Preparation, characterization, and application of NR/SBR/Organoclay nanocomposites in the tire industry

The natural rubber/styrene butadiene rubber/organoclay (NR/SBR/organoclay) nanocomposites were successfully prepared with different types of organoclay by direct compounding. The optimal type of organoclay was selected by the mechanical properties characterization of the NR/SBR/organoclay composites. The series of NR/SBR/organoclay (the optimal organoclay) nanocomposites were prepared with various organoclay contents loading from 1.0 to 7.0 parts per hundreds of rubber (phr). The nearly completely exfoliated organoclay nanocomposites with uniform dispersion were confirmed by transmission electron microscopy (TEM) and X-ray diffraction (XRD). The results of mechanical properties measurement showed that the tensile strength, tensile modulus, and tear strength were improved significantly when the organoclay content was less than 5.0 phr. The tensile strength and the tear strength of the nanocomposite with only 3.0 phr organoclay were improved by 92.8% and 63.4%, respectively. It showed organoclay has excellent reinforcement effect with low content. The reduction of the score and cure times of the composites indicated that the organoclay acted as accelerator in the process of vulcanization. The incorporation of a small amount of organoclay greatly improved the swelling behavior and thermal stability, which was attributed to the good barrier properties of the dispersed organoclay layers. The outstanding performance of co-reinforcement system with organoclay in the tire formulation showed that the organoclay had a good application prospect in the tire industry, especially for the improvement of abrasion resistance and the reduction of production cost. © 2010 Wiley Periodicals, Inc. J Appl Polym Sci, 2011

[1]  John C. Little,et al.  Transport properties in polyurethane/clay nanocomposites as barrier materials: Effect of processing conditions , 2009 .

[2]  George Tsagaropoulos,et al.  Dynamic Mechanical Study of the Factors Affecting the Two Glass Transition Behavior of Filled Polymers. Similarities and Differences with Random Ionomers , 1995 .

[3]  G. Hamed,et al.  Tensile Behavior after Oxidative Aging of Gum and Black-Filled Vulcanizates of SBR and NR , 1999 .

[4]  Krzysztof Pielichowski,et al.  Polymer/montmorillonite nanocomposites with improved thermal properties Part I. Factors influencing thermal stability and mechanisms of thermal stability improvement , 2007 .

[5]  Suprakas Sinha Ray,et al.  POLYMER/LAYERED SILICATE NANOCOMPOSITES: A REVIEW FROM PREPARATION TO PROCESSING , 2003 .

[6]  Peiyao Li,et al.  Preparation and properties of styrene butadiene rubber/natural rubber/organo-bentonite nanocomposites prepared from latex dispersions , 2009 .

[7]  P. Liu,et al.  Polymer modified clay minerals: A review , 2007 .

[8]  Jianxiang Wang,et al.  Prediction of the overall moduli of layered silicate-reinforced nanocomposites—part II: analyses , 2004 .

[9]  Ana Rita Morales,et al.  Organoclays: Properties, preparation and applications , 2008 .

[10]  G. Mathew,et al.  Role of dichlorocarbene modified styrene butadiene rubber in compatibilisation of styrene butadiene rubber and chloroprene rubber blends , 2001 .

[11]  Angel J. Marzocca,et al.  Thermal properties in cured natural rubber/styrene butadiene rubber blends , 2008 .

[12]  F. Schork,et al.  Water-based polymer/clay nanocomposite suspension for improving water and moisture barrier in coating , 2007 .

[13]  G. Nando,et al.  Organomodified montmorillonite as filler in natural and synthetic rubber , 2004 .

[14]  C. Nah,et al.  Preparation and properties of nitrile rubber/montmorillonite nanocomposites via latex blending , 2006 .

[15]  Liqun Zhang,et al.  Preparation and properties of natural rubber/rectorite nanocomposites , 2005 .

[16]  Agurtzane Mugica,et al.  Pyrolysis-FTIR and TGA techniques as tools in the characterization of blends of natural rubber and SBR , 2006 .

[17]  N. S. Tomer,et al.  Nanoscale particles for polymer degradation and stabilization—Trends and future perspectives , 2009 .

[18]  Min-Su Kim,et al.  Melt‐compounded butadiene rubber nanocomposites with improved mechanical properties and abrasion resistance , 2006 .

[19]  A. Okada,et al.  Synthesis and properties of polyimide-clay hybrid films , 1997 .

[20]  Lina Zhang,et al.  New fabricate of styrene–butadiene rubber/montmorillonite nanocomposites by anionic polymerization , 2005 .

[21]  J. Hrachová,et al.  Effect of montmorillonite modification on mechanical properties of vulcanized natural rubber composites , 2008 .

[22]  F. Sharif,et al.  Structure, properties and corrosion resistivity of polymeric nanocomposite coatings based on layered silicates , 2008 .

[23]  A. Rashidi,et al.  Review of Polymer-Organoclay Nanocomposites , 2008 .

[24]  M. Gustafsson,et al.  Thermal conductivity of styrene butadiene rubber compounds with natural rubber prophylactics waste as filler , 1999 .

[25]  T. Hjertberg,et al.  Effect of montmorillonite treatment on the thermal stability of poly(vinyl chloride) nanocomposites , 2009 .

[26]  Isaac M. Daniel,et al.  Characterization and modeling of mechanical behavior of polymer/clay nanocomposites , 2003 .

[27]  Takashi Kashiwagi,et al.  Flammability of polystyrene layered silicate (clay) nanocomposites: Carbonaceous char formation , 2002 .

[28]  Thomas Reisinger,et al.  A rheological method to compare the degree of exfoliation of nanocomposites , 2003 .

[29]  R. Rajapakse,et al.  Montmorillonite polyaniline nanocomposites: Preparation, characterization and investigation of mechanical properties , 2009 .

[30]  J. E. Mark,et al.  Clay nanolayer reinforcement of cis‐1,4‐polyisoprene and epoxidized natural rubber , 2001 .

[31]  G. Song,et al.  Characterization of high-performance exfoliated natural rubber/organoclay nanocomposites , 2008 .

[32]  L. Visconte,et al.  Different preparative modes for the incorporation of additives in NR/SBR blends , 2004 .

[33]  Constantine D. Papaspyrides,et al.  A review on polymer–layered silicate nanocomposites , 2008 .

[34]  Xudong Shi,et al.  Preparation and characterization of poly(propylene carbonate)/montmorillonite nanocomposites by solution intercalation , 2007 .

[35]  G. Song,et al.  High-performance EPDM/organoclay nanocomposites by melt extrusion , 2008 .

[36]  P. Dubois,et al.  Polymer-layered silicate nanocomposites: preparation, properties and uses of a new class of materials , 2000 .

[37]  G. Heinrich,et al.  Nanocomposites based on chloroprene rubber: Effect of chemical nature and organic modification of nanoclay on the vulcanizate properties , 2008 .

[38]  B. Pukánszky,et al.  Factors and processes influencing the reinforcing effect of layered silicates in polymer nanocomposites , 2007 .

[39]  R. E. Smallman,et al.  An assessment of high voltage electron microscopy (HVEM). An invited review , 1977 .

[40]  S. Qutubuddin,et al.  Synthesis, thermal properties and applications of polymer-clay nanocomposites , 2006 .

[41]  P. Dubois,et al.  Polymer/layered silicate nanocomposites by combined intercalative polymerization and melt intercalation: a masterbatch process , 2003 .