Influence of Resin Molecular Weight on Curing and Thermal Degradation of Plywood Made From Phenolic Prepreg Palm Veneers

The present work evaluates curing and the thermal behavior of different molecular weight phenol formaldehyde (PF) resins used to prepare PF prepreg oil palm stem veneers. The physical properties (solid contents, gelation time, pH, and viscosity) of PF resins were determined. The molecular weight of resins was characterized by gel permeation chromatography, whilst thermal properties were determined by differential scanning calorimetry and thermogravimetric analyses. The average molecular weight of PF resins were 526 g/mole (low), 1889 g/mole (medium), and 5178 g/mole (control - commercial). Among the resins, medium (MMwPF) gives better thermal stability with a retained weight of 48.9% at 300°C. High (Commercial PF) had a low decomposition temperature (109.3°C) which occurred within 11 min. Both low (LMwPF) and MMwPF started to melt at ≥120°C. Based on strength and shear values, phenolic prepreg palm veneers can be prepared using either low or medium molecular weight PF but with varying results. In all cases, the mechanical properties of palm plywood made from PF prepreg veneers were superior to those made from PF-bonded plywood using the commercial process.

[1]  Y. B. Hoong,et al.  Development of a new pilot scale production of high grade oil palm plywood: Effect of pressing pressure. , 2012 .

[2]  P. Tahir,et al.  Density distribution of oil palm stem veneer and its influence on plywood mechanical properties , 2011 .

[3]  S. Hamdan,et al.  The effect of crosslinker on mechanical and morphological properties of tropical wood material composites , 2011 .

[4]  Y. B. Hoong,et al.  Effects of treatment with low molecular weight phenol formaldehyde resin on the surface characteristics of oil palm (Elaeis quineensis) stem veneer. , 2011 .

[5]  P. Bekhta,et al.  Effect of pre-pressing of veneer on the glueability and properties of veneer-based products , 2010, European Journal of Wood and Wood Products.

[6]  N. Yunus,et al.  Evaluation on the suitability of some adhesives for laminated veneer lumber from oil palm trunks , 2009 .

[7]  Y. Imamura,et al.  Improvement of physical and biological properties of particleboards by impregnation with phenolic resin , 1991, Wood Science and Technology.

[8]  Y. Imamura,et al.  The modification of wood by treatment with low molecular weight phenol-formaldehyde resin: a properties enhancement with neutralized phenolic-resin and resin penetration into wood cell walls , 2004, Wood Science and Technology.

[9]  Antonio Pizzi,et al.  Handbook of Adhesive Technology, Revised and Expanded , 2003 .

[10]  B. Riedl,et al.  Model‐free kinetics: Curing behavior of phenol formaldehyde resins by differential scanning calorimetry , 2003 .

[11]  B. Riedl,et al.  Differential Scanning Calorimetry of Phenol-Formaldehyde (PF) Adhesives , 1999 .

[12]  Antonio Pizzi,et al.  Handbook of adhesive technology , 1994 .

[13]  Terry Sellers,et al.  Plywood and Adhesive Technology , 1985 .

[14]  D. WellonsJ,et al.  フェノール樹脂のGPC(ゲル浸透クロマトグラフィー)および光散乱 分子量測定の問題点 , 1980 .

[15]  S. Chow,et al.  Thermal Analysis of Liquid Phenol-Formaldehyde Resin Curing , 1972 .

[16]  R. Conley.  Thermal stability of polymers , 1970 .

[17]  Robert T. Conley,et al.  A study of the oxidative degradation of phenol-formaldehyde polycondensates using infrared spectroscopy†‡ , 1963 .