Orientation Dependence of the Ferroelectricity of T.G.S.

The ferroelectric behaviour of T.G.S. single crystals is studied for slabs cut along directions which form gradual orientations with the polar axis [010]. Distinct ferroelectric phenomena are observed for several directions, even for orientations well away from the polar axis, where perfectly defined ferroelectric properties are obtained (hysteresis loop, λ-curve of the dielectric constant, and maximum switching current). The results are interpreted on the basis of a simple consideration of H-bond contributions to the ferroelectricity. The theoretical conclusions are in good agreement with the experimental results. Es wird das ferroelektrische Verhalten von T.G.S. Einkristallen an tafelformigen Proben untersucht, die in verschiedenen Orientierungen zur polaren Achse [010] geschnitten wurden. Deutliche ferroelektrische Phanomene werden auch fur Orientierungen beobachtet, die betrachtlich von der polaren Achse entfernt sind, wobei vollstandig definierte, ferroelektrische Eigenschaften erhalten werden (Hysteresisschleife, λ-Kurve der Dielektrizitatskonstante und maximaler Schaltstrom). Die Ergebnisse werden mit einer einfachen Berucksichtigung des Beitrags der H-Bindungen zur Ferroelektrizitat gedeutet. Die theoretischen Schlusfolgerungen befinden sich in guter Ubereinstimmung mit den experimentellen Ergebnissen.