concrete. This paper concentrates on formulas that provide the water requirement as a function of the composition and consistency of the fresh concrete. Dozens of water requirement formulas have been published starting with Feret and Abrams. There are also several formulas that are published here for the first time.An analysis of the basic structure of water requirement formulas winds up the paper providing pointers for future research.RésuméLe dosage en eau est sans doute le plus important des facteurs simples qui déterminent la qualité globale d'un béton (ou d'un mortier); il est donc d'autant plus surprenant qu'on n'ait pas encore systématisé l'information éparse relative au calcul, ou à la prévision, de l'eau nécessaire au béton. Cet article se propose de le faire.On entend par «eau nécessaire» le dosage en eau qu'il faut pour obtenir une consistance spécifiée, et qu'on peut évaluer par diverses méthodes. On s'attache ici plus particulièrement à l'une de ces méthodes, soit aux formules où l'eau nécessaire apparaît comme une fonction de la composition et de la consistance du mélange frais.De nombreux facteurs interviennent: la classe de ciment; la dimension maximale de granulat; le type et la quantité d'adjuvant; et quelques autres. On examine ici leurs effets dans la mesure où ils sont connus.Depuis Feret et Abrams, des douzaines, de formules pour l'eau nécessaire ont été publiées. On verra ici plusieurs autres formules pour la première fois; quelques unes ne renferment qu'une variable et leur validité est étroitement limitée; d'autres renferment plusieurs variables et ont une validité plus étendue. Aucune des formules dont on dispose actuellement ne renferme toutes les variables nécessaires.Une étude de la structure de base de ces formules conclut cet article et fournira des directions pour de nouvelles recherches.

[1]  T. Powers,et al.  The properties of fresh concrete , 1968 .

[2]  M. Ozol Chapter 35—Shape, Surface Texture, Surface Area, and Coatings , 1978 .

[3]  L. J. Murdock The workability of concrete , 1960 .

[4]  Stanton Walker Control of Quality of Ready-Mixed Concrete , 1949 .

[5]  白山 和久,et al.  Discussion of a report by ACI Committee 613 : Ptoposed Recommended Practice for Selecting Proportions for Concrete , 1955 .

[6]  Paul Klieger,et al.  Landmark Series: Further Studies on the Effect of Entrained Air on Strength and Durability of Concrete with Various Sizes of Aggregates , 2003 .

[7]  R. F. Blanks,et al.  The technology of cement and concrete , 1955 .

[8]  Sándor Popovics Relation between the change of water content and the consistence of fresh concrete , 1962 .

[9]  J R Wilson RECOMMENDED PRACTICE FOR SELECTING PROPORTIONS FOR NO-SLUMP CONCRETE , 1974 .

[10]  Sandor Popovics,et al.  Concrete-making materials , 1979 .

[11]  Paul Klieger,et al.  Effect of Mixing and Curing Temperature onConcrete Strength , 1958 .

[12]  J. Clifton,et al.  Interrelations between cement and concrete properties, part 6 :: compilation of data from laboratory studies , 1971 .

[13]  Richard D. Gaynor,et al.  Effects of Aggregate Properties on Strength of Concrete , 1963 .

[14]  B. G. Singh Specific Surface of Aggregates Applied to Mix Proportioning , 1959 .

[15]  Arthur Newell Talbot,et al.  THE STRENGTH OF CONCRETE - ITS RELATION TO THE CEMENT, AGGREGATES AND WATER , 1923 .

[16]  H W Schneider,et al.  SUPPLEMENTARY STUDY OF 34-E DUAL DRUM PAVERS , 1962 .