Phase diagram effects in rapid thermal processing of REBa/sub 2/Cu/sub 3/O/sub 7- delta /
暂无分享,去创建一个
Recent investigations of rapid thermal processing of REBa/sub 2/Cu/sub 3/O/sub 7- delta / by drop tube melting, laser surface treatment, and shock compaction have shown that the microstructure resulting from these processes is a complex mixture of nonequilibrium phases. It is demonstrated that with the exception of extremely rapid solidification from above the liquidus, the microstructure and phase distribution results from the heating rather than the cooling part of the curve. Since all of the above processes induce nonuniform heating, different parts of the sample reach different maximum temperatures. The maximum temperature reached and the time spent near that maximum uniquely determine the starting state of the quench. If the entire sample is not above the liquidus, the sluggishness of the peritectic reactions results in similar microstructure regardless of the quench rate. Upon annealing the final microstructure is much more dependent on the number of nucleation sites than on the type of site, resulting in a uniform REBa/sub 2/Cu/sub 3/O/sub 7- delta / microstructure over a broad range of processing parameters.<<ETX>>
[1] Mark A. Rodriguez,et al. Direct observation of textured YBa2Cu3O7−δ crystal growth from the melt , 1992 .
[2] R. McCallum,et al. Melt-spin processing of YBa_2Cu_3O_7−x , 1991 .
[3] B. Merkle. Formation of high temperature superconductors from the solidified melt , 1992 .