Cathode materials: A personal perspective

A thermodynamically stable rechargeable battery has a voltage limited by the window of the electrolyte. An aqueous electrolyte has a window of 1.2 eV, which prevents achieving the high energy density desired for many applications. A non-aqueous electrolyte with a window of 5 eV requires Li + rather than H + as the working ion. Early experiments with Li x TiS 2 cathodes showed competitive capacity and rate capability, but problems with a lithium anode made the voltage of a safe cell based on a sulfide cathode too low to be competitive with a nickel/metal-hydride battery. Transition-metal oxides can give voltages of 4.5 V versus Li + /Li 0 . However, the challenge with oxides has been to obtain a competitive capacity and rate capability while retaining a high voltage with low-cost, environmentally friendly cathode materials. Comparisons will be made between layered Li 1-x MO 2 , spinels Li 1-x [M 2 ]O 4 , and olivines Li 1-x MPO 4 having 0<x< 1. Although higher capacities can be obtained with layered Li 1-x MO 2 compounds, which have enabled the wireless revolution, their metastability makes them unlikely to be used in power applications. The spinel and olivine framework structures have been shown to be capable of charge/discharge rates of over 10C with a suitable temperature range for plug-in hybrid vehicles.

[1]  A. Manthiram,et al.  Superior Capacity Retention Spinel Oxyfluoride Cathodes for Lithium-Ion Batteries , 2006 .

[2]  R. Holze,et al.  Cathode materials modified by surface coating for lithium ion batteries , 2006 .

[3]  A. Manthiram,et al.  Factors influencing the chemical lithium extraction rate from layered LiNi1−y−zCoyMnzO2 cathodes , 2004 .

[4]  J. Goodenough,et al.  Solid-Solution Oxides for Storage-Battery Electrodes , 1980 .

[5]  John B. Goodenough,et al.  Lithium insertion into manganese spinels , 1983 .

[6]  D. Murphy,et al.  Lithium intercalation in cubic TiS2 , 1986 .

[7]  M. Whittingham,et al.  Electrical Energy Storage and Intercalation Chemistry , 1976, Science.

[8]  Karim Zaghib,et al.  Reduction Fe3+ of Impurities in LiFePO4 from Pyrolysis of Organic Precursor Used for Carbon Deposition , 2006 .

[9]  K. S. Nanjundaswamy,et al.  Phospho‐olivines as Positive‐Electrode Materials for Rechargeable Lithium Batteries , 1997 .

[10]  John B. Goodenough,et al.  Fast Na+-ion transport in skeleton structures , 1976 .

[11]  J. Goodenough,et al.  LiNi0.5+δMn0.5–δO2—A High‐Rate, High‐Capacity Cathode for Lithium Rechargeable Batteries , 2006 .

[12]  Arumugam Manthiram,et al.  High Capacity, Surface-Modified Layered Li [ Li ( 1 − x ) ∕ 3Mn ( 2 − x ) ∕ 3Nix ∕ 3Cox ∕ 3 ] O2 Cathodes with Low Irreversible Capacity Loss , 2006 .

[13]  D. D. Yue,et al.  Fast Ion Transport in Solids, Solid State Batteries and Devices , 1974 .

[14]  J. Goodenough,et al.  Effect of ball-milling on 3-V capacity of lithium-manganese oxospinel cathodes , 2001 .

[15]  Ying Shirley Meng,et al.  Electrodes with High Power and High Capacity for Rechargeable Lithium Batteries , 2006, Science.

[16]  J. Barker,et al.  A Carbothermal Reduction Method for the Preparation of Electroactive Materials for Lithium Ion Applications , 2003 .

[17]  John B. Goodenough,et al.  Mapping of Transition Metal Redox Energies in Phosphates with NASICON Structure by Lithium Intercalation , 1997 .

[18]  Yunhui Huang,et al.  Improving Lithium Batteries by Tethering Carbon-Coated LiFePO4 to Polypyrrole , 2006 .

[19]  John B. Goodenough,et al.  Electrochemical extraction of lithium from LiMn2O4 , 1984 .

[20]  John B. Goodenough,et al.  LixCoO2 (0, 1980 .

[21]  Tsutomu Ohzuku,et al.  Layered Lithium Insertion Material of LiNi1/2Mn1/2O2 : A Possible Alternative to LiCoO2 for Advanced Lithium-Ion Batteries , 2001 .