Optimization of synthesis parameters of mesoporous silica sol–gel thin films for application on 2024 aluminum alloy substrates

Abstract Silica mesoporous films were synthesized via Evaporation Induced Self-Assembly (EISA) using Pluronic P123 as templating agent and were applied on 2024 aluminum alloy for surface treatment applications. The removal of the P123 from the film required to convert the mesostructured film into a mesoporous film was particularly studied and optimized in order to be compatible with the use of an aluminum substrate. In this work, two different kinds of removal treatments were compared: calcination at high temperatures and UV/ozone treatment. Indeed, a minimum temperature of 275 °C has to be reached to completely remove the templating agent from the film. However, this treatment also leads to a decrease in mechanical properties of the aluminum substrate. In opposition, the removal by UV/ozone illumination allows getting mesoporous films at room temperature with important pore volume and high specific surface area without impacting mechanical properties of the aluminum. The effect of these treatments on mechanical properties of bare aluminum was followed by microhardness. The development of the porosity inside the film due to the elimination of the P123 was measured by combining analytical techniques (Fourier transform infrared spectroscopy FTIR, radio-frequency glow discharge optical emission spectroscopy RF-GDOES), electrochemical impedance spectroscopy (EIS) and adsorption porosimetry using a quartz crystal microbalance.

[1]  S. Tolbert,et al.  Controlling thickness in hexagonal polymer templated mesoporous silica films , 2006 .

[2]  Yen Wei,et al.  Use of sublimation for template removal from menthol templated mesoporous organosilica prepared via sol–gel process , 2011 .

[3]  E. Teller,et al.  ADSORPTION OF GASES IN MULTIMOLECULAR LAYERS , 1938 .

[4]  Yunfeng Lu,et al.  Evaporation-Induced Self-Assembly: Nanostructures Made Easy** , 1999 .

[5]  Jyrki Kiihamäki.  Deceleration of silicon etch rate at high aspect ratios , 2000 .

[6]  H. Möhwald,et al.  Surface‐Modified Mesoporous SiO2 Containers for Corrosion Protection , 2009 .

[7]  C. Sanchez,et al.  Porosity and mechanical properties of mesoporous thin films assessed by environmental ellipsometric porosimetry. , 2005, Langmuir : the ACS journal of surfaces and colloids.

[8]  Plinio Innocenzi,et al.  Humidity sensors based on mesoporous silica thin films synthesised by block copolymers , 2004 .

[9]  R. Denoyel,et al.  Ozone treatment for the removal of surfactant to form MCM-41 type materials , 1998 .

[10]  G. Sauerbrey,et al.  Use of quartz vibration for weighing thin films on a microbalance , 1959 .

[11]  A. Franquet,et al.  Study of the effect of different aluminium surface pretreatments on the deposition of thin non‐functional silane coatings , 2004 .

[12]  Masataka Tanigaki,et al.  Effect of drying on the mesoporous structure of sol-gel derived silica with PPO-PEO-PPO template block copolymer. , 2005, Journal of colloid and interface science.

[13]  Galo J. A. A. Soler-Illia,et al.  Mesoporous hybrid thin films: the physics and chemistry beneath. , 2006, Chemistry.

[14]  A. Franquet,et al.  Effect of bath concentration and curing time on the structure of non-functional thin organosilane layers on aluminium , 2003 .

[15]  Galo J. A. A. Soler-Illia,et al.  Fundamentals of Mesostructuring Through Evaporation‐Induced Self‐Assembly , 2004 .

[16]  Sviatlana V. Lamaka,et al.  Nanoporous titania interlayer as reservoir of corrosion inhibitors for coatings with self-healing ability , 2007 .

[17]  R. Hayward,et al.  General Predictive Syntheses of Cubic, Hexagonal, and Lamellar Silica and Titania Mesostructured Thin Films§ , 2002 .

[18]  Jianlin Shi,et al.  Preparation of mesoporous silica films on a glass slide: surfactant template removal by solvent extraction , 2001 .

[19]  A. Bautista,et al.  Characterization of porous aluminium oxide films from a.c. impedance measurements , 1999 .

[20]  Olivier Dubreuil,et al.  TiO2 multilayer thick films (up to 4 µm) with ordered mesoporosity: influence of template on the film mesostructure and use as high efficiency photoelectrode in DSSCs , 2011 .

[21]  M. Textor,et al.  A photo-electron and secondary ion mass spectrometric study of the chemical composition of thermal oxide layers on technically pure aluminium , 1983 .

[22]  Sviatlana V. Lamaka,et al.  TiOx self-assembled networks prepared by templating approach as nanostructured reservoirs for self-healing anticorrosion pre-treatments , 2006 .

[23]  G. Sauerbrey.  Verwendung von Schwingquarzen zur Wägung dünner Schichten und zur Mikrowägung , 1959 .

[24]  A. Schmidtchen,et al.  Incorporation of antimicrobial compounds in mesoporous silica film monolith. , 2009, Biomaterials.

[25]  J. Kaufman,et al.  Properties of Aluminum Alloys: Tensile, Creep, and Fatigue Data at High and Low Temperatures , 2000 .

[26]  M. R. Baklanov,et al.  Determination of pore size distribution in thin films by ellipsometric porosimetry , 2000 .

[27]  H. Hillhouse,et al.  Order and orientation control of mesoporous silica films on conducting gold substrates formed by dip-coating and self-assembly: a grazing angle of incidence small-angle X-ray scattering and field emission scanning electron microscopy study. , 2005, Langmuir : the ACS journal of surfaces and colloids.

[28]  Q. Huo,et al.  Organization of Organic Molecules with Inorganic Molecular Species into Nanocomposite Biphase Arrays , 1994 .

[29]  F. Dultsev,et al.  Porous structure of SiO2 films synthesized at low temperature and pressure , 1989 .

[30]  S. Mazzini,et al.  Effect of deformation at elevated temperature before age-hardening on the mechanical properties of 2024 commercial aluminium alloy , 1991 .

[31]  Galo J. A. A. Soler-Illia,et al.  Humidity-controlled mesostructuration in CTAB-templated silica thin film processing. The existence of a modulable steady state , 2003 .

[32]  H. Amenitsch,et al.  Silica Orthorhombic Mesostructured Films with Low Refractive Index and High Thermal Stability , 2004 .